Single-component quick-drying and quick-hardening type polymer cement waterproof coating and use method thereof
A waterproof coating and fast-hardening technology, applied in the field of waterproof materials for construction, can solve the problems of low early strength, inconvenient storage and transportation at low temperature, long construction period, etc., and achieve the effect of high early strength, shortened construction period and good construction performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1
[0028] The weight ratio of the amount of water added to the powder in this embodiment is 23%, and the percentage of each substance in the powder component is:
[0029] 42.5 grade sulphoaluminate cement 40%
[0030] 40-200 mesh quartz sand 35%
[0031] 320 mesh heavy calcium carbonate 5.5%
[0032] Polyacrylate copolymer latex powder 10%
[0033] Yuanming powder 6%
[0034] Water glass 2%
[0035] Water repellent 0.2%
[0036] Lithium chloride 0.15%
[0037] Calcium oxide 0.5%
[0038] Citric acid 0.2%
[0039] Hydroxyethyl cellulose ether 0.1%
[0040] Polycarboxylic acid water reducing agent 0.2%.
[0041] Powdery defoamer 0.15%
[0042] The sulphoaluminate cement is a 42.5 grade fast hardening sulphoaluminate cement produced by Shijiazhuang Xunta Special Cement Co., Ltd.; the glass transition temperature of the polyacrylate copolymer latex powder is 10°C, and the bulk density is 500kg / m 3 ; Water repellent is Evonik’s silicone water repellent Sitren P750; cellulose ether is B...
Example Embodiment
[0044] Example 2
[0045] The weight ratio of the amount of water added to the powder in this embodiment is 26%, and the percentage of each substance in the powder component is:
[0046] 42.5 grade sulphoaluminate cement 50%
[0047] 40-200 mesh quartz sand 26.6%
[0048] Polyacrylate copolymer latex powder 13%
[0049] Yuanming powder 7%
[0050] Water glass 2%
[0051] Water repellent 0.1%
[0052] Lithium carbonate 0.25%
[0053] Calcium oxide 0.4%
[0054] Citric acid 0.15%
[0055] Hydroxyethyl cellulose ether 0.1%
[0056] Sulfonated melamine superplasticizer 0.3%
[0057] Powdery defoamer 0.1%
[0058] The sulphoaluminate cement is 42.5 grade fast hardening sulphoaluminate cement produced by Shijiazhuang Xunta Special Cement Co., Ltd.; the glass transition temperature of the polyacrylate copolymer latex powder is -8°C, and the bulk density is 500kg / m 3 ; The water-repellent is Evonik’s silicone water-repellent SitrenP750; the cellulose ether is Bayer’s WalocelMKX15000; the powdered water-...
Example Embodiment
[0060] Example 3
[0061] The weight ratio of the amount of water added to the powder in this embodiment is 22%, and the percentage of each substance in the powder component is:
[0062] 42.5 grade sulphoaluminate cement 30%
[0063] 40-200 mesh quartz sand 45%
[0064] 320 mesh heavy calcium carbonate 10%
[0065] Polyacrylate copolymer latex powder 5%
[0066] Yuanming powder 6%
[0067] Water glass 1%
[0068] Water repellent 1%
[0069] Lithium carbonate 0.3%
[0070] Calcium oxide 1%
[0071] Sodium citrate 0.25%
[0072] Methyl cellulose ether 0.15%
[0073] Sulfonated melamine superplasticizer 0.2%
[0074] Powdery defoamer 0.1%
[0075] The sulphoaluminate cement is 42.5 grade fast hardening sulphoaluminate cement produced by Shijiazhuang Xunta Special Cement Co., Ltd.; the glass transition temperature of the polyacrylate copolymer latex powder is -8°C, and the bulk density is 500kg / m 3 ; The water-repellent is Evonik’s silicone water-repellent SitrenP750; the cellulose ether is Bayer’s W...
PUM
Property | Measurement | Unit |
---|---|---|
Glass transition temperature | aaaaa | aaaaa |
Bulk density | aaaaa | aaaaa |
Flexural strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap