Delustering high-strength low-elongation viscose fiber preparation technology
A viscose fiber, high strength and low elongation technology, applied in the field of textile fiber processing, can solve the problems of high cost and achieve the effects of improving brittleness, increasing elongation, and reducing damage to elongation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0099] A process for preparing matting high-strength low-extension viscose fiber. The pulp raw material is immersed in lye, after grinding, squeezing, pulverizing, and kneading, adding pure oxygen for directional polymerization reduction, removing the lye to obtain alkali cellulose. The alkali cellulose is yellowed and dissolved to obtain a cellulose sulfonate solution, and the cellulose sulfonate solution is filtered, defoamed, matured, spinning drawing and post-treatment to obtain high-strength and low-stretch viscose fibers. The viscose fiber prepared by this embodiment meets the following technical indicators:
[0100] Dry breaking strength≥3.10 cN / dtex;
[0101] Wet breaking strength≥1.60cN / dtex;
[0102] The strength required to produce 5% elongation in the wet state≥0.55cN / dtex,
[0103] Dry elongation at break 11.0~19.0%;
[0104] The wet elongation at break is 16.0~21.0%;
[0105] Radial water swelling degree is 22~26%;
[0106] The content of matting agent is 0.8-5%.
Embodiment 2
[0108] The difference between this embodiment and embodiment 1 is that the viscose fiber prepared according to the process of embodiment 1 also satisfies:
[0109] Whiteness≥85%;
[0110] Linear density deviation rate ≤±11.0%;
[0111] Residual sulfur≤12.0mg / 100g;
[0112] Length deviation rate≤±11.0%;
[0113] Super long fiber rate ≤0.5%;
[0114] Double length fiber≤4.0mg / 100g;
[0115] Defects ≤4.0mg / 100g.
Embodiment 3
[0117] A preparation process of matting high-strength low-extension viscose fiber, the steps are as follows:
[0118] A. Put the pulp raw material on the feeder meal first, set the feeding speed to 40kg / min, then add the raw material into the dipping bucket, after grinding by the grinder, make the porridge with a concentration of 3%. The purpose is to open and disperse the fiber through mechanical action, thereby increasing the alkalization speed and alkalization rate of cellulose;
[0119] B. The porridge prepared in step A is sent to a press, and after squeezing, it is sent to a pulverizer for pulverization to obtain alkali cellulose, which is sent to a kneader, and processed to obtain a porridge with a concentration of 30% In this step, the squeezer can remove the excess lye, and the excess lye can be recycled. The treatment method is to use a filter with a 60 mesh filter and a vacuum of -0.4MPa to remove the excess hemicellulose from the lye and recover it. Alkali fiber Vegeta...
PUM
Property | Measurement | Unit |
---|---|---|
Dry breaking strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap