Preparation method of ionic liquid and secondary battery

An ionic liquid and secondary battery technology, applied in the field of one-step synthesis of quaternary ammonium or quaternary phosphonium compounds, can solve the problems of separation of products and catalysts, carcinogenicity, high toxicity, etc., and achieves a wide selection of raw materials, mild reaction conditions, and simple operation. Effect

Active Publication Date: 2020-11-06
MICROVAST POWER SYST CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Tertiary amines react easily with dimethyl sulfate, and the yield is high, but the disadvantage of using dimethyl sulfate is that it is highly toxic and carcinogenic
The biggest disadvantage of the above-mentioned process route is that it can only prepare certain kinds of quaternary ammonium salts. For example, according to the method of quaternization reaction of halogenated alkanes, it can only prepare anion that is Cl - 、Br - , I - The quaternary ammonium salt; according to the method of the quaternization reaction of dimethyl sulfate, only the anion that can be prepared is CH 3 SO 4 - quaternary ammonium salt
In the technical scheme of patent CN200510061094.4, catalysts selected from metal compounds, non-metal compounds, their mixtures or ionic liquids need to be used, so after the reaction is completed, there must be a problem of separating the product from the catalyst, and it is difficult to ensure the high purity of the product ; while the technical solution disclosed in patent CN200710008626.7 does not use a catalyst, does not involve subsequent cumbersome separation process, the operation process is relatively simple, the product purity is greatly improved, and it is more suitable for some application fields that require higher product purity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ionic liquid and secondary battery
  • Preparation method of ionic liquid and secondary battery
  • Preparation method of ionic liquid and secondary battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0116] Triethylamine (606 g) was placed in a pressure vessel together with 1000 mL of dimethyl carbonate and protected with nitrogen. Feed concentrated sulfuric acid (300g, 98%) under cooling measures. After adding sulfuric acid, raise the temperature to 200°C. During the reaction, the pressure will rise. If the reaction pressure exceeds 3.0Mpa, vent the gas through the valve to keep the pressure in the kettle from rising. . Reaction time 0.2 hours. After the reaction was completed and lowered to room temperature, the low boilers were removed under reduced pressure and the product was washed to obtain N-methyl-N-triethylammonium sulfate (950 g).

Embodiment 2

[0118] N-n-Propylpyrrolidine (500 g) was placed in a pressure vessel along with 1000 mL of dimethyl carbonate. Under nitrogen protection, bis(trifluoromethylsulfonyl)imide (1234 g) was added slowly, keeping the temperature not exceeding 60°C during the process. After the addition, react at 150°C and about 1.6MPa for 20 hours. During the reaction, release part of the gas through the release valve to avoid excessive pressure. After completion of the reaction, low boilers were removed under reduced pressure and the product was washed to obtain N-methyl-N-propylpyrrolidinium bis(trifluoromethylsulfonyl)imide salt (1675 g).

Embodiment 3

[0120] Put N-n-propylpyrrolidine (500g) together with 500g dimethyl carbonate and 500mL methanol into a pressure vessel, heat up to 120°C, then add bis(trifluoromethylsulfonyl)imide (1236g ), and the temperature in the reaction vessel is maintained at 120 to 130°C during this process. The continuous feeding time is 12 hours. After the bis(trifluoromethylsulfonyl)imide material is conveyed according to the set amount, the temperature is raised to 150° C. and the reaction is continued for 2 hours. During the reaction process, if the reaction pressure exceeds 2.6Mpa, the pressure in the kettle is kept from rising through the valve release. After the reaction was completed and lowered to room temperature, the low boilers were removed under reduced pressure and the product was washed to obtain N-methyl-N-propylpyrrolidinium bis(trifluoromethylsulfonyl)imide salt (1704 g).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
electrical conductivityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of an ionic liquid, in particular to a method for synthesizing a quaternary ammonium or quaternary phosphonium compound in one step. In this method, a nitrogen compound or a phosphorus-containing compound, a proton compound, and a carbonate are added to a reactor to react in one step to synthesize the corresponding quaternary ammonium salt or quaternary phosphonium salt ionic liquid, that is, a "one-pot" reaction, which involves three reactants. One step reaction. The present invention also provides a lithium ion secondary battery containing the ionic liquid prepared by the above preparation method. The ionic liquid preparation method of the present invention can broaden the selection range of raw materials for ionic liquid preparation, and further broaden the types of ionic liquids to be synthesized. In the preparation method, the raw materials are non-toxic and harmless, the reaction conditions are mild, the requirements for production equipment are not high, and the production cost is low. , suitable for green industry and large-scale industrial production needs.

Description

technical field [0001] The invention relates to a preparation method of an ionic liquid, in particular to a method for synthesizing a quaternary ammonium or quaternary phosphonium compound in one step. Background technique [0002] Ionic liquid (ionic liquid) is a liquid substance composed entirely of ions, which is liquid at room temperature or low temperature (-97 ° C ~ 100 ° C), so it is also called room / low temperature molten salt (room / low temperature molten salt), or called Liquid organic salt. There are many kinds of ionic liquids. According to different organic cations, ionic liquids can be divided into quaternary ammonium salts, quaternary phosphonium salts, nitrogen-containing heterocyclic onium salts, etc., nitrogen-containing heterocyclic ionic liquids include imidazolium salts, Pyridinium salts, piperidine salts, pyrrolidinium salts, etc. There are a wide variety of anions that make up ionic liquids, and inorganic anions include F - , Cl - 、Br - , I - , NO...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/0525H01M10/0566H01M10/0567H01M10/0569
CPCH01M10/0525H01M10/0566H01M10/0567H01M10/0569H01M2300/0025H01M2300/0028Y02E60/10
Inventor 郑卓群申大卫邱建聂云华赵晓珍李丹祎
Owner MICROVAST POWER SYST CO LTD