High-carbon non-tempered steel for breaking connecting rod and manufacturing method thereof

A technology of non-quenched and tempered steel and a manufacturing method, which is applied in the field of steel, and can solve problems such as failure to meet technical requirements, poor thermal processing performance, and low tensile strength, so as to improve fracture performance, strong precipitation strengthening, and improve processing performance Effect

Inactive Publication Date: 2015-07-15
BAOSHAN IRON & STEEL CO LTD
View PDF8 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] In summary, the fractured connecting rods in the prior art have the following defects: 1) low tensile strength; 2) p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-carbon non-tempered steel for breaking connecting rod and manufacturing method thereof
  • High-carbon non-tempered steel for breaking connecting rod and manufacturing method thereof
  • High-carbon non-tempered steel for breaking connecting rod and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0097] The high-carbon non-quenched and tempered steel for breaking connecting rods and its manufacturing method described in the present invention will be further explained and illustrated in conjunction with specific examples below. However, the explanations and illustrations do not constitute improper limitations on the technical solution of the present invention. .

[0098] The high-carbon non-quenched and tempered steel for the breakage connecting rod in Examples A1-A8 and Comparative Examples B1 and B2 was manufactured according to the following steps:

[0099] (1) Primary smelting in electric furnace: the primary smelting of molten steel is carried out in an electric arc furnace of 60-150 tons, and the slag is frequently flowed to remove P during the oxidation period.

[0100] (2) Ladle refining + vacuum degassing: After the initial deoxidation of LF, add an alloy block and stir for 5-10 minutes. When the temperature of the molten steel is measured T≥1580℃, enter the va...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high-carbon non-tempered steel for breaking a connecting rod and a manufacturing method thereof. The high-carbon non-tempered steel comprises the following chemical elements in percentage by weight: 0.65%-0.85% of C, 0.15%-0.25% of Si, 0.50%-0.60% of Mn, 0.010%-0.045% of P, 0.060%-0.070% of S, 0.10%-0.20% of Cr, 0.55%-0.80% of Ni, 0.03%-0.04% of V, 010%-0.20% of W, 0.0120%-0.0160% of N, 0.0001%-0.0004% of Re and the balance of Fe and inevitable impurities. The manufacturing method comprises the following steps: electric furnace primary smelting; ladle refining and vacuum degassing; die casting or continuous casting; and steel bar rolling. The high-carbon non-tempered steel has relatively high strength and good breaking performance.

Description

technical field [0001] The invention relates to a steel product, in particular to a non-quenched and tempered steel product. The invention also relates to a method for manufacturing the non-quenched and tempered steel. Background technique [0002] Non-quenched and tempered steel is a new type of energy-saving steel material that combines rolling (or forging) and heat treatment. This steel material can save the quenching and tempering treatment (that is, quenching + high temperature tempering). At present, non-quenched and tempered steel is generally used in automobile connecting rods. In terms of the development of non-quenched and tempered steels for connecting rods, the use of non-quenched and tempered steels for breaking connecting rods is also a new development idea. With the rapid development of the automobile industry, domestic and foreign automobile manufacturers continue to apply new technology to improve product quality, reduce product cost, and improve production...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/60
Inventor 安金敏丁毅覃明刘湘江
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka