Antibacterial soluble hemostatic material and preparation method thereof
A hemostatic material and soluble technology, applied in the field of medical devices, can solve the problem of no antibacterial function, and achieve excellent hemostatic effect, good biocompatibility, and no toxic and side effects.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] An antibacterial and soluble hemostatic material, prepared by acupuncture process of sodium carboxymethyl cellulose fiber and carboxymethyl chitosan fiber, the mass ratio of sodium carboxymethyl cellulose fiber and carboxymethyl chitosan fiber is 7:3.
[0027] The preparation method of the hemostatic material comprises the following steps:
[0028] (1) Pretreat the medical absorbent cotton fibers with absolute ethanol for 30 minutes;
[0029] (2) After the pretreatment, soak the medical absorbent cotton fibers in a mixed solution of ethanol and alkali (25wt%) (v / v=1:1) for alkalization at 30°C for 30 minutes;
[0030] (3) After the alkalization reaction is completed, add chloroacetic acid ethanol solution (acid-base ratio: 3:1) to the reaction system, react at 30°C for 30 minutes, raise the temperature to 70°C, and react for 2.5 hours;
[0031] (4) After the reaction, adjust the pH to 7 with a mixed solution of acetic acid ethanol (V / V=1:4), then wash with 80% ethanol...
Embodiment 2
[0037] An antibacterial and soluble hemostatic material, prepared by acupuncture process of sodium carboxymethyl cellulose fiber and carboxymethyl chitosan fiber, the mass ratio of sodium carboxymethyl cellulose fiber and carboxymethyl chitosan fiber is 7:3.
[0038] (1) Pretreat the medical absorbent cotton fiber for 30 minutes with absolute ethanol;
[0039] (2) After the pretreatment, soak the medical absorbent cotton fibers in a mixed solution of ethanol and alkali (25wt%) (v / v=1:1) for alkalization at 30°C for 30 minutes;
[0040] (3) After the alkalization reaction is completed, add chloroacetic acid ethanol solution (acid-base ratio: 4:1) to the reaction system, react at 30°C for 30 minutes, raise the temperature to 70°C, and react for 2.5 hours;
[0041] (4) After the reaction, adjust the pH to 7 with a mixed solution of acetic acid ethanol (V / V=1:4), then wash with 80% ethanol aqueous solution for 3 times, and finally obtain sodium carboxymethylcellulose fiber by fre...
Embodiment 3
[0047] An antibacterial and soluble hemostatic material, prepared by acupuncture process of sodium carboxymethyl cellulose fiber and carboxymethyl chitosan fiber, the mass ratio of sodium carboxymethyl cellulose fiber and carboxymethyl chitosan fiber is 7:3.
[0048] (1) Pretreat the medical absorbent cotton fibers with absolute ethanol for 30 minutes;
[0049] (2) After the pretreatment, soak the medical absorbent cotton fibers in a mixed solution of ethanol and alkali (30wt%) (v / v=1:1) for alkalization at 30°C for 30 minutes;
[0050] (3) After the alkalization reaction is completed, add chloroacetic acid ethanol solution (acid-base ratio: 3:1) to the reaction system, react at 30°C for 30 minutes, raise the temperature to 70°C, and react for 2.5 hours;
[0051] (4) After the reaction, adjust the pH to 7 with a mixed solution of acetic acid ethanol (V / V=1:4), then wash with 80% ethanol aqueous solution for 3 times, and finally obtain sodium carboxymethylcellulose fiber by fr...
PUM
Property | Measurement | Unit |
---|---|---|
Length | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap