Environmentally friendly high-strength waterproof membrane self-adhesive

A waterproof membrane and self-adhesive technology, which is applied in the direction of non-polymer adhesive additives, adhesives, wax adhesives, etc., can solve the problems of unsatisfactory, unfavorable environmental protection of asphalt-based self-adhesive, and achieve oxidation resistance Improvement, the process of adding raw materials is simple and easy, and the effect of good compatibility

Active Publication Date: 2018-04-13
GUIZHOU LANTU NEW MATERIALS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Self-adhesive waterproof membranes generally include self-adhesive polymer modified bitumen waterproof membranes and waterproof membranes with self-adhesive layers (divided into asphalt-based membranes and polymer membranes). Currently, waterproof membranes with self-adhesive layers are on the market. Most of the self-adhesives used in materials are made of polymer-modified asphalt base. Although the base asphalt has been modified by high-molecular polymers, the performance meets the construction and waterproof requirements, but it is still far from meeting the requirements of construction and construction in terms of durability. Requirements for the same life expectancy, and asphalt-based self-adhesives are not conducive to environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1 of the present invention: environment-friendly high-strength waterproof coiled material self-adhesive, calculated in parts by mass, including 10 parts of styrene-butadiene-styrene thermoplastic elastomer, 50 parts of chlorinated paraffin, and 50 parts of tackifying resin and 0.1 part of antioxidant; the chlorinated paraffin is 52-type chlorinated paraffin, and its viscosity at 50°C is 500-1500mPa.s; the tackifying resin includes C5 resin, terpene resin and rosin resin, Calculated by mass percentage, rosin resin is 20%, terpene resin 40%, carbon five resin 40%, total 100%; the softening point of described carbon five resin is 80~120 ℃, and average molecular weight is 500~2500; The antioxidant is antioxidant 1010; the mass ratio of styrene and butadiene in the styrene-butadiene-styrene thermoplastic elastomer is 30 / 70.

[0014] The preparation method of environmentally friendly high-strength waterproof membrane self-adhesive adhesive is to take each component...

Embodiment 2

[0015] Embodiment 2 of the present invention: environment-friendly high-strength waterproof coil self-adhesive, calculated in parts by mass, including 20 parts of styrene-butadiene-styrene thermoplastic elastomer, 40 parts of chlorinated paraffin, and 40 parts of tackifying resin and 0.5 parts of antioxidant; the chlorinated paraffin is 52-type chlorinated paraffin, and its viscosity at 50°C is 500-1500mPa.s; the tackifying resin includes C5 resin, terpene resin and rosin resin, Calculated by mass percentage, rosin resin is 25%, terpene resin 40%, carbon five resin 35%, total 100%; the softening point of described carbon five resin is 80~120 ℃, and average molecular weight is 500~2500; The antioxidant is antioxidant 1010; the mass ratio of styrene and butadiene in the styrene-butadiene-styrene thermoplastic elastomer is 30 / 70.

[0016] The preparation method is the same as in Example 1.

[0017] The required waterproof membrane self-adhesive is obtained. The peel strength of ...

Embodiment 3

[0018] Embodiment 3 of the present invention: environment-friendly high-strength waterproof coil self-adhesive, calculated in parts by mass, including 30 parts of styrene-butadiene-styrene thermoplastic elastomer, 40 parts of chlorinated paraffin, and 40 parts of tackifying resin and 1 part of antioxidant; the chlorinated paraffin is 52-type chlorinated paraffin, and its viscosity at 50°C is 500-1500mPa.s; the tackifying resin includes C5 resin, terpene resin and rosin resin, Calculated by mass percentage, rosin resin is 15%, terpene resin 45%, carbon five resin 40%, total 100%; the softening point of described carbon five resin is 80~120 ℃, and average molecular weight is 500~2500; The antioxidant is antioxidant 1010; the mass ratio of styrene and butadiene in the styrene-butadiene-styrene thermoplastic elastomer is 30 / 70.

[0019] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
softening pointaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides an environment-friendly high-strength waterproof coiled material self-adhesive. The SBS thermoplastic elastomer of the present invention can increase the toughness and elasticity of the system; the compatibility between chlorinated paraffin and SBS is good, can reduce the glass transition temperature of the system, and reduce the processing temperature; the carbon five resin in the tackifying resin has good tackifying properties and heat resistance, can increase the viscosity of the system and widen the construction temperature; the mixture of rosin resin and terpene resin is used as a tackifier to improve the adhesion of the system; the addition of antioxidants improves the oxidation resistance of the system, and the present invention The technical solution has the advantages of simple production without special production equipment; reasonable process and simple and easy raw material addition process. The self-adhesive of the present invention is light yellow in shape, has extremely high peel strength and shear strength at room temperature, has excellent adhesion to various polar and non-polar materials, has high performance, and is environmentally friendly. Simple, can be used for low temperature coating at 120°C, and is energy-saving and environmentally friendly, and can be widely used in engineering construction.

Description

technical field [0001] The invention relates to the field of adhesives, in particular to an environment-friendly self-adhesive adhesive for high-strength waterproof coiled materials. Background technique [0002] Since the 1990s, self-adhesive waterproof membrane, as a new type of building waterproof material, has rapidly become popular in my country's industrial and civil construction, construction, It has been popularized and applied in subway tunnels, bridge deck waterproofing and other fields. Self-adhesive waterproof membranes generally include self-adhesive polymer modified bitumen waterproof membranes and waterproof membranes with self-adhesive layers (divided into asphalt-based membranes and polymer membranes). Currently, waterproof membranes with self-adhesive layers are on the market. Most of the self-adhesives used in materials are made of polymer-modified asphalt base. Although the base asphalt is modified by high-molecular polymers, the performance meets the con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J191/06C09J153/02C09J157/02C09J145/00C09J193/04C09J11/06
Inventor 杨再祥陈小平石文建黄安荣雷勇王德军陈洋
Owner GUIZHOU LANTU NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More