Iron hoop

A technology of iron hoop and protective film, applied in coatings, anti-corrosion coatings, epoxy resin coatings, etc., can solve the problems to be improved and achieve excellent wear resistance.

Inactive Publication Date: 2016-02-03
CHANGSHU FUDA METAL PROD CO LTD
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The wear resistance, anti-scaling, anti-aging, anti-oxidation, corrosion resistance and weather resistance of existing iron hoops need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] An iron hoop with a protective film attached to the surface of its main body, the protective film is composed of the following components in parts by weight:

[0015] 1-2 parts of dimolybdenum boride, 10.2 parts of modified epoxy resin, 2.3 parts of tetraethylamine tetrafluoroborate, 1.2 parts of vinyl trimethoxysilane, 0.7 parts of γ-glycidyl ether trimethoxysilane, 0.9 parts of pentaerythritol, 2.8 parts of pentaerythritol, 1.9 parts of xylene.

Embodiment 2

[0017] The iron hoop has a protective film attached to the surface of its main body, and the protective film is composed of the following components in parts by weight:

[0018] 1 part of dimolybdenum boride, 10.2 parts of modified epoxy resin, 2.3 parts of tetraethylamine tetrafluoroborate, 1.2 parts of vinyl trimethoxysilane, 0.7 parts of γ-glycidyl ether trimethoxysilane, 0.9 parts Pentaerythritol, 2.8 parts pentaerythritol, 1.9 parts xylene.

Embodiment 3

[0020] The iron hoop has a protective film attached to the surface of its main body, and the protective film is composed of the following components in parts by weight:

[0021] 2 parts of dimolybdenum boride, 10.2 parts of modified epoxy resin, 2.3 parts of tetraethylamine tetrafluoroborate, 1.2 parts of vinyl trimethoxysilane, 0.7 parts of γ-glycidyl ether trimethoxysilane, 0.9 parts Pentaerythritol, 2.8 parts pentaerythritol, 1.9 parts xylene.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an iron hoop. A protective film is adhered to the surface of a main body of the iron hoop, and the protective film comprises the following components in parts by weight: 1-2 parts of Mo2B, 10.2 parts of modified epoxide resin, 2.3 parts of tetraethylammonium tetrafluoroborate, 1.2 parts of vinyl trimethoxysilane, 0.7 part of gamma-epoxypropylether trimethoxysilane, 0.9 part of pentaerythritol, 2.8 parts of pentaerythritol and 1.9 parts of xylene. The iron hoop disclosed by the invention has good wear resistance, scale prevention, ageing resistance, oxidation resistance, corrosion resistance and weather resistance as the protective film is adhered to the surface of the main body of the iron hoop.

Description

technical field [0001] The present invention relates to iron hoops. Background technique [0002] The wear resistance, anti-scaling, anti-aging, anti-oxidation, corrosion resistance and weather resistance performance of the existing iron hoop all need to be improved. Contents of the invention [0003] The object of the present invention is to provide an iron hoop with a protective film attached to the surface of its main body, which has excellent wear resistance, anti-scaling, anti-aging, anti-oxidation, corrosion resistance and weather resistance. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of iron hoop, the surface of its main body is attached with a protective film, and the protective film is composed of the following components in parts by weight: [0005] 1-2 parts of dimolybdenum boride, 10.2 parts of modified epoxy resin, 2.3 parts of tetraethylamine tetrafluoroborate, 1.2 parts of vinyl trimeth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/08C09D7/12
Inventor 陈震
Owner CHANGSHU FUDA METAL PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap