Guided tissue regeneration membrane and preparation method thereof
A technology for guiding tissue regeneration and membrane precursors, which can be used in the field of medical materials to solve problems such as excessive degradation in vivo and poor mechanical strength.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0027] Such as figure 1 The preparation method of the guided tissue regeneration film includes the following steps:
[0028] S10, pretreating the skin of the mammal to obtain a dermis slice.
[0029] The operation of obtaining the dermis skin piece after pretreatment of the mammalian skin is as follows: the mammalian skin is preliminarily degreased and depilated by a mechanical method, and then the mammalian skin is removed with a skin removal machine to remove 0.1mm to 0.4mm. After the epidermis and subcutaneous fat tissue, a dermis slice with a thickness of 0.2 mm to 1 mm was made.
[0030] Generally, the dermis skin can be cut into skins with a size of 3cm×6cm~5cm~10cm.
[0031] Mammalian skin consists of successive layers of fur, epidermis, dermis, and subcutaneous tissue.
[0032] Specifically, the skin of mammals is the skin of pigs, cattle, sheep or horses. Preferably, the mammalian skin is belly skin of pigs, cows, sheep or horses.
[0033] The obtained dermis sli...
Embodiment 1
[0059] (1) Preparation of dermal slices
[0060] Preliminarily degrease the whole abdominal skin of healthy pigs by mechanical method, remove the hair with tweezers, remove the subcutaneous fat of the pigskin with an electric skin remover, and then remove 0.4mm of the epidermis to make a dermis with a thickness of 0.3mm The skin slices were then soaked in an aqueous solution of penicillin-streptomycin with a mass concentration of 0.01%, placed in a refrigerator at 4°C overnight, and then transferred to a low-temperature refrigerator at -25°C for storage.
[0061] (2) Preparation of membrane precursor for guided tissue regeneration
[0062] Decellularization treatment: Soak the thawed dermis slices successively in 0.1% sodium chloride (hypotonic salt) and 1.0% sodium chloride (hypertonic salt) solutions for 2 times, 6h / time , through the treatment of hypotonic solution, the tissue absorbs water and swells, so that the cells in the tissue are broken, and the collagen fiber stru...
Embodiment 2
[0070] (1) Preparation of dermal slices
[0071] Preliminarily degrease the whole abdominal skin of healthy pigs by mechanical method, remove the hair with tweezers, remove the subcutaneous tissue of the pigskin with an electric skin remover, and then remove 0.1mm of the epidermis to make a dermis with a thickness of 0.9mm The skin slices were then soaked in an aqueous solution of gentamicin with a mass concentration of 0.1%, placed in a refrigerator at 4°C overnight, and then transferred to a low-temperature refrigerator at -25°C for storage.
[0072] (2) Preparation of membrane precursor for guided tissue regeneration
[0073] Decellularization treatment: soak the thawed dermis slices successively in a solution with a mass concentration of 0.9% sodium chloride (hypotonic salt) and a mass concentration of 9.0% sodium chloride (hypertonic salt) for 3 times, 4h / time , through the treatment of hypotonic solution, the tissue absorbs water and swells, so that the cells in the tissu...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap