Novel graphene negative electrode active material for lead-acid battery and preparation method thereof

A graphene anode, lead-acid battery technology, applied in battery electrodes, circuits, electrical components and other directions, can solve the problems affecting battery cycle life, poor charging acceptance, poor performance, etc., to improve cycle life As well as the effect of high current charge and discharge capacity, improved performance, and enhanced electrical conductivity

Active Publication Date: 2017-05-03
江苏海宝电池科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The research and development of lead-carbon batteries will be a development trend of super batteries in the future, but the lead-acid batteries currently on the market have many shortcomings: such as poor charging acceptance and long charging time; negative electrode sulfation affects battery cycle use life; under extreme conditions such as high and low temperature, poor performance, etc.; therefore, there is an urgent need for a method to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel graphene negative electrode active material for lead-acid battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A new type of graphene negative electrode active material for lead-acid storage battery, its percentage by weight, colloidal graphite 1%, humic acid 0.8%, lignin 0.8%, barium sulfate 0.9%, polypropylene staple fiber 0.15%, polytetrafluoroethylene 0.12%, 0.09% polyvinyl alcohol; 0.15% 1,2-propanediol, 0.15% nano-powdered graphene, 1% acetylene black, 80% lead powder, 8% 1.4g / ml sulfuric acid, and the rest is high-purity deionized water .

Embodiment 2

[0022] A new type of graphene negative electrode active material for lead-acid storage battery, its percentage by weight, colloidal graphite 1.2%, humic acid 0.5%, lignin 0.3%, barium sulfate 1.2%, polypropylene staple fiber 0.07%, polytetrafluoroethylene 0.15%, 0.03% polyvinyl alcohol; 0.2% 1,2-propanediol, 0.3% nano-powder graphene, 0.8% acetylene black, 85% lead powder, 1.4g / ml sulfuric acid 7%, the rest is high-purity deionized water .

Embodiment 3

[0024] A new type of graphene negative electrode active material for lead-acid storage battery, which comprises 0.5% of colloidal graphite, 0.6% of humic acid, 0.8% of lignin, 0.5% of barium sulfate, 0.2% of polypropylene staple fiber, and polytetrafluoroethylene by weight percentage. 0.05%, 0.2% polyvinyl alcohol; 0.1% 1,2-propanediol, 0.1% nano-powdered graphene, 1.5% acetylene black, 75% lead powder, 1.4g / ml sulfuric acid 10%, the rest is high-purity deionized water .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

A novel graphene anode active compound used for lead-acid storage batteries is disclosed. The graphene anode active compound comprises following components by weight: 0.5-1.2% of colloidal graphite, 0.5-0.8% of humic acid, 0.3-0.8% of lignin, 0.5-1.2% of barium sulfate, 0.07-0.2% of staple fiber, 0.05-0.15% of polytetrafluoroethylene, 0.03-0.2% of poly(vinyl alcohol), 0.1-0.2% of 1,2-propanediol, 0.1-0.3% of graphene, 0.8-1.5% of acetylene black, 75-85% of lead powder and 7-10% of a diluted sulfuric acid solution, with the balance being deionized water. The graphene anode active compound enhances conductivity and low-temperature charge-discharge properties of anode plates and delays sulfation tendency of anode active compounds. Under the premise of not influencing the initial stage capacity of batteries, cyclic service lifetime of batteries is prolonged, high-current charge-discharge capability of batteries is improved, and using performance under extreme conditions is improved to a certain degree.

Description

technical field [0001] The invention relates to a novel negative electrode active material for lead-acid batteries using graphene as an additive; the invention also relates to a preparation method of the negative electrode active material. Background technique [0002] The research and development of lead-carbon batteries will be a development trend of super batteries in the future, but the lead-acid batteries currently on the market have many shortcomings: such as poor charging acceptance and long charging time; negative electrode sulfation affects battery cycle use life; under extreme conditions such as high and low temperatures, poor performance, etc.; therefore, a method to solve the above problems is urgently needed. Contents of the invention [0003] The object of the present invention is to provide a novel negative electrode active material using graphene as an additive and a preparation method thereof. [0004] The technical scheme adopted in the present invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/58H01M4/62
CPCH01M4/581H01M4/625Y02E60/10
Inventor 胡华闫智刚杨海涛沈维新
Owner 江苏海宝电池科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com