Two-step splitting method of polyester and polyamide composite super-fine fibers

A superfine fiber, polyester nylon composite technology, applied in the direction of fiber type, fiber treatment, plant fiber, etc., can solve the problems of fabric winding resilience and flatness decrease, fiber stiffness decrease, fabric thickness and gram weight decrease, etc. , to avoid the decrease of fiber breaking strength, reduce the amount of fiber opening liquid, and achieve the effect of sufficient strength

Active Publication Date: 2016-04-20
无锡市天华超净科技有限公司
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the greater the fiber opening, the greater the alkali loss, and the ultra-fine fibers continue to be hydrolyzed and become thinner, so the strength of the monofilament becomes smaller, the fiber stiffness (fiber breaking strength) decreases, and the thickness and grammage of the fabric also decrease. As a result, the fabric structure is loose, the winding resilience and flatness of the fabric are reduced, and the strength is also reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Two-step splitting method of polyester and polyamide composite super-fine fibers
  • Two-step splitting method of polyester and polyamide composite super-fine fibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] Objects, advantages and features of the present invention will be illustrated and explained by the following non-limiting description of preferred embodiments. These embodiments are only typical examples of applying the technical solutions of the present invention, and all technical solutions formed by adopting equivalent replacements or equivalent transformations fall within the protection scope of the present invention.

[0030] The invention discloses a two-step fiber-opening method for polyester-nylon composite superfine fibers, which adopts the two-step method of alkali-weight reduction fiber-opening (chemical process) and then mechanical fiber-opening, which changes the traditional process and generally only uses chemical technology to open fibers. Fibrous habitual thinking.

[0031] Specifically, the method includes the following steps:

[0032] S1, Alkali reduction and fiber opening step: set the specified weight of polyester-nylon composite microfiber cloth on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a two-step splitting method of polyester and polyamide composite super-fine fibers. The method comprises the steps that 1, the alkaline deweighting splitting step is conducted, wherein two large friction surface guide wheels of a liquid flow dyeing machine are coated with polyester and polyamide composite super-fine fiber cloth, and the splitting rate of the polyester and polyamide composite super-fine fiber cloth is made to reach a first preset value through splitting conducted at first splitting temperature, specified impact water pressure and guide wheel rotating speed within first time in a first splitting solution and an auxiliary; 2, the mechanical splitting step is conducted, wherein mechanical splitting is conducted on the polyester and polyamide composite super-fine fiber cloth which is subjected to alkaline deweighting splitting and arranged on the large friction surface guide wheels of the liquid flow dyeing machine at second splitting temperature and specified water flow impact speed, water temperature and guide wheel speed within second time in a second splitting solution and an auxiliary, and the splitting rate of the polyester and polyamide composite super-fine fiber cloth subjected to mechanical splitting is made to reach a second preset value. The two-step splitting method of the polyester and polyamide composite super-fine fibers has the advantages that a chemical and mechanical secondary splitting method is adopted, the influence of chemical agents on the physical property of the fibers can be reduced, and the alkaline deweighting quantity can be controlled in a lower range.

Description

technical field [0001] The invention relates to a fiber opening method, in particular to a two-step fiber opening method for polyester-nylon composite superfine fibers. Background technique [0002] Polyester-nylon composite is a composite fiber produced by composite spinning technology. Polyester-nylon composite fiber becomes superfine fiber after fiber opening. [0003] As the most basic requirement of the automatic production line reel cloth (polyester-nylon composite microfiber cloth) is: full fiber opening (usually when the fiber opening rate of polyester-nylon composite superfine fiber reaches 60%, it can be considered that the fiber opening meets the requirements); at the same time, There must be sufficient strength and thickness, as well as the winding resilience of the fabric, and the best flatness, so as to ensure the long-term stable operation of the cloth surface on the automatic wiping line. [0004] However, the fiber opening of the existing polyester / nylon co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06B1/14D06B23/02D06M11/38D06M101/32D06M101/06
CPCD06B1/145D06B23/023D06M11/38D06M2101/06D06M2101/32
Inventor 臧锡炎许陶飞
Owner 无锡市天华超净科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products