A kind of amorphous block copolymer modified polyethylene glue
A block copolymer and polyethylene technology, applied in the direction of graft polymer adhesives, adhesives, adhesive types, etc., can solve problems such as poor compatibility, achieve good product performance, increase Vicat temperature, and process The effect of simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] At room temperature, 100 g of maleic anhydride and 4 g of 2,5-dimethyl-2,5-di-tert-butylperoxyhexane were dissolved in 100 g of acetone. Mix 3kg of high-density polyethylene and 2kg of linear low-density polyethylene into the feeding barrel evenly. Set the temperature of the heating cylinder of the extruder to 75°C, 160°C, 180°C, 180°C, 185°C, 85°C, 185°C, 185°C, 190°C along the extrusion direction; the screw speed is 100 r / min. The heating cylinder reaches the predetermined temperature, and 5kg of polyethylene compound is added to the extruder from the main feeding port of the first section of the extruder, and the feeding speed is 0.15kg / min; at the same time, the acetone solution containing maleic anhydride and the initiator is passed through The metering pump injects from the liquid feeding port of the third section of the extruder at a speed of 0.002kg / min, and extrudes to obtain the polyethylene graft bonding resin. After mixing 4kg of polyethylene graft adhesive...
Embodiment 2
[0019] At room temperature, 100 g of maleic anhydride and 8 g of 2,5-dimethyl-2,5-di-tert-butylperoxyhexane were dissolved in 100 g of acetone. Mix 3kg of high-density polyethylene and 2kg of ethylene-octene copolymer evenly into the feeding barrel. Set the temperature of the heating cylinder of the extruder to 75°C, 160°C, 180°C, 180°C, 185°C, 185°C, 185°C, 185°C, 190°C along the extrusion direction; the screw speed is 100 r / min. The heating cylinder reaches the predetermined temperature, and 5kg of polyethylene compound is added to the extruder from the main feeding port of the first section of the extruder, and the feeding speed is 0.15kg / min; at the same time, the acetone solution containing maleic anhydride and the initiator is passed through The metering pump injects from the liquid feeding port of the third section of the extruder at a speed of 0.006kg / min, and extrudes to obtain the polyethylene graft bonding resin. After mixing 4kg of polyethylene graft adhesive resi...
PUM
Property | Measurement | Unit |
---|---|---|
Vicat softening point | aaaaa | aaaaa |
Vicat softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap