A kind of spray paint and preparation method thereof

A paint and propellant technology, applied in coatings, anti-corrosion coatings, cellulose coatings, etc., can solve non-polar plastic substrate adhesion and color diversification, non-polar non-scratch resistance Adhesion to plastic substrates, undisclosed scratch resistance and weather resistance, etc., to achieve strong electroplating effect, good scratch resistance, and improve the weather resistance and decorative effects of the paint film

Active Publication Date: 2019-10-01
AMRICAN SANVO HONG KONG CHEM TECH HLDG LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

201510295321.3 discloses a paint with electroplating appearance effect and its preparation method and construction technology. This invention mainly solves the technical problems that the paint film of electroplated silver paint is thin, not resistant to alcohol, and easily eroded by UV varnish topcoat. , smooth, high hardness, strong wear resistance, excellent weather resistance, and extremely high scratch resistance; Specific instructions on the adhesion and color variety of permanent plastic substrates
The above 3 patents are not related to the scratch resistance performance of electroplating spray paint, outdoor weather resistance, adhesion to non-polar plastic substrates and rich colors. Specific descriptions and beneficial effects disclosure
[0008] 200810213292.1 disclosed Tuya automatic spray paint. This invention solves the problems of poor covering power of paint film, poor UV resistance and strong irritating odor. It has high solid content, super strong covering power, good weather resistance, low VOC, environmental protection and energy saving, etc. Advantages; but the specific data of its solid content and VOC content do not involve specific instructions on scratch resistance and adhesion to non-polar plastic substrates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of spray paint and preparation method thereof
  • A kind of spray paint and preparation method thereof
  • A kind of spray paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] S1. Add 4 parts of cyclohexane and 6 parts of sec-butyl acetate, start stirring, slowly add 5 parts of cellulose resin and 17 parts of acrylate modified petroleum resin, disperse at 1200r / min for 1.5h until completely dissolved;

[0041] S2, add 4 parts of cyclohexane, 6 parts of sec-butyl acetate, start stirring, add 2 parts of modified polyamide wax and stir well, add 6 parts of electroplating silver paste (average particle size is 10 microns), 0.8 parts of zinc powder in turn , continue to disperse for 0.5h after stirring;

[0042] S3. Add the remaining 12 parts of cyclohexane, 16 parts of sec-butyl acetate, 7 parts of butanone, 1 part of dimethyl carbonate, 1.4 parts of propylene glycol methyl ether, 0 parts of polyethylene modified acrylic resin, and 0.5 parts of phthalocyanine blue Slurry, turn on the machine and stir well, add S1 and S2 in turn in the dispersed state, add 1 part of cellulose resin, 0.5 part of nano-alumina after stirring, disperse at 800r / min for...

Embodiment 2

[0045] S1. Add 5 parts of cyclohexane and 5 parts of sec-butyl acetate, start stirring, slowly add 2 parts of cellulose resin and 18 parts of acrylate modified petroleum resin, disperse at 1200r / min for 1.5h until completely dissolved;

[0046] S2, add 5 parts of cyclohexane, 5 parts of sec-butyl acetate, start stirring, add 1.0 parts of modified polyamide wax and stir well, then add 4.5 parts of electroplating silver paste (average particle size is 6 microns), 0.5 parts of zinc powder , continue to disperse for 0.5h after stirring;

[0047]S3, add the remaining 15 parts of cyclohexane, 15 parts of sec-butyl acetate, 6 parts of butanone, 1 part of dimethyl carbonate, 2 parts of propylene glycol methyl ether, 6 parts of polyethylene modified acrylic resin, 0.8 part of phthalocyanine green pulp , turn on the machine and stir evenly, add S1 and S2 in turn in the dispersed state, add 1 part of cellulose resin, 1 part of nano-alumina after stirring, disperse at 800r / min for 10min, ...

Embodiment 3

[0050] S1. Add 6 parts of cyclohexane and 4 parts of sec-butyl acetate, start stirring, slowly add 3 parts of cellulose resin and 8 parts of acrylate modified petroleum resin, disperse at 1000r / min for 1 hour until completely dissolved;

[0051] S2, add 6 parts of cyclohexane, 4 parts of sec-butyl acetate, start stirring, add 1.5 parts of modified polyamide wax and stir well, add 5 parts of electroplating silver paste (average particle size is 8 microns), 0.5 parts of zinc powder in turn , and continue to disperse for 1 hour after stirring;

[0052] S3, add the remaining 15 parts of cyclohexane, 10 parts of sec-butyl acetate, 8 parts of butanone, 1.9 parts of propylene glycol methyl ether, 18 parts of chlorinated polypropylene modified acrylic resin, 1.6 parts of iron oxide red paste, start the machine and stir well, Add S1 and S2 sequentially in the dispersed state, stir well, add 1 part of cellulose resin, 2 parts of nano-alumina, disperse at 700r / min for 20 minutes, add 4.0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a spray lacquer. The spray lacquer is obtained by combining paint, an aerosol can, an aerosol valve, a propellant and stirring beads. The paint is prepared from, by weight, 22.0-35.0 parts of thermoplastic resin, 4.0-9.0 parts of metal powder, 0-2.0 parts of color paste, 2.0-9.0 parts of an adhesion promoter, 0.2-1.0 part of an anti-scratch flatting agent, 1.5-5.0 parts of an anti-scratch agent and 53.0-68.0 parts of a solvent. By the adoption of the technical scheme, the spray lacquer has the advantages that the spray lacquer is strong in electroplating effect, rich in color, good in corrosion resistance and capable of being covered with gloss oil, and the weather resistance and decorativeness of a lacquer film can be easily improved; the spray lacquer has good adhesion to a nonpolar substrate, and the lacquer film has excellent overall properties such as high hardness and good scratch resistance; the spray lacquer is high in solid content and does contain benzene solvents. The invention further discloses a preparation method of the spray lacquer.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a spray paint and a preparation method thereof. [0002] technical background [0003] Aerosol paint (also known as spray paint) usually consists of an aerosol can, an aerosol valve, content (paint) and a propellant, in addition to a stirring ball (glass bead) that is loaded into the aerosol can to help stir. As the main product in the aerosol industry, aerosol paint products have the advantages of flexible construction, flexible and convenient operation, rich and bright colors, excellent decorative effects, and excellent protection functions. They are widely used in metal, wood, glass, ABS plastics, etc. Coating of various substrates. [0004] Spray paint generally has the defects of low solid content and high VOC content. With the country's increasing emphasis on environmental protection and the collection of paint consumption tax, the solvent-based spray paint industry is facing a sev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D157/00C09D101/02C09D133/00C09D5/10
Inventor 陈炳耀陈炳强
Owner AMRICAN SANVO HONG KONG CHEM TECH HLDG LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com