Recyclable furan resin impregnation technology

A technology of furan resin and impregnation process, which is applied in the field of furan resin impregnation process, which can solve the problems of potential safety hazards, unusable and waste of furan resin, and achieve the effects of avoiding danger, reducing production cost and improving production efficiency

Inactive Publication Date: 2015-07-22
NANTONG CHENGGUANG GRAPHITE EQUIP
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the traditional artificial graphite furan resin impregnation process in China is to use an impregnation kettle to soak the artificial graphite electrode in acid, vacuumize, impregnate, cool, and dry. The main

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of recyclable furan resin impregnation process of the present invention comprises the following steps:

[0026] (1) Dust removal and drying: the graphite electrode is subjected to dust removal treatment to remove impurities and dust, and dried to an anhydrous state;

[0027] (2) Vacuuming: Put the dedusted and dried graphite electrode into the impregnation container to vacuumize to 0.08Mpa and keep it for 2 hours;

[0028] (3) First impregnation: Add furan resin into the impregnation container, vacuumize to 0.6Mpa, and keep it for 2 hours;

[0029] (4) Drain: Drain the resin attached to the graphite electrode to remove the resin tumor on the electrode surface;

[0030] (5) Solidification and cooling: solidify the graphite electrode at 160°C for 1 hour, and cool to room temperature;

[0031] (6) Vacuuming: Put the graphite electrode into the impregnation container again to vacuumize to 0.08Mpa and keep it for 2 hours;

[0032] (7) The second impregnation: ad...

Embodiment 2

[0040] A kind of recyclable furan resin impregnation process of the present invention comprises the following steps:

[0041] (1) Dust removal and drying: the graphite electrode is subjected to dust removal treatment to remove impurities and dust, and dried to an anhydrous state;

[0042] (2) Vacuuming: Put the dedusted and dried graphite electrode into the impregnation container to vacuumize to 0.08Mpa and keep it for 2 hours;

[0043] (3) First impregnation: Add furan resin into the impregnation container, vacuumize to 0.6Mpa, and keep it for 2 hours;

[0044] (4) Drain: Drain the resin attached to the graphite electrode to remove the resin tumor on the electrode surface;

[0045] (5) Solidification and cooling: solidify the graphite electrode at 180°C for 1 hour, and cool to room temperature;

[0046] (6) Vacuuming: Put the graphite electrode into the impregnation container again to vacuumize to 0.08Mpa and keep it for 2 hours;

[0047] (7) The second impregnation: ad...

Embodiment 3

[0055] A kind of recyclable furan resin impregnation process of the present invention comprises the following steps:

[0056] (1) Dust removal and drying: the graphite electrode is subjected to dust removal treatment to remove impurities and dust, and dried to an anhydrous state;

[0057] (2) Vacuuming: Put the dedusted and dried graphite electrode into the impregnation container to vacuumize to 0.08Mpa and keep it for 2 hours;

[0058] (3) First impregnation: Add furan resin into the impregnation container, vacuumize to 0.6Mpa, and keep it for 2 hours;

[0059] (4) Drain: Drain the resin attached to the graphite electrode to remove the resin tumor on the electrode surface;

[0060] (5) Solidification and cooling: solidify the graphite electrode at 170°C for 1 hour, and cool to room temperature;

[0061] (6) Vacuuming: Put the graphite electrode into the impregnation container again to vacuumize to 0.08Mpa and keep it for 2 hours;

[0062] (7) The second impregnation: ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a recyclable furan resin impregnation technology. The technology comprises dust removing and drying, vacuum pumping, impregnation, curing and cooling, vacuum pumping, impregnation, curing and cooling are performed repeatedly according to the technological steps, the vacuum pumping step refers to that a graphite electrode is subjected to vacuum pumping until the pressure is 0.08 Mpa and kept for 2 h, and during impregnation, the graphite electrode is subjected to vacuum pumping until the pressure is 0.6 Mpa and kept for 2 h; the curing step refers to that the graphite electrode is cured at the temperature of 160-180 DEG C for 1 h and then cooled to the normal temperature. According to the furan resin impregnation technology, an acid soaking technology is omitted, so that furan resin can be recycled, the production cost is reduced, and the enterprise benefit is increased.

Description

technical field [0001] The invention relates to the technical field of a graphite impregnation process, in particular to a recyclable furan resin impregnation process. Background technique [0002] At present, the traditional artificial graphite furan resin impregnation process in China is to use an impregnation kettle to soak the artificial graphite electrode in acid, vacuumize, impregnate, cool, and dry. The main disadvantage of the acid soaking step is that the graphite electrode is soaked in strong acid. The operation has brought potential safety hazards, and caused the furan resin to be unusable after repeated soaking in acid, thereby causing waste. Contents of the invention [0003] Purpose of the invention: The present invention aims at the deficiencies in the prior art and proposes a recyclable furan resin impregnation process. [0004] Technical solution: A recyclable furan resin impregnation process according to the present invention comprises the following step...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/48
Inventor 张月圆黄垭楹蒋锦锋陈萍
Owner NANTONG CHENGGUANG GRAPHITE EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap