Forming method of cobalt-based high-temperature alloy multi-step large special-shaped ring

A high-temperature alloy and special-shaped ring technology, applied in metal rolling, metal processing equipment, etc., can solve the problems of affecting the forming effect, unreasonable matching between blank and mold, unreasonable blank or mold design, etc. many effects

Inactive Publication Date: 2016-03-16
GUIZHOU ANDA AVIATION FORGING
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For complex multi-step special-shaped rings, when this method is used for forming, the forming effect will be seriously affected due to the unreasonable design of the blank or the mold, or the unreasonable matching of the blank and the mold during the rolling process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forming method of cobalt-based high-temperature alloy multi-step large special-shaped ring
  • Forming method of cobalt-based high-temperature alloy multi-step large special-shaped ring
  • Forming method of cobalt-based high-temperature alloy multi-step large special-shaped ring

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0032] The main chemical element content (percentage by weight) of the alloy is: 0.05% to 0.15% of C content, 20.0% to 24.0% of Cr content, 20.0% to 24.0% of Ni content, 13.0% to 16.0% of W content, 13.0% to 16.0% of W content, La content 0.03% ~ 0.12%, Si content 0.20% ~ 0.50%, Fe content ≤ 0.30%, B content ≤ 0.015%, Mn content ≤ 1.25%, P content ≤ 0.020%, S content ≤ 0.015 %, containing Ag ≤ 0.0010%, containing Bi ≤ 0.0001%, containing Pb ≤ 0.0010%, containing Cu ≤ 0.07%, and the balance being Co.

[0033] The steps of this method are as follows:

[0034] Step 1: Prepare intermediate ring blank

[0035] Such as figure 1 As shown, according to the structural characteristics of the cobalt-based superalloy multi-step large-scale special-shaped ring 1, the cross-section of the forging is cut layer by layer equidistantly from the height direction with the help of drawing software, and the cross-sectional area data of the multi-step large-scale special-shaped ring 1 is obtained ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a forming method of a cobalt-based high-temperature alloy multi-step large special-shaped ring. The forming method comprises the following steps: firstly, adopting drawing software to assist the preparation of an intermediate ring blank, and putting the intermediate ring blank in a ring rolling mill for rolling; during rolling, elevating a worktable top where the intermediate ring blank is located by 5mm-10mm to enable a main roller to contact with a lower end of the intermediate ring blank firstly and guarantee the filling of a die cavity with a metal material starting from bottom to top, thereby gradually completing the formation of all the steps, and then bulging the rolled multi-step large special-shaped ring. Such a method is capable of forming the multi-step large special-shaped ring, and also capable of effectively avoiding a phenomena of rib deviation or rib crossing during the formation of the multi-step large special-shaped ring, thereby improving the properties of the forging. The method is suitable for the formation of the cobalt-based high-temperature alloy multi-step large special-shaped rings.

Description

technical field [0001] The invention relates to a forming method of a multi-step large-scale special-shaped ring, in particular to a forming method of a cobalt-based superalloy multi-step large-scale special-shaped ring. Background technique [0002] Special-shaped ring forgings are designed according to the contour of the part, which can effectively improve the utilization rate of materials, obtain ideal performance and streamlines that match the contour of the part. However, in reality, the shape of parts is often strange, and it is difficult to design completely according to the outline of the part. It can only be designed as a special-shaped ring forging that is similar to the cross-section of the part and is relatively simple. Compared with the rectangular ring forging, this method uses more materials. Although the rate has increased, the amount of improvement is limited. At present, most of the special-shaped rings formed by rolling are simple special-shaped rings, fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21H1/06B21H1/22B21J5/00
CPCB21H1/06B21H1/22B21J5/002
Inventor 谢永富陈祖祥吕日红杨亚平陈红芳
Owner GUIZHOU ANDA AVIATION FORGING
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com