Laminated glass functional glue film and preparation technology thereof

A preparation process, a technology for laminated glass, used in adhesives, film/sheet adhesives, adhesive additives, etc.

Inactive Publication Date: 2016-10-05
浙江利昌科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These laminated films have strong adhesion, high adhesion, high flexibility, high transparency, and no foaming. However, although the laminated glass glue made of traditional laminated films has strong safety performance, it has no other special features. function of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0017] 1. Recipe

[0018] EVA resin 96.0%;

[0019] Benzophenone UV aging resistance additive 0.5%;

[0020] Cross-linking agent 1.5%;

[0021] Coupling agent 1.0%;

[0022] Pigment (Red Iron Oxide): 1.0%.

[0023] The preparation steps are as follows:

[0024] (1) First mix 10% EVA resin, coloring pigments, and anti-ultraviolet aging additives. The mixing temperature is 60 ° C ~ 100 ° C. After mixing, it is granulated by a granulator;

[0025] (2) Mix the particles obtained by mixing and granulation with the remaining EVA resin, crosslinking agent, and coupling agent in a mixer to make a mixture;

[0026] (3) Melt the mixture through the extruder, extrude it into a film form from the die head, press the film through the pressure roller, cool and shape it, and wind it up to obtain the finished EVA functional film.

[0027] 2. Product performance

[0028] a) Red transparent functional film;

[0029] b) Light transmittance: 89%;

[0030] c) Peel strength: 92N / cm;

[00...

example 2

[0033] 1. Recipe

[0034] EVA resin 92%;

[0035] Anti-ultraviolet aging additive 0.5%;

[0036] Cross-linking agent 1.5%;

[0037] Coupling agent 1.0%;

[0038] Fluorescent material (long-lasting luminous powder yellow-green): 5.0%.

[0039] The preparation steps are as follows:

[0040] (1) First mix 13% EVA resin, fluorescent materials, and anti-ultraviolet aging additives. The mixing temperature is 60°C to 100°C. After mixing, granulate through a granulator;

[0041] (2) Mix the particles obtained by mixing and granulation with the remaining EVA resin, crosslinking agent, and coupling agent in a mixer to make a mixture;

[0042] (3) Melt the mixture through the extruder, extrude it into a film form from the die head, press the film through the pressure roller, cool and shape it, and wind it up to obtain the finished EVA functional film.

[0043] 2. Product performance

[0044] a) Fluorescent transparent functional film;

[0045] b) Light transmittance: 88%;

[004...

example 3

[0049] 1. Recipe

[0050] EVA resin 94%;

[0051] Anti-ultraviolet aging additive 0.3%;

[0052] Cross-linking agent 0.8%;

[0053] 0.6% coupling agent;

[0054] Fluorescent material (long-lasting luminous powder yellow-green): 2.3%;

[0055] Green pearlite powder: 2%;

[0056] The preparation steps are as follows:

[0057] (1) First mix 12% EVA resin, fluorescent material, green pearlite powder, and anti-ultraviolet aging additives. The mixing temperature is 60 ° C ~ 100 ° C. After mixing, it is granulated by a granulator;

[0058] (2) Mix the particles obtained by mixing and granulation with the remaining EVA resin, crosslinking agent, and coupling agent in a mixer to make a mixture;

[0059] (3) Melt the mixture through the extruder, extrude it into a film form from the die head, press the film through the pressure roller, cool and shape it, and wind it up to obtain the finished EVA functional film.

[0060] 2. Product performance

[0061] a) Green pearlescent fluor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Peel strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation process of a functional adhesive film for laminated glass and its product. The composition and weight ratio are as follows: (1) EVA resin is 92% to 97%, and the VA content in the EVA resin is 24% to 28%. , melt flow rate 20g / 10min~45g / 10min; (2) liquid peroxide crosslinking agent, the content is 0.3%~1.5%; (3) benzophenone UV aging resistance additives, UV aging resistance additives (4) Liquid silane coupling agent, with a content of 0.1% to 1.0%; (5) Rare earth-doped sulfate or aluminate Afterglow powder fluorescent powder, the powder particle size is between 100 nanometers and 20 microns, and the content is 0.5% to 5%; (6) Inorganic materials or pearlite coloring pigments with a temperature resistance above 200 ° C, the powder particle size is between Between 500 nanometers and 20 microns, the content is between 0.5% and 5.0%. Through kneading, granulation, melting and extruding into a film form, the finished EVA film is obtained through pressure roller pressing, cooling and shaping, and winding.

Description

technical field [0001] The invention relates to a preparation process of a functional adhesive film for laminated glass. Background technique [0002] The traditional adhesive film for laminated glass, such as PVG, PVB, EVA, etc., is sandwiched between two pieces of glass, and the glass is bonded together by heating and pressure to become laminated glass. These laminated films have strong adhesion, high adhesion, high flexibility, high transparency, and no foaming. However, although the laminated glass glue made of traditional laminated films has strong safety performance, it has no other special features. function. Contents of the invention [0003] The object of the present invention is to provide a kind of laminated film preparation process that makes laminated glass have more functions in order to overcome the deficiencies in the prior art [0004] In order to achieve the above object, the present invention provides the following technical solution: a preparation pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J7/00C09J123/08C09J11/04C09J11/06
Inventor 詹显光李西军金怀东周雪梅
Owner 浙江利昌科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap