A kind of hybrid organic framework material and its preparation method and application

A metal-organic framework and hybrid technology, applied in chemical instruments and methods, refined hydrocarbon oil, inorganic chemistry, etc., can solve the problems of limited service life of materials, unassisted desulfurization application technology, high development cost, and offset steric hindrance. Influence, enhance the desulfurization effect, the effect of strong thermal stability

Active Publication Date: 2019-05-21
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the development cost of imidazole metal-organic framework materials is very high, and its ligand methylimidazole is corrosive and expensive, so it is not conducive to product promotion and application
In addition, the zeolite imidazole framework material falls off during the regeneration process, resulting in a limited service life of the material; moreover, the adsorbent is developed for the mercaptan components in gasoline, and its scope of application is limited, which is not helpful for the increasingly inferior gasoline and diesel desulfurization applications technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hybrid organic framework material and its preparation method and application
  • A kind of hybrid organic framework material and its preparation method and application
  • A kind of hybrid organic framework material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Weigh 5gCu(NO 3 ) 2 ·3H 2 O. Add 3g of 1,4,5,8-naphthalene tetracarboxylic acid into 2000g of acetone aqueous solution, the volume ratio of acetone and water is 1:2, the pH after mixing is 0.73, and put it in an ultrasonic oscillator after airtight, adjust the ultrasonic The frequency is 100KHz, the ultrasonic power is 450W, and it is ultrasonically oscillated at room temperature until a sky blue precipitate appears. Add 0.27 g of soluble starch aqueous solution with a mass concentration of 25 wt % dropwise, keep the ultrasonic conditions unchanged, and continue ultrasonication for 35 min. The obtained mixed solution is suction-filtered, and the filter cake is put into an aqueous acetone solution containing ammonium chloride. The mass ratio of the filter cake to ammonium chloride is 1:1, and the ratio of ammonium chloride to acetone is 1g:120mL. The volume ratio to water is 1:2, and the mechanical stirring is performed at 70 rpm for 60 min. The above solution was su...

Embodiment 2

[0040] The method and raw material are basically the same as in Example 1, except that the copper source is replaced with CuSO of equal quality 4 ·5H 2 O, other reaction conditions and material composition remain unchanged, and hybrid metal-organic framework material B is obtained.

Embodiment 3

[0042] The method and raw material of embodiment 1 are basically the same, the difference is: the volume ratio of acetone and water in the aqueous acetone solution is adjusted to 1:10, and the volume ratio of acetone and water in the aqueous acetone solution containing ammonium chloride is adjusted to 1:10, Other reaction conditions and material composition remain unchanged, and a hybrid metal-organic framework material C is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hybridized organic framework material preparation method. The method comprises the following steps: 1) adding 1,4,5,8-naphthalene tetracarboxylic acid and a copper source in a solvent, uniformly mixing the materials, performing first ultrasonic treatment, when a precipitate is generated, adding a starch slouble aqueous solution, continuously performing secondary ultrasonic processing; and 2) filtering a mixture through secondary ultrasonic processing, placing a filtered solid in an acetone aqueous solution containing ammonium salt and stirring the materials, then filtering the material, washing the material with water and drying the material to obtain the hybridized organic framework material. The invention also provides the hybridized organic framework material prepared by the method and an application thereof. The hybridized organic framework material has strong thermostability and appropriate pore structure, has more active sites and good space symmetry, and is suitable for an adsorption desulphurization process for fuel oil such as gasoline and diesel oil.

Description

technical field [0001] The invention relates to a hybrid metal organic framework material and its preparation method application, in particular to an organic framework material which can be used for fuel oil adsorption and its preparation method and application. Background technique [0002] With the world's increasing emphasis on environmental protection and the increasingly stringent environmental regulations, the production of low-sulfur and ultra-low-sulfur fuel oil is gradually attracting people's attention. The main forms of sulfide in fuels are mercaptans, sulfides, disulfides and thiophene organic sulfides, especially the thiophenes have a large content and are difficult to remove. Although traditional hydrodesulfurization can effectively remove sulfides such as thiophenes, there are disadvantages such as loss of octane number, high equipment investment and operating costs, so other low-cost fuel oil deep desulfurization technologies are urgently needed. Adsorption ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/22B01J20/28B01J20/30C10G25/00
Inventor 赵亮邢兵王海洋马蕊英王刚
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap