Anti-cracking floor tiles

A technology of floor tiles and bentonite, which is applied in the field of building materials, can solve problems such as being easily cracked by heavy objects and low surface strength, and achieve good radiation protection performance, scientific and reasonable formula, and low cost.

Inactive Publication Date: 2017-01-04
LIUZHOU YITING TRADE
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to facilitate people's travel and maintain the beautiful appearance of the city, people harden the sidewalk. The hardening of the existing road is to lay floor tiles on it. The existing floor tiles are generally made of limestone and sand. The strength is not high, and it is easy to be cracked by heavy objects. Therefore, how to manufacture a high-strength, heavy-duty, and unbreakable floor tile is a new problem that is constantly being solved by those skilled in the art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] This anti-cracking floor tile is made of raw materials of the following weights:

[0019] Bentonite: 16kg, Limestone: 25kg, Clay: 12kg, Barite: 5kg, Karaya Powder: 2kg, Glass Fiber: 2kg, Wood Fiber: 1kg;

[0020] It includes the following steps:

[0021] A. The barite, limestone, bentonite and clay are ground respectively, and then filtered with a 70-mesh sieve to obtain barite powder, lime powder, bentonite powder and clay powder, which are for subsequent use;

[0022] b. The barite powder, lime powder, bentonite powder and clay powder obtained in step A and karaya gum powder, glass fiber and wood fiber are put into the mixer, and are stirred at a speed of 3000 rev / min for 8 minutes to obtain a mixture;

[0023] c. Add water in the mixture that step B makes, stir 6 minutes with the speed of 4600 rev / min, wherein the weight ratio of mixture and water is 12:1, stale standby;

[0024] D. Put the mixture obtained in step C into a mold and press it into a primary embry...

Embodiment 2

[0027] This anti-cracking floor tile is made of raw materials of the following weights:

[0028] Bentonite: 19kg, Limestone: 35kg, Clay: 14kg, Barite: 10kg, Karaya Powder: 5kg, Glass Fiber: 5kg, Wood Fiber: 3kg;

[0029] The rest are the same as the first embodiment.

Embodiment 3

[0031] This anti-cracking floor tile is made of raw materials of the following weights:

[0032] Bentonite Clay: 17kg, Limestone: 30kg, Clay: 13kg, Barite: 8kg, Karaya Powder: 3kg, Glass Fiber: 4kg, Wood Fiber: 2kg;

[0033] The rest are the same as the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pressureaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses anti-cracking floor tiles and relates to the technical field of building materials. The anti-cracking floor tiles are prepared from, by weight, 16-19 parts of bentonite, 25-35 parts of limestone, 12-14 parts of clay, 5-10 parts of barite, 2-5 parts of karaya gum powder, 2-5 parts of glass fiber and 1-3 parts of wood fibers. The anti-cracking floor tiles are natural, environmentally friendly, high in strength and capable of bearing pressure, and do not easily break.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an anti-cracking floor tile. Background technique [0002] In order to facilitate people's travel and maintain the beauty of the city, people harden the sidewalks. The hardening of the existing roads is to lay floor tiles on them, and the existing floor tiles are generally made of limestone and sand. The problem is that the strength is not high and it is easy to be fractured by heavy objects. Therefore, how to manufacture a high-strength floor tile that can withstand heavy pressure and is not easy to crack is a new problem that is constantly solved by those skilled in the art. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to provide a floor tile that is natural and environmentally friendly, has high strength, can withstand heavy pressure and is not easily broken. [0004] In order to solve the above problems, the technical scheme of the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/80C04B33/04C04B33/13
CPCC04B35/80C04B33/04C04B33/1305C04B33/131C04B2235/3208C04B2235/448C04B2235/5212C04B2235/5216C04B2235/96
Inventor 王嘉龙
Owner LIUZHOU YITING TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap