Coating capable of releasing negative oxygen ions, and preparation method and application thereof

A technology of negative oxygen ions and coatings, applied in the field of coatings capable of releasing negative oxygen ions and their preparation, can solve the problems of limited release distance, slow release speed of negative oxygen ions, low speed and strength, etc., and is beneficial to human health. , Improve the living environment, the effect of fresh indoor air

Inactive Publication Date: 2016-11-23
SHANGHAI CIMIC HEALTHY ENVIRONMENT TECH CO LTD
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the decorative material has the ability to release negative oxygen ions due to the use of tourmaline, the speed and strength of tourmaline to release negative oxygen ions are relatively small, and generally speaking, it can only release negative oxygen ions within a narrow range. Therefore, although researchers in this field know that tourmaline can release negative oxygen ions, and have been committed to using it in production and life to improve the environment, due to the radioactivity of tourmaline itself, it is difficult to add too much radioactivity. Reached, the amount of addition is small and cannot release enough negative oxygen ions, and the speed of releasing negative oxygen ions is very slow, and the release distance is very limited, it is difficult to effectively improve the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating capable of releasing negative oxygen ions, and preparation method and application thereof
  • Coating capable of releasing negative oxygen ions, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing a coating capable of releasing negative oxygen ions;

[0029] (1) Prepare raw materials by the following components in parts by weight:

[0030] Expanded vermiculite 5;

[0031] Tourmaline 0.5;

[0032] Adhesive 94.5.

[0033] The expanded vermiculite is formed by placing the vermiculite raw material in an extruding furnace at 600° C. for 30 seconds.

[0034] The particle diameter of described expanded vermiculite is 10 orders, and the particle diameter of described tourmaline is 5000 orders;

[0035] (2) Mixing material: mix the above-mentioned raw materials with a stirrer, and stir evenly to obtain a coated product. The stirring speed is 300rpm, and the stirring time is 10min.

[0036] The resulting coating is used on the surface of mineral wool boards, gypsum boards, calcium silicate boards, and fiberglass boards, and the negative ion coating is used for decoration with a breathable decorative surface.

Embodiment 2

[0038] A method for preparing a coating capable of releasing negative oxygen ions;

[0039] (1) Prepare raw materials by the following components in parts by weight:

[0040] Expanded vermiculite 25;

[0041] Tourmaline 1;

[0042] Adhesive 74.

[0043] The expanded vermiculite is formed by placing the vermiculite raw material in an extruding furnace at 600° C. for 30 seconds.

[0044] The particle diameter of described expanded vermiculite is 800 orders, and the particle diameter of described tourmaline is 3000 orders;

[0045] (2) Mixing material: mix the above-mentioned raw materials with a stirrer, and stir evenly to obtain a coated product. The stirring speed is 300rpm, and the stirring time is 10min.

[0046] The resulting coating is used on the surface of mineral wool boards, gypsum boards, calcium silicate boards, and fiberglass boards, and the negative ion coating is used for decoration with a breathable decorative surface.

Embodiment 3

[0048] A method for preparing a coating capable of releasing negative oxygen ions;

[0049] (1) Prepare raw materials by the following components in parts by weight:

[0050] Expanded vermiculite 15;

[0051] Tourmaline 4;

[0052] Adhesive 81.

[0053] The expanded vermiculite is formed by placing the vermiculite raw material in an extruding furnace at 600° C. for 30 seconds.

[0054] The particle diameter of described expanded vermiculite is 600 orders, and the particle diameter of described tourmaline is 2000 orders;

[0055] (2) Mixing material: mix the above-mentioned raw materials with a stirrer, and stir evenly to obtain a coated product. The stirring speed is 300rpm, and the stirring time is 10min.

[0056] The resulting coating is used on the surface of mineral wool boards, gypsum boards, calcium silicate boards, and fiberglass boards, and the negative ion coating is used for decoration with a breathable decorative surface.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a coating capable of releasing negative oxygen ions, and a preparation method and application thereof. The preparation method comprises the following steps: (1) weighing of raw materials: weighing, by weight, 1 to 30 parts of expanded vermiculite, 0.1 to 10 parts of tourmalinite and 60 to 99 parts of an adhesive; and (2) material mixing: uniformly mixing the raw materials under stirring by using a stirrer so as to obtain the coating capable of releasing negative oxygen ions. Compared with the prior art, the coating provided by the invention has the advantages of capacity of releasing negative oxygen ions, environment friendliness, good practicality and the like.

Description

technical field [0001] The invention relates to a building material, in particular to a coating capable of releasing negative oxygen ions and a preparation method thereof. Background technique [0002] Negative oxygen ions Known as "air vitamins", negative oxygen ions are beneficial to the physical and mental health of the human body. It mainly affects the physiological activities of the human body through the human nervous system and blood circulation. Negative oxygen ions can expand the capillaries of the human body, thereby promoting blood circulation and promoting the regeneration of cell tissues. And it can also prevent cell oxidation, which is the so-called anti-aging, promote metabolism, and improve immunity. In addition, it also has the effects of removing ignorance, preventing bacterial growth, preventing mildew, and storing heat. Tourmaline can release negative oxygen ions, but the rate and concentration of tourmaline releasing negative oxygen ions is low, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B26/00C04B41/65
Inventor 陈克俭上官军
Owner SHANGHAI CIMIC HEALTHY ENVIRONMENT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com