Graphene modified natural emulsion preparation method and high barrier condom

A technology of graphene modification and natural latex, which is applied in the direction of male contraceptives, etc., can solve the problem of not being able to prevent the transmission of sexually transmitted diseases, and achieve the effects of reducing the chance of penetration, improving strength and toughness, and improving barrier performance

Active Publication Date: 2016-05-04
沈阳天地乳胶有限公司
View PDF5 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The "New England Journal of Medicine" reported that the failure rate of condoms to prevent AIDS was 16.7%, and the "British Social Science Medical Journal" reported that the failure rate of condoms to prevent AIDS was as high as 31%; the National Institutes of Health (NIH), Food and Drug Administration FDA, Centers for Disease Control and Prevention (CDC) and the United States Agency for International Development (US-AID) jointly formed a scientific task force to examine hepatitis B, AIDS, gonorrhea, chlamydia, syphilis, chancroid, lymphogranuloma venereum, Several sexually transmitted diseases, including genital herpes and genital warts, found that currently widely used condoms do not prevent the transmission of any of the sexually transmitted diseases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene modified natural emulsion preparation method and high barrier condom

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The high -resistance condom of the present invention uses graphene modified natural latex to be prepared on the condom mold, and the preparation method of graphene modified natural latex includes the following steps:

[0033] 1) Mix the graphene powder with the decentralized auxiliary agent in proportion.The concentration of graphene in nano-decentralization A is 0.5-50mg / ml, the size of the graphene after grinding is 200-800nm, and the thickness is 1-3nm., Pleurotic plus O, Sodium Polar Phosphate, Diffengers NF, Sixteenanel Penzenzine Sulfate, Siliconhane Benzene Sulfate, Stabilizer LW, Sodium Global Sulfate, and TexotylhumidaAt least one mixture of sulfonate.

[0034] 2) After adding a stabilizer and surfactant to the natural latex solution under the continuous stirring state, continue to stir for 5-10 minutes; then slowly add the granular nano-dispersed solution A, and continue to stir for 5-10 minutes; add promoter, then add promoter, then add promoter,Anti -agent, vulc...

Embodiment 1

[0048] The high -resistance condoms of this embodiment are prepared by graphene modified natural latex, and the preparation method of graphene modified natural latex includes the following steps:

[0049] 1) Mix the dispersing additives with the graphene powder at 10: 1 according to the quality ratio, and the graphene nano -decentralized liquid A is obtained after grinding;The graphene size after grinding is 500-700nm and the thickness is 1-3nm. The grinding equipment is grinded for 6 hours during grinding;liquid.

[0050] 2) After adding a stabilizer and surfactant to the natural latex solution in the continuous stirring state, continue to stir for 5 minutes; then slowly add the graphene nano -dispersing solution A, and continue to stir for 7 minutes; then add promotional agent, anti -agent, vulcanized vulcanizationEstablishing agent and vulcanization agent, obtained latex mixture B.

[0051] Further, with 60%natural latex as 100PHR;

[0052] The amount of stabilizer is 0.2PHR, a...

Embodiment 2

[0063] The high -resistance condoms of this embodiment use the graphene modified natural latex to be prepared on the condom mold, and the preparation method of graphene modified natural latex includes the following steps:

[0064] 1) Mix decentralized additives with graphene powder at 5: 1 according to the quality ratio.The latter graphene size is 200-500nm, and the thickness is 1-3nm. When grinding, the grinding equipment is grinded for 8 hours; the dispersant is a dispersant NF.

[0065] 2) After adding a stabilizer and surfactant to the natural latex solution in the continuous stirring state, continue to stir for 10 minutes; then slowly add the graphene nano -dispersing solution A, and continue to stir for 5 minutes; then add promoter, agent, sulfide, vulcanizationEstablishing agent and vulcanization agent, obtained latex mixture B.

[0066] Further, with 60%natural latex as 100PHR;

[0067] The amount of stabilizer is 1PHR, and the stabilizer is ammonia or KOH;

[0068] The do...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphene modified natural emulsion preparation method and a high barrier condom. The graphene modified natural emulsion preparation method and the high barrier condom have the beneficial effects that firstly graphene and a dispersing agent mixed liquor are mixed, ground and stirred and then the product is mixed in a natural emulsion aqueous solution, so that graphene can be uniformly dispersed in emulsion and the strength of a natural emulsion composite material is improved; meanwhile, the number of micropores is smaller due to the graphene / emulsion composite action, thus greatly reducing the virus penetration probability; the thickness of the graphene condom can be 5-80mu m, so that the use requirements of the condom can be met; dense high barrier packing layers are formed by the composite crosslinked nano-packing technology, so that the natural gaps among molecules are reduced; therefore not only can HIVs be blocked but also hepatitis B viruses, hepatitis C viruses, human papilloma viruses, and the like, and most harmful bacteria, which are smaller than the HIVs, can not pass through the micropores.

Description

Technical field [0001] The present invention is a composition technology field of natural rubber. It is specifically for a graphene modified natural latex preparation method and high -resistance condom. Background technique [0002] The role of condoms is mainly used to prevent pregnancy and prevent sex diseases, also called condoms.However, some research projects and a large amount of international data from the National Family Planning Commission of China show that the materials used in the current market are mainly natural latex, and their natural cracks are about 3000Nm, which is enough to prevent human sperm head with a diameter of about 5000nm.However, the diameter of AIDS virus is only 120nm, the diameter of human papilloma virus is between 45-55nm, and the diameter of large spherical particles in hepatitis B virus is 42nm.The volume of various viruses is far less than the natural cracks of natural latex. Even if the condom is used correctly, it is still possible to infect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08K13/06C08K9/04C08K9/02C08K3/04C08K3/06C08K5/13C08K3/22A61F6/04
CPCA61F6/04C08K3/04C08K3/06C08K3/22C08K5/13C08K9/02C08K9/04C08K13/06C08K2003/2296C08K2201/011C08L7/00
Inventor 饶先花潘长富李朝龙高翾王强史浩飞
Owner 沈阳天地乳胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com