A production process and single-sided technology, applied in the field of production process of KPF structure single-sided coated backplane, can solve the problem of high production cost, achieve low cost, reduce one-time compounding process, and reduce manufacturing cost.

Inactive Publication Date: 2015-03-25
XIAMEN TAOZHEN TECH CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usually, the outer weathering layer is PVDF material with a thickness of 25um, the middle reinforcement layer is PET with a thickness of 250um, the inner weathering layer is PE coating, and the bonding layer is polyuretha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The specific implementation of the present invention will be further described below in conjunction with the examples. The following examples are only used to illustrate the technical solution of the present invention more clearly, but not to limit the protection scope of the present invention.

[0021] The technical scheme of concrete implementation of the present invention is:

[0022] A kind of production technology of KPF structure single-sided coating back plate, comprises the following steps:

[0023] 1) Coat high-performance polyurethane glue with a thickness of 10um on the PET surface that has been treated with low-temperature plasma, and then enter the oven for drying;

[0024] 2) Lay a PVDF fluorine film with a thickness of 12um on the glue surface of the glue-coated PET material;

[0025] 3) After winding, the other side of the PET surface is also treated with low-temperature plasma, and coated with high-performance polyurethane glue with a thickness of 10u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production process for a KPF structure single-face coating backboard. The process includes the following steps that (1) one surface of a PET material is coated with high-performance polyurethane glue with the thickness being 10 microns after low-temperature plasma treatment is conducted on the surface of the PET material and the PET material is delivered into an oven to be dried; (2) a PVDF film with the thickness being 12 microns is compounded to the glue face coated with the glue of the PET material; (3) after the material is rolled, low-temperature plasma treatment is conducted on the other surface of the PET material, the other surface is coated with the high-performance polyurethane glue with the thickness being 10 microns, and the material is delivered into the oven to be dried; (4) modified PE paint with the thickness being 4 microns is compounded to the other glue face coated with the glue of the PET material; (5) after being rolled, the material is cured in the oven for 40 hours at the 40 DEG C so that the backboard can be manufactured. According to the production process, manufacturing cost is reduced, a compounding working procedure is omitted, the rate of finished products is effectively increased, cost is saved, and a manufacturing method is simple.

Description

technical field [0001] The invention relates to a production process of a KPF structure single-sided coating backboard. Background technique [0002] The insulated backsheet for solar photovoltaic cells (referred to as solar insulated backsheet) is located on the back of the solar panel to protect and support the battery, and must have reliable insulation, water resistance and aging resistance. [0003] The KPF structure solar insulating back sheet of the existing scheme is generally composed of four layers, the outer layer is made of PVDF fluorine film, and the inner layer is PET. The laminated layer with EVA is directly coated with PE coating, and the PVDF fluorine film and PET are usually connected by adhesive. Usually, the outer weathering layer is PVDF material with a thickness of 25um, the middle reinforcement layer is PET with a thickness of 250um, the inner weathering layer is PE coating, and the bonding layer is polyurethane glue with a thickness of 10um. These pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01L31/18
CPCH01L31/02167H01L31/18Y02P70/50
Inventor 仲春
Owner XIAMEN TAOZHEN TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap