A kind of composite sodium base lubricating grease and preparation method thereof

A compound sodium-based grease, the technology of lubricating grease, applied in the direction of lubricating composition, petroleum industry, thickener, etc., can solve the related research problems without graphene application, and achieve excellent thermal stability, high dropping point, Ability-enhancing effect

Active Publication Date: 2017-11-03
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nanomaterials are also gradually used in the application of grease, such as nano-silica, nano-diamond, nano-titanium dioxide, nano-zinc oxide, etc., but there is still no research on the application of graphene in grease

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite sodium base lubricating grease and preparation method thereof
  • A kind of composite sodium base lubricating grease and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] According to the second aspect of the present invention, the present invention provides a method for preparing a composite sodium-based grease, the method comprising: uniformly mixing graphene, a composite sodium-based thickener and part of the base oil, at a constant temperature of 180-230°C Refining, cooling, adding the remaining base oil, and adding necessary additives to obtain the finished product.

[0028] Among them, the amount of graphene, composite sodium-based thickener, and base oil makes the resulting composite sodium-based grease, based on the weight of the grease, include the following components: 65-95% lubricating base oil, 5-30% Composite sodium-based thickener, 0.2-15% graphene.

[0029] Preferably, the amount of graphene, composite sodium-based thickener, and base oil makes the resulting composite sodium-based grease, based on grease weight, include the following components: 70-90% lubricating base oil, 8- 25% complex sodium-based thickener, 1-10% gr...

Embodiment 1

[0046] Preparation of graphene oxide:

[0047] Mix 1g of graphite flakes, 0.5g of sodium nitrate and 23ml of concentrated sulfuric acid in an ice bath, slowly add 3g of potassium permanganate while stirring, keep the temperature below 10°C and stir for 1h, then stir the mixture at 35°C for 0.5h, then add Dilute with 50ml of deionized water, a lot of heat is released during the process, keep the temperature below 100°C in an ice bath, after adding 50ml of water, stir the mixture for 0.5h, then add 200ml of deionized water for further dilution. Potassium permanganate was then reduced by adding 10 ml of a 30% by weight aqueous hydrogen peroxide solution. Finally, the mixture was washed and filtered with 5% hydrochloric acid (400ml) to remove metal ions. Then, the acid was removed with 0.5 L of deionized water, and dried at 60 °C for 24 h to obtain graphene oxide.

[0048] Preparation of graphene:

[0049] Add 0.1g of the graphene oxide prepared above to 100ml of water for ultr...

Embodiment 2

[0054] The preparation of graphene oxide is the same as in Example 1.

[0055] Preparation of graphene:

[0056] Add 0.1 g of the prepared graphene oxide into 100 ml of water for ultrasonic dispersion (ultrasonic frequency 35 kHz) for 30 min, then add 5 ml of hydrazine hydrate (mass concentration: 85%), and react in an oil bath at 100 ° C for 24 h. The powder obtained after water washing, suction filtration and drying is graphene, and the properties of graphene are shown in Table 2 below.

[0057] Preparation of complex sodium grease:

[0058] Raw material components: graphene 31.2g; 150BS base oil 420g (viscosity at 100°C is 31mm 2 / s); 23.26g sodium hydroxide; 13.40g terephthalic acid; 121.18g 12-hydroxystearic acid; 1.8g diisooctyl diphenylamine;

[0059] Add 31.2 grams of graphene, 210 grams of base oil and 121.18 grams of 12-hydroxystearic acid into the fat-making kettle, heat and stir, when the temperature rises to 90 ° C, add lye containing 23.26 grams of sodium hydr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
decomposition temperatureaaaaaaaaaa
drop melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite sodium-based lubricating grease and a preparation method thereof. Based on the grease weight, the complex sodium-based grease includes the following components: 65-95% lubricating base oil, 5-30% complex sodium-based thickener, and 0.2-15% graphene. The composite sodium-based lubricating grease of the present invention has excellent properties such as high temperature resistance, water resistance, adhesion, colloid stability, extreme pressure and wear resistance, lubrication life, corrosion resistance and salt spray resistance.

Description

technical field [0001] The invention relates to a lubricant material, in particular to a composite sodium-based lubricating grease and a preparation method thereof. Background technique [0002] Introducing a small amount of low-molecular-weight acidic compounds or their salts into sodium-based grease can obtain complex sodium-based grease with a dropping point higher than that of simple sodium soap. For example, adding a small amount of sodium salicylate soap to sodium fatty acid soap grease and heating it to 257°C can increase the dropping point of sodium-based grease. Simultaneously add 0.1-5% sodium acrylic acid salt in the lubricating grease that contains 5-35% fatty acid sodium soap, can reduce the solubility of sodium soap in water as US2468098; Morway et al. Molecular acid preparation of complex sodium grease. CN101153236A added solid powders with different particle size distributions to the grease, which not only enhanced the water resistance of the grease, but al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/06C10M123/02C10M177/00
Inventor 么佳耀郑会孙洪伟何懿峰段庆华张建荣陈政刘中其姜靓
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com