Anti-static anti-flaming oil-proof water-repellent polyester/linen blended fabric and preparation method thereof
A blended fabric and anti-static technology, which is applied in textiles, fabrics, textiles, and papermaking, can solve the problems of single anti-static, flame-retardant, oil-proof, and water-repellent functions, and achieve huge social and economic benefits and strong market competitiveness. , excellent performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0031] Example 1
[0032] An anti-static, flame-retardant, oil-proof and water-repellent polyester-cotton-linen blended fabric is prepared by the following method:
[0033] Step 1, anti-static grey fabric weaving
[0034] Twist 68% polyester, 14% cotton and 18% flax into polyester-cotton-linen blended yarn, and twist nylon 20D / 3F conductive yarn and polyester-cotton-linen blended yarn into conductive yarn. The grey fabric is woven with polyester-cotton-linen blended yarn as warp and weft. Conductive yarns are woven at intervals in the warp and weft directions while weaving. The distance between two adjacent conductive yarns in the warp direction is 0.5cm, and the adjacent ones in the weft direction The distance between the two conductive yarns is 0.5 cm. Prepare anti-static grey cloth.
[0035] Step two, dyeing
[0036] Perform dyeing pretreatment on the anti-static grey fabric of step 1, and then dip and roll on the dyeing machine, and then dry and soap to obtain an anti-static poly...
Example Embodiment
[0042] Example 2
[0043] An anti-static, flame-retardant, oil-proof and water-repellent polyester-cotton-linen blended fabric is prepared by the following method:
[0044] Step 1, anti-static grey fabric weaving
[0045] Twist 50% polyester, 30% cotton and 20% flax into polyester-cotton-linen blended yarn, and twist nylon 20D / 3F conductive yarn and polyester-cotton-linen blended yarn into conductive yarn. The grey fabric is woven with polyester-cotton-linen blended yarn as warp and weft. Conductive yarns are woven at intervals in the warp and weft directions while weaving. The distance between two adjacent conductive yarns in the warp direction is 1cm. The spacing of the conductive yarns is 1 cm. Prepare anti-static grey cloth.
[0046] Step two, dyeing
[0047] Perform dyeing pretreatment on the anti-static grey fabric of step 1, and then dip and roll on the dyeing machine, and then dry and soap to obtain an anti-static polyester-cotton-linen blended colored fabric.
[0048] Step th...
Example Embodiment
[0053] Example 3
[0054] An anti-static, flame-retardant, oil-proof and water-repellent polyester-cotton-linen blended fabric is prepared by the following method:
[0055] Step 1, anti-static grey fabric weaving
[0056] Twist 70% polyester, 15% cotton and 15% flax into polyester-cotton-linen blended yarn, and twist nylon 20D / 3F conductive yarn and polyester-cotton-linen blended yarn into conductive yarn. The grey fabric is woven with polyester-cotton-linen blended yarn as warp and weft. Conductive yarns are woven at intervals in the warp and weft directions while weaving. The distance between two adjacent conductive yarns in the warp direction is 2cm. The spacing of the conductive yarns is 2 cm. Prepare anti-static grey cloth.
[0057] Step two, dyeing
[0058] Perform dyeing pretreatment on the anti-static grey fabric of step 1, and then dip and roll on the dyeing machine, and then dry and soap to obtain an anti-static polyester-cotton-linen blended colored fabric.
[0059] Step th...
PUM
Property | Measurement | Unit |
---|---|---|
Concentration | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap