Molten steel feeding system used for preparing amorphous strips

A supply system and a technology for amorphous strips, applied in the field of amorphous strip manufacturing, can solve the problems of inability to achieve continuous production of amorphous strips, single temperature, etc., and achieve the effect of realizing flow control and temperature control.

Active Publication Date: 2016-08-10
ADVANCED TECHNOLOGY & MATERIALS CO LTD
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a liquid steel supply system for preparing amorphous strips, to at least solve the technical problems of the single effect of purifying molten steel or quickly adjusting the temperature of molten steel in the prior art, and at the same time solve the problems of the existing technology Existing technical problems that cannot realize the continuous production of amorphous strips

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Molten steel feeding system used for preparing amorphous strips
  • Molten steel feeding system used for preparing amorphous strips
  • Molten steel feeding system used for preparing amorphous strips

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The present invention will be described in further detail below in conjunction with the accompanying drawings and specific embodiments.

[0033] Such as figure 1 As shown, the molten steel supply system for preparing amorphous strips in the preferred embodiment of the present invention mainly includes a resistance heating tundish 1 for receiving molten steel and purifying the molten steel; and an induction heating nozzle package 2 placed in The bottom of the resistance heating tundish 1 is used to receive the molten steel injected into the resistance heating tundish 1 and to adjust the temperature of the molten steel; a nozzle 21 is provided below the induction heating nozzle package 2, and the nozzle 21 is used to pour the molten steel into A continuous amorphous ribbon is formed on chill rolls.

[0034] In a word, the molten steel supply system for preparing amorphous strips provided by the present invention is composed of a resistance heating tundish 1 with a calmin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a molten steel feeding system used for preparing amorphous strips. The molten steel feeding system comprises a resistance heating tundish and an induction heating nozzle bag, wherein the resistance heating tundish is used for receiving molten steel and purifying the molten steel; the induction heating nozzle bag is arranged below the resistance heating tundish, used for receiving the molten steel injected by the resistance heating tundish and used for conducting temperature regulating on the molten steel; and a nozzle is arranged below the induction heating nozzle bag and used for pouring of the molten steel. By means of the molten steel feeding system used for preparing the amorphous strips, inclusions in the molten steel can float up so as to achieve the aim of purifying the molten steel; and meanwhile, the temperature of the molten steel can be rapidly adjusted, and the temperature needed for preparing the amorphous strips is achieved.

Description

technical field [0001] The invention belongs to the technical field of manufacturing amorphous strips, in particular, the invention relates to a molten steel supply system for preparing amorphous strips. Background technique [0002] At this stage, the preparation of amorphous alloy strips mostly adopts the method of single-roll rapid quenching. The system of single roll quick quenching method is mainly composed of the following parts: smelting furnace, tundish, stopper rod, nozzle package, cooling roll, thickness measuring device and grabbing device. After the master alloy is smelted in the smelting furnace, a molten alloy is formed. The molten alloy is poured into the tundish through the smelting furnace. After the process of slag removal and temperature adjustment in the tundish, it is injected into the nozzle package through the steel pouring port under the tundish, and poured into the cooling roller through the nozzle below the nozzle package. superior. After the mol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/10B22D11/117B22D11/06
CPCB22D11/06B22D11/10B22D11/117
Inventor 李德仁卢志超张宏浩赵宏伟郑太福高昇李立军
Owner ADVANCED TECHNOLOGY & MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap