Rapid curing drying method for energy source battery positive electrode plate

A battery cathode, fast curing technology, applied in the direction of lead-acid battery electrodes, etc., can solve the problems of large steam consumption and energy consumption in the curing room, poor energy saving and emission reduction effect, low battery cycle life, etc., to shorten the curing time and save energy. The effect of improving the consumption and cycle life

Active Publication Date: 2016-10-26
ANHUI YONGHENG STORAGE BATTERY
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Obviously, the traditional plate curing and drying time is long, the amount of steam and energy used in the curing room is large, the energy consumption is high, the product quality is poor, the cycle life of the battery is low, the production efficiency is low, and the effect of energy saving and emission reduction is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1: A method for rapid curing and drying of the positive plate of an energy battery. The paste-coated wet plate is placed in a special curing chamber. The environment for rapid curing and drying of the polar plate in the curing room is: the first stage is at a temperature of 48°C, the humidity is 100%, and the curing time is 7 hours; the second stage is at a temperature of 80°C, the humidity is 100%, and the curing time is 4 hours; the third stage is The temperature is 50-51°C, the humidity is 85%, and the curing time is 6 hours; the fourth stage is that the temperature is 50-51°C, the wind speed is 90%, and the humidity is removed for 4 hours; the fifth stage is that the temperature is 60°C, and the drying time is 3 hours. ; The sixth section is at a temperature of 70°C and dried for 7 hours. The total curing and drying time is 30 hours.

Embodiment 2

[0039] Embodiment 2: A method for rapid curing and drying of the positive plate of an energy battery. The paste-coated wet plate is placed in a special curing chamber. The environment for rapid curing and drying of the polar plate in the curing room is: the first stage is at a temperature of 46-49°C, the humidity is 100%, and the curing time is 7.2-8 hours; the second stage is at a temperature of 80°C, the humidity is 100%, and the curing time is 4 hours ;The third section is temperature 47~53℃, humidity 85%, curing time 6 hours; the fourth section is temperature 47~53℃, wind speed 90% condition, dehumidification for 4 hours; the fifth section is temperature 60℃ , drying for 3 hours; the sixth section is a temperature of 68 ~ 70 ℃, drying for 7 hours.

[0040] In a word, the present invention can greatly reduce the time for rapid curing and drying of the positive plate, has the advantages of simple and practical process, saves production time, saves cost, has good practical ef...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to a rapid curing drying method for an energy source battery positive electrode plate. According to the method, a multi-section low-temperature and high-temperature mixing curing method is used for a storage batter positive electrode plate, wherein the low temperature-high temperature is used for the electrode plate curing drying environment at the early stage of the curing drying, the high temperature-high temperature is used for the electrode plate curing drying environment at the middle stage of the curing drying, and the uniform dewatering is used for the electrode plate curing drying environment at the late stage of the curing drying. According to the present invention, with the method, the rapid curing drying time of the positive electrode plate can be substantially reduced, and the advantages of simple, practical and convenient process, production time saving, cost saving, good practical effect, energy saving, consumption reducing, production efficiency improving, high battery cycle life, and good product quality.

Description

[0001] technical field [0002] The invention belongs to a method for fast curing and drying of an energy battery positive plate. Background technique [0003] Battery technology belongs to the new energy industry, and it is developing very rapidly in our country. The core that affects battery life is the battery plate, and the quality of the plate depends on the process control of the plate during the curing and drying process. The curing and drying of the plate is to put the paste-coated wet plate in a special curing room, and to cure and dry it under certain temperature and humidity conditions, so that the residual free lead in the lead paste is further oxidized into lead oxide and lead. Form basic lead sulfate; at the same time, the surface of the grid is corroded, and lead oxide is formed on the surface of the grid to combine with the lead oxide in the lead paste, thereby improving the bonding force and strength of the grid and the active material. [0004] The tra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/20H01M4/21
CPCH01M4/20H01M4/21Y02E60/10
Inventor 母建平胡满娣杭琪陈上识
Owner ANHUI YONGHENG STORAGE BATTERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap