Manufacturing method of composite board

A manufacturing method and composite board technology, applied in the field of board manufacturing, can solve the problems of large cost input, high usage, deformation of boards, etc., and achieve the effects of protecting the environment, reducing usage, and reducing load-bearing performance.

Inactive Publication Date: 2017-05-31
天津市统业家俱工贸有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the process of making steel-wood furniture, the use of boards is high and the cost is high. However, due to the high load-bearing effect in furniture production and the need to prevent deformation of the boards, high-priced boards such as solid wood are often used in production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] An embodiment of the present invention will be briefly described below in conjunction with an embodiment.

[0015] The working process of this example:

[0016] A method for manufacturing a composite panel, comprising the steps of:

[0017] (1) heat-press forming the straw into a straw board for subsequent use;

[0018] (2) Apply hot melt adhesive evenly on both sides of the straw board;

[0019] (3) The hot melt adhesive is covered with metal mesh;

[0020] (4) Enter the roller press, heat to 180-220°C and roll repeatedly, the number of times of rolling is not less than 3 times;

[0021] (5) The outer layer of metal mesh and hot melt adhesive is coated with adhesive, and the outer layer of adhesive is covered with fiberboard;

[0022] (6) The outer layer of the fiberboard is coated with adhesive, and then covered with wooden boards, and rolled without heating, and the number of times of rolling is not less than 3 times;

[0023] (7) The outer layer of the board is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a manufacturing method of a composite board. The manufacturing method comprises the following steps: processing straw into a straw board for later use through hot-press molding; uniformly coating the two surfaces of the straw board with a hot-melt adhesive; covering the hot-melt adhesive with metal nets; entering a roller press, heating to 180-220 DEG C, and repeatedly carrying out roller pressing for not less than three times; coating the outer layers of the metal nets and the hot-melt adhesive with a bonding agent, and covering the outer layer of the bonding agent with fiber boards; coating the outer layers of the fiber boards with a bonding agent, covering the bonding agent with wood boards, keeping the temperature, and carrying out roller pressing for not less than three times; and coating the outer layers of the wood boards with paint and drying the paint. The bearing force of the board can be effectively increased, the expansion deformation of the composite board is avoided, the tenacity of the board is enhanced, and a pure solid board material can be replaced. The deformation probability of the board material is reduced under the condition of keeping the bearing performance of the board material, the usage of the solid board material is gradually reduced, and the environment is protected.

Description

technical field [0001] The invention relates to the field of plate manufacturing methods, in particular to a manufacturing method of a composite plate. Background technique [0002] In the process of making steel-wood furniture, the amount of boards used is high and the cost investment is large. However, due to the high load-bearing effect in furniture production and the need to prevent deformation of the boards, expensive boards such as solid wood are often used in production. Solid wood boards are increasingly scarce, and overexploitation of forests will cause great harm to the environment. How to manufacture composite boards to replace solid wood boards and reduce the deformation probability of boards while maintaining the load-bearing performance of the boards has become an urgent problem to be solved. Contents of the invention [0003] In order to overcome the shortcomings of the existing plate manufacturing methods, the invention provides a composite plate manufactu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/00B32B37/10B32B37/12
CPCB27D1/00B32B37/10B32B37/12
Inventor 银国清
Owner 天津市统业家俱工贸有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More