Preparation method of healthy type low temperature hot melt adhesive

A low-temperature heat, hot-melt adhesive technology, applied in the direction of adhesives, adhesive types, polyurea/polyurethane adhesives, etc. It can improve the air quality in the shoes, optimize the surrounding environment of the human body, and improve the quality uniformity.

Active Publication Date: 2016-03-16
HANGZHOU KAIYUE NEW MATERIAL CO LTD
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The low-temperature hot-melt adhesives in the prior art have the following disadvantages: the air permeability is average, so that the inside of the shoes cannot completely remove the sweat from the human feet, and the effect of sweat-absorbing, dehumidifying and drying cannot be achieved, so that the long-term humid environment promotes the reproduction of bacteria and causes foot ulcers. A series of foot diseases such as athlete's foot, odor, and even rot and peeling occur. Similarly, poor moisture absorption and drying performance will also breed mold on car interiors and leather goods, reducing their service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The preparation method of healthy low-temperature hot-melt adhesive, raw materials include the following components by weight percentage: 45 parts of TPU hot-melt adhesive resin, 10 parts of PETG, 25 parts of negative ion / bamboo activated carbon composite material, 3 parts of compatibilizer

[0024] (1) Put the above-mentioned raw materials into the storage mechanism and remove metal through high-intensity magnetism;

[0025] (2) Transport each raw material into the material tank and stir for 30 minutes until uniform;

[0026] (3) The stirred raw materials are transported to the feed hopper of the tape casting extruder after secondary strong magnetic demetallization, and are fed to the screw machine at a constant speed by the metering and feeding mechanism according to the preset quantity, and then passed through the screw machine 130 ℃ high-temperature melting and kneading to uniformly cast into sheets, and then cold-pressed to shape;

[0027] The TPU hot melt adhesiv...

Embodiment 2

[0032] The preparation method of healthy low-temperature hot-melt adhesive, raw materials include the following components by weight: 60 parts of TPU hot-melt adhesive resin, 20 parts of PETG, 30 parts of negative ion / bamboo activated carbon composite material, 5 parts of compatibilizer, and 1 part of organic bentonite ,

[0033] (1) Put the above-mentioned raw materials into the storage mechanism and remove metal through high-intensity magnetism;

[0034] (2) Transport each raw material to the material tank and stir for 45 minutes until uniform;

[0035] (3) The stirred raw materials are transported to the feed hopper of the casting extruder after secondary strong magnetic demetallization, and are fed to the screw machine at a constant speed by the metering and feeding mechanism according to the preset quantity, and then passed through the screw machine 150 ℃ high-temperature melting and kneading to uniformly cast into sheets, and then cold-pressed to shape;

[0036] The TP...

Embodiment 3

[0041] The preparation method of healthy low-temperature hot-melt adhesive, raw materials include the following components by weight: 51 parts of TPU hot-melt adhesive resin, 15 parts of PETG, 28 parts of negative ion / bamboo activated carbon composite material, 4 parts of compatibilizer, 2 parts of organic bentonite ;

[0042] (1) Put the above-mentioned raw materials into the storage mechanism and remove metal through high-intensity magnetism;

[0043] (2) Transport each raw material to the material tank and stir for 40 minutes until uniform;

[0044] (3) The stirred raw materials are transported to the feed hopper of the tape casting extruder after secondary strong magnetic demetallization, and are fed to the screw machine at a constant speed by the metering and feeding mechanism according to the preset quantity, and then passed through the screw machine 130 -150℃ high-temperature melting, kneading, uniform casting into sheets, and then cold pressing to shape;

[0045] The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a healthy type low temperature hot melt adhesive, which comprises the following components by weight: 45-60 parts of TPU hot melt adhesive resin, 10-20 parts of PETG, 25-30 parts of a negative ion / bamboo-based activated carbon composite material, and 3-5 parts of a compatilizer. The method includes: (1) putting the raw materials into a material storage mechanism respectively to remove metals by high strong magnetism; (2) conveying the raw materials into a material cylinder to conduct complete stirring for 30-45min to an even state; and (3) subjecting the well mixed raw materials to secondary metal removal by strong magnetism, then conveying the treated raw materials to the feed hopper of a tape casting extruder, conducting constant speed feeding to a screw machine by a metering feed mechanism according to a preset quantity, carrying out 130-150DEG C high temperature melt mixing evenly by the screw machine to perform tape casting into a sheet, and then conducting cold pressing shaping. The healthy type low temperature hot melt adhesive provided by the invention contains organic bentonite, can significantly improve the quality homogeneity and breathability homogeneity of low temperature hot melt adhesive, and has greatly improved breathability and high quality.

Description

technical field [0001] The invention relates to a preparation method of hot melt adhesive, in particular to a preparation method of healthy low-temperature hot melt adhesive. Background technique [0002] The low-temperature hot-melt film has extremely high elasticity, excellent rigidity, and strong flexibility. The three-dimensional effect is more excellent after the front and rear are solidified and shaped. Smooth lines, comfortable to wear, excellent elasticity, long-lasting shape, no need to apply glue, good adhesion, extremely convenient operation, and can be reused, the product is green and environmentally friendly. Leftovers can be recycled and reused. It is an environmentally friendly material that replaces traditional materials. At present, the low-temperature hot-melt film on the shoe material market can be used in various types of shoe shaping midsoles and automotive interiors, luggage, handbags, stationery, toys, leather goods, furniture and other fields. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/04C09J11/04
CPCC08L2205/03C09J11/04C09J175/04C08L67/02C08L67/00C08K3/04C08K3/346
Inventor 傅陆军
Owner HANGZHOU KAIYUE NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products