A high-strength pc optical cable splice box

An optical cable splice box and high-strength technology, which is applied in the field of high-strength PC optical cable splice boxes, can solve the problems of low weather resistance and insufficient strength of the splice box, and achieve good weather resistance, good toughness, and high strength.

Active Publication Date: 2018-07-06
BOND GRP CO LTD +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a high-strength PC optical cable splice box with high strength, good toughness, anti-ultraviolet radiation, anti-aging and good weather resistance in order to solve the defects of low weather resistance and insufficient strength of the existing splice box

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength pc optical cable splice box
  • A high-strength pc optical cable splice box

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A high-strength PC optical cable splice box, the PC optical cable splice box contains the following components in parts by weight: 50 parts of modified polycarbonate, 45 parts of polyvinyl chloride, 30 parts of modified carbon fiber, 1 part of lubricant, and 1 part of nuclear agent, 5 parts of benzoyl peroxide, 4 parts of pentaerythritol stearate, 20 parts of calcium carbonate powder, 1 part of antioxidant, 6 parts of UV protection agent, 3 parts of modified graphene, 1 part of nano-silicon carbide 5 parts with nanometer chromium carbide.

[0023] The modification method of modified graphene is: 25 parts by weight of graphene oxide are dispersed in 300 parts by weight of trishydroxymethylaminomethane buffer solution and ultrasonically treated for 2h to obtain a suspension; then 200 parts by weight of dicyclohexyl Carboimide, 155 parts by weight of dimethyl siloxane and 120 parts by weight of dibutyl sebacate, heated to 280°C for 2 hours after ultrasonication for 20 minu...

Embodiment 2

[0029] A high-strength PC optical cable splice box, the PC optical cable splice box contains the following components in parts by weight: 63 parts of modified polycarbonate, 58 parts of polyvinyl chloride, 36 parts of modified carbon fiber, 2 parts of lubricant, and 1.5 parts of nucleating agent, 6 parts of benzoyl peroxide, 5 parts of pentaerythritol stearate, 25 parts of calcium carbonate powder, 2 parts of antioxidant, 7 parts of UV protection agent, 4 parts of modified graphene, 2 parts of nano silicon carbide 6 parts with nanometer chromium carbide.

[0030]The modification method of modified graphene is: 25 parts by weight of graphene oxide are dispersed in 300 parts by weight of trishydroxymethylaminomethane buffer solution and ultrasonically treated for 2h to obtain a suspension; then 200 parts by weight of dicyclohexyl Carboimide, 155 parts by weight of dimethylsiloxane and 120 parts by weight of dibutyl sebacate, heated to 300°C for 3 hours after ultrasonication for ...

Embodiment 3

[0036] A high-strength PC optical cable splice closure, the PC optical cable splice closure contains the following components in parts by weight: 75 parts of modified polycarbonate, 60 parts of polyvinyl chloride, 50 parts of modified carbon fiber, 3 parts of lubricant, and 2 parts of nuclear agent, 7 parts of benzoyl peroxide, 6 parts of pentaerythritol stearate, 35 parts of calcium carbonate powder, 3 parts of antioxidant, 10 parts of UV protection agent, 7 parts of modified graphene, 3 parts of nano-silicon carbide parts and 10 parts of nano-chromium carbide.

[0037] The modification method of modified graphene is: 25 parts by weight of graphene oxide are dispersed in 300 parts by weight of trishydroxymethylaminomethane buffer solution and ultrasonically treated for 2h to obtain a suspension; then 200 parts by weight of dicyclohexyl Carboimide, 155 parts by weight of dimethylsiloxane and 120 parts by weight of dibutyl sebacate, heated to 320°C for 4 hours after ultrasonica...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-strength PC optical cable connect, which comprises the following components, by weight part, 50-75 parts of modified polycarbonate, 45-60 parts of polyvinyl chloride, 30-50 parts of modified carbon fibers, 1-3 parts of a lubricant, 1-2 parts of a nucleating agent, 5-7 parts of benzoyl peroxide, 4-6 parts of pentaerythrityl tetrastearate, 20-35 parts of calcium carbonate powder, 1-3 parts of an antioxidant, 6-10 parts of an ultraviolet screening agent, 3-7 parts of modified graphene, 1-3 parts of nanometer silicon carbide and 5-10 parts of nanometer chromium carbide. The high-strength PC optical cable connect is flame-retardant, waterproof and shockproof, is high in strength, and is good in toughness, ultraviolet resistance, aging resistance and weathering resistance.

Description

technical field [0001] The invention relates to a high-strength PC optical cable joint box with high strength, good toughness, anti-ultraviolet, anti-aging and good weather resistance. Background technique [0002] China's Twelfth Five-Year Plan requires to improve China's informatization level. Therefore, during the Twelfth Five-Year Period, the communication industry will definitely accelerate its development. With the entry of optical cables into rural areas, the scale of the industry will increase day by day, and the durability of the system will be improved. Reducing the accident rate becomes a problem that needs to be considered. [0003] In modern transmission technology, optical cable splice closures are widely used in communication, network systems, CATV cable television, and optical cable network systems. According to the optical cable connection method, the splice box can be divided into two types: straight-through connection and branch connection. Due to the st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L27/06C08L63/00C08K13/06C08K9/04C08K9/02C08K7/06C08K3/04C08K5/14C08K5/103C08K3/26C08K3/34C08K3/14C08K3/22
CPCC08K2201/011C08K2201/014C08L27/06C08L69/00C08L2201/02C08L2201/08C08L2203/20C08L2205/03C08L63/00C08K13/06C08K9/04C08K9/02C08K7/06C08K3/04C08K5/14C08K5/103C08K2003/265C08K3/34C08K3/14C08K2003/2241C08K2003/2296
Inventor 胡德林
Owner BOND GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap