Preparation, application and desizing method of composite size for sizing high-count pure cotton yarn
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of composite pulp and pure cotton, which is applied in the processing of textile material equipment configuration, dry cleaning fiber products, textile material processing, etc. The effect of wear resistance
Active Publication Date: 2018-05-04
SUQIAN YUANYANG BIOTECH
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, it is mostly used in breeding, and it is rarely used in other aspects. Pile up or discard a large amount of beer lees outdoors, which will pollute the environment.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0033] A preparation method for a composite size used for sizing high-count pure cotton yarns, comprising the following steps:
[0034] (1) Add the dried beer grains into water, the bath ratio is 1:5, wash 4 times, filter with a 50-mesh sieve, and filter out the remaining soluble sugar in the beer grains, which is beneficial to the improvement of the serous film performance;
[0035] (2) place the brewer's grains after desugaring outside, and carry out natural drying;
[0036] (3) Adopting a universal pulverizer to pulverize the dried distiller's grains into 50 mesh powders;
[0037] (4) Sodium hydroxide solution is used to extract the protein soluble matter in the pulverized beer dried distiller's grains powder, the ratio of sugar-removed beer dried distiller's grains to water is 1:6, the alkali concentration is 1%, and the heating temperature is 50°C. The heating time is 30min;
[0038] (5) Adopt high-speed centrifuge to carry out solid-liquid separation to the prepared br...
Embodiment 2
[0051] A method for preparing composite size for high-count pure cotton yarn sizing, comprising the following steps:
[0052] (1) Add the dried beer grains into water with a liquor ratio of 1:30, wash once, filter with a 100-mesh sieve, and filter out the remaining soluble sugar in the beer grains, which is beneficial to the improvement of the serous film performance;
[0053] (2) put the brewer's grains after desugaring into a blast oven for drying, and the temperature can be 50°C;
[0054] (3) Adopting a universal pulverizer to pulverize the dried distiller's grains into 50 mesh powders;
[0055] (4) Alkaline solution is used to extract the protein soluble substances in the pulverized beer dried distiller's grains powder, the ratio of sugar-free beer dried distiller's grains to water is 1:10, the alkali concentration is 1.5%, the heating temperature is 90°C, and the heating time is 60min;
[0056] (5) Adopt high-speed centrifuge to carry out solid-liquid separation to the pr...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to preparation and application of a composite sizing agent for high-count cotton yarn sizing and a desizing method. The preparation and application comprise the following steps: (1) using brewer's grains as a raw material for preparation of the composite sizing agent, putting the above materials into a sodium hydroxide solution, heating at constant temperature of 50-90 DEG C for 30-90 min, centrifuging or carrying out suction filtration to remove undissolved residue, and using a supernatant to prepare the composite sizing agent for high-count cotton yarn sizing; and (2) carrying out sizing process of cotton yarn by the use of a single-yarn sizing machine, adopting a double soak and press mode with temperature of sizing box being 40-70 DEG C, dying room temperature being 50-80 DEG C and sizing speed being 10-50 m / min, controlling permeation and coating ratio of the size in the yarn according to pressure adjustment, and carrying out coordination control of sizing percentage by sizing agent concentration and pressure. The prepared composite sizing agent is low-cost, has good sizing performance, is suitable for cotton yarn sizing, is easy to desize, contains no hardly degradable substance or substances harmful to the environment, and is clean and environmentally friendly.
Description
technical field [0001] The invention relates to the preparation, application and desizing method of a novel composite size suitable for sizing high-count pure cotton yarns. Background technique [0002] The purpose of sizing is to saturate and cover the yarn with sizing material to increase its strength, improve wear resistance, and reduce hairiness, thereby reducing or preventing warp yarn breakage in the weaving process and improving weaving efficiency. It is a must in the textile industry. An indispensable process. At present, the three main varieties in the size industry are: polyvinyl alcohol, modified starch and acrylic size. Starch size has good film-forming properties, strong affinity with natural fibers, and is easy to desizing; but starch size has insufficient sizing strength, is easy to break, and has poor wear resistance. Polyvinyl alcohol sizing film has high strength and good flexibility, and is often used for sizing pure cotton. However, it is difficult to d...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More