Microcellular foaming self-cleaning type plastic plate and preparation method thereof

A plastic sheet, self-cleaning technology, applied in the sheet field, can solve the problems of poor storage stability of composite materials, complex preparation process, nanoparticle agglomeration, etc., and achieve the effect of preventing soft agglomeration, improving interface structure, and good photocatalytic ability

Inactive Publication Date: 2017-04-26
ANHUI BEIMA TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, due to the large specific surface area and high surface energy of nano-TiO2, which is in a non-thermodynamic stable state, the prepared composite materials are prone to the disadvantages of nanoparticle agglomeration, poor storage stability of the composite material, and complicated preparation process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A micro-foaming self-cleaning plastic sheet, which is composed of the following parts by weight of raw materials:

[0021] Dibutyl phthalate 3, azodicarbonamide 1, pentaerythritol 3, zinc dialkyl dithiophosphate 0.4, calcium ricinoleate 1, titanium tetrachloride 10, ferric chloride 3.7, 25% peroxide Hydrogen 6, methyl methacrylate 7, azobisisobutyronitrile 0.1, polyvinyl chloride 100, silane coupling agent kh5600.7, stannous sulfide 0.3, tert-butyl hydroquinone 0.7, ammonium polyphosphate 3, poly Sorbate 800.6, calcium borate 2.

[0022] A method for preparing the micro-foaming self-cleaning plastic sheet includes the following steps:

[0023] (1) Add the above-mentioned ammonium polyphosphate to 14 times its weight in deionized water, stir evenly, raise the temperature to 53°C, keep stirring for 10 minutes, add the above-mentioned polysorbate 80, and stir to room temperature to obtain a water emulsion;

[0024] (2) Add the above-mentioned titanium tetrachloride to 60 times it...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a microcellular foaming self-cleaning type plastic plate. The microcellular foaming self-cleaning type plastic plate is prepared from raw materials in parts by weight as follows: 3-4 parts of dibutyl phthalate, 1-2 parts of azodicarbonamide, 3-4 parts of pentaerythritol, 0.4-1 part of zinc dialkyl dithiophosphate, 1-2 parts of calcium ricinoleate, 10-14 parts of titanium tetrachloride, 3.7-4 parts of ferric chloride, 6-8 parts of hydrogen peroxide with concentration of 25%-30%, 7-9 parts of methyl methacrylate, 0.1-0.2 parts of azodiisobutyronitrile, 100-130 parts of polyvinyl chloride, 0.7-1 part of a silane coupling agent kh5600, 0.3-1 part of stannous sulfide, 0.7-1 part of tert-butyl hydroquinone, 3-5 parts of ammonium polyphosphate, 0.6-1 part of polysorbate 80 and 2-4 parts of calcium borate. Added Fe-doped titanium dioxide has quite good photocatalysis capacity, and pollutants attached to the surface of the plate can be degraded and removed, so that self-cleaning performance is realized.

Description

Technical field [0001] The invention relates to the technical field of board, in particular to a micro-foaming self-cleaning plastic board and a preparation method thereof. Background technique [0002] Titanium dioxide is a transition metal oxide and also a semiconductor material. Because of its good biocompatibility, resistance to chemical corrosion, and harmlessness to the human body, it is also rich in materials due to the rich content of titanium sources. And because of its low price, it has attracted widespread attention. The application of titanium dioxide is reflected in all aspects of people's lives. At present, the use of titanium dioxide inorganic products has reached the world's leading level. Due to the characteristics of titanium dioxide, it can be used as a very important inorganic chemical material, so it has a huge influence and application in many fields such as national defense aviation, industrial production, and cutting-edge technology. Titanium dioxide can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/10C08K13/06C08K9/06C08K9/04C08K3/32C08K3/22C08K3/38C08J9/10
CPCC08J9/103C08J2203/04C08J2327/06C08J2451/10C08L27/06C08L2201/08C08L2203/14C08L2205/03C08L51/10C08K13/06C08K9/06C08K9/04C08K2003/323C08K2003/2241C08K2003/387
Inventor 陈篯孙维乐
Owner ANHUI BEIMA TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap