Vinylon and polyester white harness thread and production method thereof

A production method and thread technology, applied in textiles and papermaking, textile, yarn, etc., can solve problems such as fabric warp defect, thread breakage, large thread stretching, etc., to achieve increased friction coefficient, enhanced breaking strength, and stretchable rate drop effect

Inactive Publication Date: 2015-10-14
安徽创星实业有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The product is in the weaving factory, due to the large amount of expansion and contraction of the harness, it affects the normal production
Especially in the season when the air humidity is high, the expansion and contraction of the harness becomes larger, seriously reducing the weaving efficiency of the loom, and it is easier to cause warp defects of the fabric, and even the breakage of the harness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A production method of vinylon polyester white silk thread, comprising the following steps:

[0022] 1) For the yarn, one strand of 333dtex-466dtex polyester yarn and two strands of 29.5tex vinylon stretch-cut yarn are combined into one strand;

[0023] 2) Pre-twisting, twisting direction Z, number of strands, twisting twist / 100㎝, twisting with 1 strand that has been merged, and the twisting degree is 466-610 / m;

[0024] 3) Double twisting, twisting direction S, number of strands twist is twist / 100㎝, synthesize 3 strands with primary twisting, and then twist, twisting is 240-320 / m;

[0025] 4) Take the double-twisted 240-320 strands and wind them into stranded wires by the spinning machine;

[0026] 5) Sizing in the slurry tank, the concentration of the slurry is 15-25%;

[0027] 6) Put the stranded wire into the adjusted slurry, soaking time is 40 minutes to 70 minutes;

[0028] 7) Sizing the polyester stranded wire, remove 60-70% of the slurry by the dehydrator;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a vinylon and polyester white harness thread and a production method thereof. The production method comprises the following steps: 1) carrying out doubling; 2) carrying out first twisting; 3) carrying out second twisting; 4) winding 240-320 strands subjected to second twisting into a stranded thread by a yarn reeler; 5) mixing size in a size pool; 6) putting the stranded thread in the mixed size; 7) removing 60-70% of size from the sized polyester / vinylon stranded thread by a dehydrator; 8) putting the sized stranded thread on a waxed thread machine to undergo drafting setting for 15-25 minutes, carrying out manual waxing for 2-3 minutes when the dryness of the polyester / vinylon harness thread is 70-80%, and air-drying the thread after the thread comes off the waxed thread machine until the humidity is lower than 3%, thus preparing the vinylon and polyester white harness thread. The vinylon and polyester white harness thread provided by the invention has the advantages that the breaking strength is obviously enhanced; the ratio of expansion and contraction is reduced; the friction coefficient is increased by 30-60%.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a production method and a product of a wester white silk thread. Background technique [0002] At present, the weaving width of the jacquard loom is increasing, which puts forward higher requirements for the harness. For this reason, the development of a harness with high strength and low stretching rate has been used to ensure that the shed of the jacquard loom is clear and weaves smoothly. An urgent need. At the same time, the high-strength, low-stretch harness can effectively reduce the warp defects of the fabric. [0003] At present, the vinylon polyester white-toned yarn produced by common methods has low tensile breaking strength. The expansion and contraction of the harness is relatively large under a small load. When the product is in the weaving factory, due to the large amount of expansion and contraction of the harness, the normal production is affected...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03C3/40D02G3/44D02G3/04D02G3/28D06M15/333D06M15/507D06M101/32
CPCD03C3/40D02G3/045D02G3/28D02G3/44D06M15/333D06M15/507D06M2101/32D10B2321/06D10B2331/04
Inventor 刘克祥
Owner 安徽创星实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com