A kind of negative electrode material of lithium ion battery, its preparation method and lithium ion battery

A lithium-ion battery and anode material technology, applied in battery electrodes, secondary batteries, circuits, etc., can solve the problems of unfavorable large-scale production, long preparation time, poor controllability, etc., and achieve high electrochemical cycle performance and rate performance , the effect of high specific capacity

Active Publication Date: 2018-09-21
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method alleviates the volume effect of silicon to a certain extent, but the conditions and time for adding each component are relatively strictly limited, the reaction temperature is high, the preparation time is long, the preparation steps are cumbersome, and the controllability is poor, which is not conducive to mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of negative electrode material of lithium ion battery, its preparation method and lithium ion battery
  • A kind of negative electrode material of lithium ion battery, its preparation method and lithium ion battery
  • A kind of negative electrode material of lithium ion battery, its preparation method and lithium ion battery

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The present invention provides a kind of preparation method of above-mentioned negative electrode material of lithium ion battery, comprises the following steps:

[0035] Mixing n-hexane, emulsifier, n-pentanol, deionized water, organic ligands and nano silicon powder to obtain the first microemulsion;

[0036] mixing n-hexane, emulsifier, n-pentanol, deionized water and metal inorganic salts to obtain a second microemulsion;

[0037] The first microemulsion and the second microemulsion are mixed and reacted, and the reaction product is subjected to carbonization treatment to obtain a lithium ion battery negative electrode material.

[0038] The method for preparing the first microemulsion is preferably:

[0039] Dispersing the organic ligand and nano silicon powder in deionized water to obtain the first mixed solution;

[0040] Mix n-hexane, emulsifier and n-pentanol evenly to obtain a second mixed solution;

[0041] Uniformly mixing the first mixed liquid and the sec...

Embodiment 1

[0063] Disperse the nano-silica powder in ethanol, heat it in a water bath to 60°C, add 3-aminopropyltriethoxysilane (APTES) under the condition of stirring, stir at constant temperature for 3 hours, cool to room temperature, and then add under the condition of stirring Succinic anhydride, continue to stir for 4 hours to obtain carboxylated modified nano-silicon powder; the mass ratio of the nano-silicon powder, ethanol, APTES and succinic anhydride is 200:118:1:400.

[0064] Uniformly mixing n-hexane, Span 80, n-pentanol, deionized water, 2-methylimidazole and carboxylated-modified nano silicon powder to obtain the first microemulsion. Among them, the mass ratio of 2-methylimidazole, carboxylated nano silicon powder, Span 80 and deionized water is 25:25:1400:4, and the volume ratio of n-hexane, n-pentanol and deionized water is 50 :25:1.

[0065] Mix n-hexane, Span 80, n-amyl alcohol, deionized water and zinc nitrate hexahydrate uniformly to obtain the second microemulsion. ...

Embodiment 2

[0072]Disperse the nano-silica powder in ethanol, heat it in a water bath to 60°C, add 3-aminopropyltriethoxysilane (APTES) under the condition of stirring, stir at constant temperature for 3 hours, cool to room temperature, and then add under the condition of stirring Succinic anhydride, continue to stir for 8 hours to obtain carboxylated nano-silicon powder; the mass ratio of the nano-silicon powder, ethanol, APTES and succinic anhydride is 300:180:1.5:600.

[0073] Uniformly mixing n-hexane, Span 80, n-pentanol, deionized water, trimesic acid and carboxylated nano-silica powder to obtain the first microemulsion. Among them, the mass ratio of trimesic acid, carboxylated nano silicon powder, Span 80 and deionized water is 2:1:1750:5, and the volume ratio of n-hexane, n-pentanol and deionized water is 60: 30:1.

[0074] Mix n-hexane, Span 80, n-amyl alcohol, deionized water and copper nitrate trihydrate uniformly to obtain the second microemulsion. Among them, the mass ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a lithium ion battery negative material. The lithium ion battery negative material comprises nano silicon particles and carbon material particles, wherein the nano silicon particles are uniformly dispersed among the carbon material particles to form microspheres; and the carbon material particles are carbonized metallic organic skeleton materials. The microsphere structural silicon-carbon composite material is obtained by adopting a micro-emulsion method. Compared with the prior art of embedding nano silicon into each single carbon material particle to form a core-shell structure, a lithium ion battery manufactured with the negative material has higher electrochemical cycling performance and multiplying power performance; and meanwhile, the preparation method is simple and easy, and is low in reaction temperature, short in preparation time, good in controllability and favorable for mass production. An experiment shows that the primary discharge specific capacity of the prepared lithium ion battery at the multiplying power of 0.1C is 1800 to 2069 mAh / g, and after the lithium ion battery is circulated for 120 times, the discharge specific capacity is 1000 to 1280 mAh / g.

Description

technical field [0001] The invention relates to the technical field of lithium ion batteries, in particular to a lithium ion battery negative electrode material, a preparation method thereof and a lithium ion battery. Background technique [0002] Lithium-ion batteries have the advantages of high operating voltage, high specific energy, wide operating temperature range, stable discharge, small size, light weight, no memory effect, and environmental friendliness. Therefore, they are widely used in portable electronic devices, electric vehicles, space technology, and defense industries. and other fields have shown broad application prospects. [0003] With the increasing demand for high-capacity and long-life batteries in mobile electronic devices, people have put forward higher requirements for the performance of lithium-ion batteries. As an important factor to improve the energy and cycle life of lithium-ion batteries, negative electrode materials are in the world. has been...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/38H01M4/583H01M4/62H01M10/0525
CPCH01M4/362H01M4/386H01M4/583H01M4/625H01M10/0525Y02E60/10
Inventor 张可利杨正东夏永高刘兆平
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com