Waterproof material production method

A technology of waterproof material and production method, which is applied in the field of waterproof material production, can solve the problems of flexibility, water resistance and anti-cracking performance to be improved, and achieve the effect of good flexibility

Inactive Publication Date: 2016-04-20
江苏格雷特复合材料有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing kitchen and bathroom products need to be improved in terms of flexibility, water resistance, and crack resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for producing a waterproof material, comprising the steps of:

[0021] 1) Mix 1-2 parts by weight of hexyldecanol, 3.5 parts by weight of chlorinated paraffin, 1.8 parts by weight of sodium lauryl sulfate, 8.5 parts by weight of silicon-acrylic emulsion, and 15 parts by weight of water to prepare component A;

[0022] 2) 2.6 parts by weight of amorphous α-olefin copolymer, 2.3 parts by weight of Portland cement, 1.7 parts by weight of polyethylene glycol octylphenyl ether, 2.4 parts by weight of hydroxypropyl methylcellulose, 8.1 parts by weight Quartz sand is mixed evenly to obtain component B;

[0023] 3) Mix 6.7 parts by weight of component A and 3.5 parts by weight of component B, heat to 50°C, stir evenly, and cool naturally to prepare a waterproof material.

Embodiment 2

[0025] A method for producing a waterproof material, comprising the steps of:

[0026] 1) Mix 1 part by weight of hexyldecanol, 3.5 parts by weight of chlorinated paraffin, 1.8 parts by weight of sodium lauryl sulfate, 8.5 parts by weight of silicon acrylic emulsion, and 15 parts by weight of water to prepare component A;

[0027] 2) 2.6 parts by weight of amorphous α-olefin copolymer, 2.3 parts by weight of Portland cement, 1.7 parts by weight of polyethylene glycol octylphenyl ether, 2.4 parts by weight of hydroxypropyl methylcellulose, 8.1 parts by weight Quartz sand is mixed evenly to obtain component B;

[0028] 3) Mix 6.7 parts by weight of component A and 3.5 parts by weight of component B, heat to 50°C, stir evenly, and cool naturally to prepare a waterproof material.

Embodiment 3

[0030] A method for producing a waterproof material, comprising the steps of:

[0031] 1) Mix 2 parts by weight of hexyldecanol, 3.5 parts by weight of chlorinated paraffin, 1.8 parts by weight of sodium lauryl sulfate, 8.5 parts by weight of silicon acrylic emulsion, and 15 parts by weight of water to prepare component A;

[0032] 2) 2.6 parts by weight of amorphous α-olefin copolymer, 2.3 parts by weight of Portland cement, 1.7 parts by weight of polyethylene glycol octylphenyl ether, 2.4 parts by weight of hydroxypropyl methylcellulose, 8.1 parts by weight Quartz sand is mixed evenly to obtain component B;

[0033] 3) Mix 6.7 parts by weight of component A and 3.5 parts by weight of component B, heat to 50°C, stir evenly, and cool naturally to prepare a waterproof material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterproof material production method. The method comprises the steps of 1, evenly mixing 1-2 parts by weight of hexyldecanol, 3.5 parts by weight of chlorinated paraffin, 1.8 parts by weight of lauryl sodium sulfate, 8.5 parts by weight of silicone acrylic emulsion and 15 parts by weight of water, so that a component A is obtained; 2, evenly mixing 2.6 parts by weight of amorphous state alpha-olefin copolymer, 2.3 parts by weight of portland cement, 1.7 parts by weight of polyethylene glycol octylphenol ether, 2.4 parts by weight of hydroxy propyl methylcellulose and 8.1 parts by weight of quartz sand, so that a component B is obtained; 3, mixing 6.7 parts by weight of component A and 3.5 parts by weight of component B, increasing temperature to 50 DEG C, and conducting even stirring and natural cooling, so that a waterproof material is obtained. The waterproof material prepared with the method has high flexibility, water resistance and cracking resistance and is suitable for manufacturing kitchen and toilet products.

Description

technical field [0001] The invention relates to a production method of waterproof material. Background technique [0002] The existing kitchen and bathroom products need to be improved in terms of flexibility, water resistance, and anti-cracking performance. Contents of the invention [0003] The object of the present invention is to provide a production method of a waterproof material. The prepared waterproof material has good flexibility, water resistance and crack resistance, and is suitable for preparing kitchen and bathroom products. [0004] In order to achieve the above object, the technical solution of the present invention is to design a production method of waterproof material, comprising the steps of: [0005] 1) Mix 1-2 parts by weight of hexyldecanol, 3.5 parts by weight of chlorinated paraffin, 1.8 parts by weight of sodium lauryl sulfate, 8.5 parts by weight of silicon-acrylic emulsion, and 15 parts by weight of water to prepare component A; [0006] 2) 2....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B24/00C04B24/02C04B24/16C04B24/42C04B14/06C04B24/26C04B24/32C04B24/38C04B111/27
CPCC04B40/0039C04B28/04C04B2111/27C04B24/00C04B24/02C04B24/16C04B24/42C04B24/2611C04B24/32C04B24/383C04B14/06
Inventor 张志刚
Owner 江苏格雷特复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com