In-mould injection moulding process of aluminum shell

An in-mold injection molding and molding technology, applied in the coating and other directions, can solve the problems of easy separation, difficult joining, and difficult CNC processing, and achieve the effect of firm bonding, simple process, and difficult separation.

Active Publication Date: 2015-03-25
DONGGUAN SINCO ELECTRONICS
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the great difference in the physical properties of metal and plastic, it is difficult to join commonly used engineering plastics directly to the surface of metal aluminum. It is usually designed as a mosaic structure to increase the joint firmness of the two materials, but it is difficult for small and precise parts. Design the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • In-mould injection moulding process of aluminum shell
  • In-mould injection moulding process of aluminum shell
  • In-mould injection moulding process of aluminum shell

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0047] Example 1.

[0048] The in-mold injection molding process of the aluminum casing of this embodiment includes the following steps:

[0049] The first step is to clean the aluminum case:

[0050] Clean the surface of the aluminum case;

[0051] In the second step, the surface of the aluminum casing is treated with nano-scale microporous surface:

[0052] Step 1, fix the aluminum case with clean surface on the hanger with electrodes;

[0053] Step 2: Put the aluminum case into Fe(OH) using the hanger 3 In the colloidal solution, electrify for electrolysis for 20 seconds; among them, Fe(OH) 3 The colloidal solution is prepared by adding FeCl 3 Fe(OH) generated by reaction with hot water in a heating tank 3 Colloidal saturated solution.

[0054] Step 3, put the aluminum casing after the electrolysis treatment in step 2 into the NaOH solution with a concentration of 4% for 30 seconds;

[0055] Step 4: Take the aluminum casing out of the NaOH solution and then pu...

Example Embodiment

[0063] Example 2.

[0064] The in-mold injection molding process of the aluminum casing of this embodiment includes the following steps:

[0065] The first step is to clean the aluminum case:

[0066] Clean the surface of the aluminum case;

[0067] In the second step, the surface of the aluminum casing is treated with nano-scale microporous surface:

[0068] Step 1, fix the aluminum case with clean surface on the hanger with electrodes;

[0069] Step 2: Put the aluminum case into Fe(OH) using the hanger 3 In the colloidal solution, electrolytic treatment is carried out for 30 seconds after electrification; among them, Fe(OH) 3 The colloidal solution is prepared by adding FeCl 3 Fe(OH) generated by reaction with hot water in a heating tank 3 Colloidal saturated solution.

[0070] Step 3, put the aluminum casing after the electrolysis treatment in step 2 into a NaOH solution with a concentration of 8% and soak for 20 seconds;

[0071] Step 4, take out the aluminum...

Example Embodiment

[0079] Example 3.

[0080] The in-mold injection molding process of the aluminum casing of this embodiment includes the following steps:

[0081] The first step is to clean the aluminum case:

[0082] Clean the surface of the aluminum case;

[0083] In the second step, the surface of the aluminum casing is treated with nano-scale microporous surface:

[0084] Step 1, fix the aluminum case with clean surface on the hanger with electrodes;

[0085] Step 2: Put the aluminum case into Fe(OH) using the hanger 3 In the colloidal solution, electrify and conduct electrolysis treatment for 10 seconds; among them, Fe(OH) 3 The colloidal solution is prepared by adding FeCl 3 Fe(OH) generated by reaction with hot water in a heating tank 3 Colloidal saturated solution.

[0086] Step 3, put the aluminum casing after the electrolysis treatment in step 2 into a NaOH solution with a concentration of 2% for 40 seconds;

[0087] Step 4, take out the aluminum casing from the NaOH so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of injection moulding of mobile phone shells, in particular to an in-mould injection moulding process of an aluminum shell. The in-mould injection moulding process comprises the following steps: 1, cleaning the aluminum shell; 2, performing nanoscale microporous surface treatment on the surface of the aluminum shell: 1), fixing the aluminum shell on a hanger with electrodes; 2), putting the aluminum shell into an Fe(OH)3 colloidal solution by using the hanger, and electrifying the aluminum shell for a certain period of time; 3), putting the aluminum shell into a NaOH solution, and soaking for a certain period of time; 4), putting the aluminum shell into an NH4CL solution, and cleaning for a certain period of time; 5), putting the aluminum shell into purified water, and cleaning for many times; 6), drying the aluminum shell to finish the nanoscale microporous surface treatment to the surface of the aluminum shell; 3, performing injection moulding. By the in-mould injection moulding process, the aluminum shell and plastic are firmly combined and are unlikely to separate, and a requirement on plane-to-plane combination of the aluminum shell and the plastic can be met.

Description

technical field [0001] The invention relates to the technical field of injection molding of mobile phone casings, in particular to an in-mold injection molding process for aluminum casings. Background technique [0002] At present, most of the internal brackets of mobile phones are made of metal aluminum, and the internal brackets of the mobile phone case frame need to be injection molded to meet the structural and appearance requirements. In the prior art, the injection molding process for the inner bracket of the mobile phone case frame is as follows: first, the aluminum case frame is processed by CNC, and then the insulating plastic structure is directly injected on the bracket. However, due to the great difference in the physical properties of metal and plastic, it is difficult to join commonly used engineering plastics directly to the surface of metal aluminum. It is usually designed as a mosaic structure to increase the joint firmness of the two materials, but it is di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C45/14B29C45/78B29C45/77C25F3/04
CPCB29C45/14B29C45/1753B29C45/77B29C45/78B29C2945/76498B29C2945/76531C25F3/04
Inventor 李文联
Owner DONGGUAN SINCO ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap