Low-temperature kiln-changing erythema glaze for light-weight porcelain, its preparation and application method

A light-weight porcelain and erythema glaze technology, applied in the field of ceramic manufacturing, can solve the problems of inability to meet consumer needs, single glaze effect, large energy consumption, etc., to improve product quality and sales price, unique artistic sense, energy saving Effect

Active Publication Date: 2018-05-15
FUJIAN PROVINCE DEHUA COUNTY GRANGTOP CERAMICS CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional kiln-changing glaze is fired at medium and high temperature, the firing temperature is above 1200°C, and the firing time is mostly more than 12 hours. The high firing temperature, long time, and large energy loss lead to high cost and are not environmentally friendly; There are light-weight Baiyun pottery kiln-changing glazes with a single glaze effect and monotonous varieties, which cannot meet the needs of consumers with different personalities

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0022] The glaze is as follows in parts by weight: 40 parts of glass powder, 30 parts of transparent frit glaze, 10 parts of red material, 5 parts of nepheline powder, 5 parts of boric acid, 8 parts of kaolin, and 2 parts of zinc oxide.

[0023] The preparation method of the above-mentioned light-weight porcelain low-temperature kiln erythema glaze comprises the following steps:

[0024] Step 1: Put glass powder, transparent frit glaze, nepheline powder, boric acid, kaolin, and zinc oxide into a ball mill jar according to the weighing ratio of the glaze, and add 60% of water;

[0025] Step 2, after ball milling for 12 hours, put the red material into the ball mill jar and mill together for 30 minutes;

[0026] In step 3, the glaze obtained in step 2 is passed through a 200-mesh sieve for use, so as to obtain the kiln erythema glaze.

[0027] The method of using the low-temperature kiln erythema glaze for light porcelain comprises the following steps:

[0028] Step 1, prepari...

specific Embodiment 2

[0031] The glaze is as follows in parts by weight: 42 parts of glass powder, 28 parts of transparent frit glaze, 6 parts of red material, 8 parts of nepheline powder, 6 parts of boric acid, 5 parts of kaolin, and 5 parts of zinc oxide.

[0032] The preparation method of the light-weight porcelain low-temperature kiln erythema glaze described in specific embodiments 2 to 4 comprises the following steps:

[0033] Step 1: Put glass powder, transparent frit glaze, nepheline powder, boric acid, kaolin, and zinc oxide into a ball mill jar according to the weighing ratio of the glaze, and add 50-60% of water;

[0034] Step 2: After ball milling for 10-15 hours, put the red material into the ball mill jar and mill together for 20-40 minutes;

[0035] In step 3, the glaze obtained in step 2 is passed through a 200-mesh sieve for use, so as to obtain the kiln erythema glaze.

[0036] The using method of the light-weight porcelain low-temperature kiln erythema glaze described in specifi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of ceramic manufacturing, and in particular relates to a kiln-transformed glaze formula, preparation method and application method for firing light-weight porcelain. The formula of the low-temperature kiln-changing erythema glaze for light-weight porcelain includes glass powder, transparent frit glaze, red material, nepheline powder, boric acid, kaolin, and zinc oxide. The kiln-changing erythema glaze formula glaze has low cost, is convenient to use, has a low firing temperature and has a unique artistic sense. The glaze effect produced by this kind of kiln-change erythema glaze has a red or copper-red background color, and irregular black spots are evenly distributed on the background color. The size and density of the black spots depend on the type of ceramic and the glaze The thickness varies, with a unique artistic effect. Porcelain made with this kind of glaze improves the product grade and sales price, and has high economic value; in addition, this kind of glaze can be mass-produced industrially, can be popularized quickly, is easy to use, and has strong competitiveness in the market.

Description

technical field [0001] The invention belongs to the field of ceramic manufacturing, and in particular relates to a kiln-transformed glaze for firing light porcelain, a preparation method and a use method. Background technique [0002] Kiln-changing glaze means that when the utensils are fired in the kiln, due to the oxidation or reduction of various color elements in the kiln, they will show unexpected glaze color effects after they come out of the kiln. The traditional kiln-changing glaze is fired at medium and high temperature, the firing temperature is above 1200°C, and the firing time is mostly more than 12 hours. The high firing temperature, long time, and large energy consumption lead to high cost and are not environmentally friendly; There are light-weight Baiyun pottery kiln-changing glazes with a single glaze effect and monotonous varieties, which cannot cater to the needs of consumers with different personalities. [0003] In order to solve the above problems, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86
Inventor 李桂贤刁龙海
Owner FUJIAN PROVINCE DEHUA COUNTY GRANGTOP CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap