A constant expansion, high-strength technology, applied in the field of metal materials, can solve problems such as unsatisfactory alloys, and achieve the effect of improving purity, good mechanical properties, and promoting technological progress and industrial development.

Active Publication Date: 2015-12-09
CHONGQING MATERIALS RES INST
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] There is currently no alloy that meets the above properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-intensity controlled-expansion alloy containing Cr
  • High-intensity controlled-expansion alloy containing Cr
  • High-intensity controlled-expansion alloy containing Cr

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] High-strength constant expansion alloy, its chemical composition is calculated by weight percentage: C: 0.03; Si: 0.10; Mn: 0.60; Ni: 35.0; Cr: 2.5; Nb: 0.8; Co: 0.8; the balance is Fe;

[0060] The preparation method of the above-mentioned novel high-strength constant expansion alloy comprises the following steps:

[0061] a) Melting

[0062] Each component is weighed according to the weight percentage of its chemical composition. The alloy adopts vacuum induction melting. When vacuum induction melting is carried out, a secondary refining process is adopted. The first refining temperature is slightly higher and the time is slightly longer;

[0063] first refining

[0064] Put the base materials into the furnace: Fe, Nb, Co, Ni, Cr, melt at a temperature higher than 1600°C, and control the vacuum degree of 15-25Pa, and melt at a time of 0.6min / kg;

[0065] second refining

[0066] The second refining adopts low-temperature short-time refining, puts C, Si, and Mn into...

Embodiment 2

[0079] High-strength constant expansion alloy, its chemical composition is calculated by weight percentage: C: 0.05; Si: 0.20; Mn: 0.50; Ni: 37.5; Cr: 1.0; Nb: 0.8; Co: 1.0; the balance is Fe, produced Alloy ingots are hot-worked and cold-worked into alloy materials, which are used in seals.

[0080] The preparation method is the same as in Example 1. The obtained samples were tested, and the performance test values ​​are shown in Table 4:

[0081] Table 4 Example 1 sample performance test value

[0082]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-intensity controlled-expansion alloy containing Cr. The alloy comprises the following components in percentage by weight: not greater than 0.08% of C, not greater than 0.40% of Si, not greater than 1.0% of Mn, not greater than 0.010% of S, not greater than 0.010% of P, 35.0-38.0% of Ni, 0.8-2.5% of Cr, not greater than 1.0% of Nb, 0.5-1.5% of Co, and the balance Fe. The alloy is high in mechanical intensity under room temperature and high in dynamic elasticity modulus, and can be applied to precision instruments and equipment with special requirements or other precision instruments and equipment with such requirements.

Description

technical field [0001] The invention relates to a metal material, in particular to a Cr-containing high-strength constant expansion alloy. Background technique [0002] The main feature of the constant expansion alloy is that it has an expansion coefficient close to that of the sealed material such as glass or ceramics within a certain temperature range, so that the effect of matching (or non-matching) sealing can be achieved. Therefore, it can also be called sealing alloy. It is widely used as lead and structural material in electron tubes, transistors and integrated circuits. The so-called matched sealing means that the difference between the expansion coefficients of the alloy and the material to be sealed is less than 10% within the range from the sealing temperature to room temperature. "Air leak. [0003] At present, the main alloy grades of constant expansion alloys are: [0004] 1. Fe-Ni series constant expansion alloy [0005] Typical grades are: 4J42 alloy. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/52C22C33/04C21D6/00
Inventor 王方军王东哲张中美刘敏贺文海刘海定李永友喻峰
Owner CHONGQING MATERIALS RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap