Hot-melt adhesive for bookbinding and production method thereof

A technology for hot-melt adhesives and books and periodicals, applied in the directions of adhesives, rosin adhesives, wax adhesives, etc. Binding efficiency, beautiful binding effect

Active Publication Date: 2017-08-15
HEBEI WEIKE CHEM MATERIAL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the above-mentioned technical problems, the purpose of the present invention is to provide a hot-melt adhesive for binding books and periodicals that is pollution-free, has a wide bonding surface, cures quickly, does not need to be dried, and is easy to use, so as to solve the problem of the existing hot-melt adhesive for book binding. Defects of poor fluidity, yellowish color and low adhesion that cannot bind thick books and periodicals

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A hot-melt adhesive for bookbinding, which comprises paraffin, ethylene-vinyl acetate copolymer, terpene, rosin, styrene-butadiene rubber and antioxidant, wherein the weight fractions of the above components are respectively 10 parts of paraffin, ethylene - 56.75 parts of vinyl acetate copolymer, 15 parts of terpene, 5 parts of rosin, 3 parts of styrene-butadiene rubber and 0.25 part of antioxidant; 10 parts of pentaerythritol.

[0021] The production method of the hot-melt adhesive used for above-mentioned bookbinding, it comprises the following steps,

[0022] The first step is to add the above-mentioned amount of rosin powder into the reaction kettle equipped with a thermometer, depressurize to discharge the air in the reaction kettle, and pass in nitrogen gas, preheat for 15 minutes, and when the rosin is in a molten state, press the set amount in order Add terpene, styrene-butadiene rubber, and antioxidant into the reaction kettle according to the above-mentioned a...

Embodiment 2

[0026] A hot-melt adhesive for bookbinding, which includes paraffin, ethylene-vinyl acetate copolymer, terpene, rosin, styrene-butadiene rubber and antioxidant, wherein the weight fractions of the above components are respectively 25 parts of paraffin, ethylene - 30 parts of vinyl acetate copolymer, 20 parts of terpene, 9.2 parts of rosin, 5 parts of styrene-butadiene rubber and 0.8 part of antioxidant; 10 parts of pentaerythritol.

[0027] The production method of the hot-melt adhesive used for above-mentioned bookbinding, it comprises the following steps,

[0028] The first step is to add the above-mentioned amount of rosin powder into the reaction kettle equipped with a thermometer, depressurize to discharge the air in the reaction kettle, and pass in nitrogen gas, preheat for 15 minutes, and when the rosin is in a molten state, press the set amount in order Add terpene, styrene-butadiene rubber, and antioxidant into the reaction kettle according to the above-mentioned amou...

Embodiment 3

[0032] A hot-melt adhesive for bookbinding, which comprises paraffin, ethylene-vinyl acetate copolymer, terpene, rosin, styrene-butadiene rubber and antioxidant, wherein the weight fractions of the above components are respectively 10 parts of paraffin, ethylene - 39.2 parts of vinyl acetate copolymer, 20 parts of terpene, 10 parts of rosin, 5 parts of styrene-butadiene rubber and 0.8 part of antioxidant; 15 parts of pentaerythritol.

[0033] The production method of the hot-melt adhesive used for above-mentioned bookbinding, it comprises the following steps,

[0034] The first step is to add the above-mentioned amount of rosin powder into the reaction kettle equipped with a thermometer, depressurize to discharge the air in the reaction kettle, and pass in nitrogen gas, preheat for 15 minutes, and when the rosin is in a molten state, press the set amount in order Add terpene, styrene-butadiene rubber, and antioxidant into the reaction kettle according to the above-mentioned am...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

A hot melt adhesive for book binding is prepared from raw materials in parts by weight as follows: 10-25 parts of paraffin wax, 30-60 parts of an ethylene vinyl acetate copolymer, 15-25 parts of terpene, 5-10 parts of rosin, 3-5 parts of styrene-butadiene rubber, 0.25-0.8 parts of an antioxidant and 10-15 parts of pentaerythritol. The hot melt adhesive for book binding is pollution-free, wide in adhesion surface, fast to cure, drying-free and convenient to use, and can solve the problem that books with larger thickness cannot be bound due to poor liquidity, yellow color and small adhesion force of the conventional hot melt adhesive for book binding.

Description

technical field [0001] The invention belongs to the technical field of hot-melt adhesives, and in particular relates to a hot-melt adhesive for bookbinding and a production method thereof. Background technique [0002] In recent years, hot-melt adhesives for bookbinding have developed rapidly, and more and more bookbinding factories use hot-melt adhesives to bond books. This process has become the main method for binding books, and there is a tendency to further expand the scope of use in the future. , Market demand has promoted the rapid development of hot-melt adhesives for bookbinding. The development process of binding materials for books and periodicals is from the use of flour paste-synthetic resin glue polyvinyl acetate-polyvinyl alcohol-hot melt adhesives, especially the emergence of hot melt adhesives has greatly improved the speed of book binding processing and shortened the time for publishing books. cycle, adapted to the needs of publishing and society. [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J123/08C09J191/06C09J193/04C09J109/06C09J11/06
Inventor 赵中锋
Owner HEBEI WEIKE CHEM MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com