A technology for screen printing and screen printing, which is applied in the field of screen printing, can solve the problems such as the reuse of screen printing plates without thick stencils and the poor reuse effect of screen printing plates, and achieves reduction of printing costs, clear printing and good effect. Good results

Active Publication Date: 2020-05-08
南阳天一密封股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a material for reusing screen printing screens and a method for reusing the same, which solves the problem of poor reusing effect of existing screen printing screens and the lack of reuse of screen thick mold printing screens in the field of automobile plate making. Technology and other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A material for reusing screen printing screen plates, including photosensitive adhesive and release powder, the photosensitive adhesive includes 100 parts of alcohol-soluble binary copolymerized nylon, 20 parts of acrylamide and bisacrylamide monomers in parts by weight part, 3.5 parts of benzophenone and 0.08 part of thermostabilizer, described acrylamide: the weight ratio of bisacrylamide is 1:1; Described release powder comprises 50 parts of sodium metaperiodate in parts by weight , 8 parts of surfactant, 1 part of chelating agent, 6 parts of peroxide, 4 parts of inorganic salt.

[0023] Surfactant is fatty alcohol polyoxyethylene ether sodium sulfate.

[0024] The mixture is stearyl citrate.

[0025] The peroxide is ammonium persulfate.

[0026] Inorganic salts are sodium chloride and KClO 4 , and their weight ratio is 1:1.

[0027] A method for reusing silk screen screen plates, comprising the following steps:

[0028] (1) Mix the photosensitive adhesive and a...

Embodiment 2

[0033] A material for reusing screen printing screen plates, including photosensitive adhesive and release powder, the photosensitive adhesive includes 100 parts of alcohol-soluble ternary copolymerized nylon, 35 parts of acrylamide and bisacrylamide monomers in parts by weight part, 4.8 parts of benzophenone and 0.16 part of thermostabilizer, described acrylamide: the weight ratio of bisacrylamide is 1: 2; Described release powder comprises 55 parts of sodium metaperiodate in parts by weight , 5 parts of surfactant, 2 parts of chelating agent, 8 parts of peroxide, 3 parts of inorganic salt.

[0034] The surfactant is sodium α-sulfo fatty acid methyl ester.

[0035] The chelating agent is ethylenediaminetetraacetic acid.

[0036] The peroxide is potassium persulfate.

[0037] The inorganic salt is potassium chloride and KClO, and their weight ratio is 1:2.

[0038] A method for reusing silk screen screen plates, comprising the following steps:

[0039] (1) Mix the photosen...

Embodiment 3

[0044] A material for reusing screen printing screen plates, including photosensitive adhesive and release powder, the photosensitive adhesive includes 100 parts by weight of alcohol-soluble ternary copolymerized nylon, 30 parts of acrylamide and bisacrylamide monomers part, 2.6 parts of benzophenone and 0.23 part of heat stabilizer, described acrylamide: the weight ratio of bisacrylamide is 1:1.5; Described release powder comprises 60 parts of sodium metaperiodate in parts by weight , 10 parts of surfactant, 3 parts of chelating agent, 10 parts of peroxide, 5 parts of inorganic salt.

[0045] The surfactant is sodium alkylbenzene sulfonate.

[0046] The chelating agent is tricarboxymethylamine.

[0047] The peroxide is sodium persulfate.

[0048] The inorganic salt is sodium carbonate and KClO, and their weight ratio is 1:1.

[0049] A method for reusing silk screen screen plates, comprising the following steps:

[0050] (1) Mix the photosensitive adhesive and absolute et...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a reutilization material for a silk screen board and a reutilization method of the reutilization material. The material comprises sensitive glue and demolding powder, the sensitive glue comprises, by weight, 100 parts of second alcohol soluble or nylon terpolymer, 20-35 parts of acrylic amide and bisacrylamide monomers, 2.6-4.8 parts of benzophenone and 0.08-0.23 parts of heat stabilizer, and the weight ratio of the acrylic amide to the bisacrylamide is 1: (1-2). The demolding powder comprises, by weight, 50-60 parts of sodium metaperiodate, 5-10 parts of surface active agents, 1-3 parts of chelating agents, 6-10 parts of peroxide and 3-5 parts of inorganic salt. Characteristics of thick molding printing screen are considered on the whole, clearly printing and completely demolding are achieved by the aid of sensitive glue, demolding powder and demolding process of mutual coordination effects, silk screen tension of the silk screen board is larger than or equal to 20N / CM based on completely demolding, normal circulation use requirements are met, the silk screen board can be reutilized by 7-8 times, and printing cost is effectively reduced.

Description

technical field [0001] The invention relates to a material for reusing screen printing screen plates and a reusing method thereof, belonging to the technical field of screen printing. Background technique [0002] The method of direct plate making in the automotive industry is to first put the photosensitive film coated with photosensitive material face up on the working table, put the stretched screen frame flat on the film base, and then put it in the screen frame. The photosensitive paste is coated under pressure with a soft scraper, and the plastic film base is removed after it is fully dried, and the photosensitive film wrist screen is attached to the printing plate, and the screen printing screen is produced after developing and drying. Most of the screen frames are made of aluminum alloy screen frames. Since the pre-applied glue on the surface of the gasket plays a role in strengthening the seal, thick film printing is used. The special photosensitive glue on the surf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G03F7/42G03F7/027G03F7/004
CPCG03F7/004G03F7/027G03F7/42
Inventor 赵红祥江柏桥杨松涛陈宇翔朱建周樊红星张冰潭
Owner 南阳天一密封股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap