A kind of preparation method and electroplating solution of brazing filler metal for aluminum alloy vacuum brazing

A technology of aluminum alloy and electroplating solution, applied in welding equipment, metal processing equipment, welding/cutting medium/material, etc., can solve the problems of increasing brazing production cycle and brazing cost, cumbersome brazing process, and contaminating the surface of parts. , to shorten the welding production time, simplify the welding production process, and achieve the effect of small grain size

Active Publication Date: 2016-08-24
CHINA ELECTRONIC TECH GRP CORP NO 38 RES INST
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this process are as follows: the soldering sheet needs to be prefabricated, which increases the brazing production cycle and brazing cost; the soldering sheet needs to be cut and cleaned according to the shape of the surface to be welded of the part to be welded before use, resulting in a It is cumbersome; the conventional soldering piece is thicker, the thickness is generally 0.1-0.15mm, and the excess solder during welding is easy to cause overflow and pollute the surface of the part

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method and electroplating solution of brazing filler metal for aluminum alloy vacuum brazing
  • A kind of preparation method and electroplating solution of brazing filler metal for aluminum alloy vacuum brazing
  • A kind of preparation method and electroplating solution of brazing filler metal for aluminum alloy vacuum brazing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0017] Aiming at the current existing brazing material, that is, solder, the present invention designs an alternative preparation method of brazing filler metal for aluminum alloy vacuum brazing. It can be directly attached to the workpiece to be welded. During the vacuum brazing process, there is no need to prepare the solder sheet separately, no need to design the shape of the solder sheet, no need to perform welding cutting, and no need to perform solder sheet assembly, which greatly reduces the cost of vacuum brazing. The cost is reduced, the welding production time is shortened, and the weldin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a brazing filler metal for aluminum alloy vacuum braze welding and a plating solution. The brazing filler metal for the aluminum alloy vacuum braze welding is prepared by adopting an electro-deposition method, the preparation method of the brazing filler metal for the aluminum alloy vacuum braze welding comprises the following steps: 1) preparing the plating solution; 2) preparing an electrode; 3) implementing electro-deposition process; and 4) baking the brazing filler metal obtained by the electro-deposition method, the brazing filler metal is the brazing filler metal for the aluminum alloy vacuum braze welding. The brazing filler metal prepared by adopting the preparation method of the brazing filler metal for the aluminum alloy vacuum braze welding is directly adhered onto a workpiece to be welded, a soldering lug is not prepared separately during implementing the vacuum braze welding process, the shape of the soldering lug requires no design, welding and cutting are not required, soldering lug assembly is not required either, the cost of the vacuum braze welding is reduced greatly, the welding production time is shortened, and the process of welding production is simplified. The invention further discloses the plating solution applied to the preparation method of the brazing filler metal for the aluminum alloy vacuum braze welding.

Description

technical field [0001] The invention relates to a method for preparing solder, in particular to a method for preparing solder for aluminum alloy vacuum brazing and an electroplating solution used in the preparation method. Background technique [0002] Aluminum alloy vacuum brazing technology is widely used in the manufacture of electronic products, the manufacture of automobile radiators, and the preparation of some structural and functional parts of aerospace products. Existing vacuum brazing technologies all require special soldering sheets, and the effective connection of parts to be welded is realized by melting the soldering sheets during the welding process. The disadvantages of this process are as follows: the soldering sheet needs to be prefabricated, which increases the brazing production cycle and brazing cost; the soldering sheet needs to be cut and cleaned according to the shape of the surface to be welded of the part to be welded before use, resulting in a It ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/40
CPCC25D3/44
Inventor 栾兆菊王新海李正方坤王传伟
Owner CHINA ELECTRONIC TECH GRP CORP NO 38 RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products