Method for preparing high density porous two-dimensional molybdenum disulfide nanosheet

A molybdenum disulfide and nanosheet technology, applied in molybdenum sulfide, chemical instruments and methods, chemical/physical processes, etc., can solve the problems of easy falling off, complicated operation, low atomic ratio, etc., and achieve precise adjustment of size and density, Porous structure is ordered and the effect of avoiding loss

Active Publication Date: 2017-06-20
山东天汇光年无人机科技有限公司
View PDF14 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Two-dimensional MoS 2 Generally, there are two phases: semiconductor phase (2H phase) and metal phase (1T phase). Studies have shown that 2H-MoS 2 The catalytic activity of MoS comes from the unsaturated bonding atoms at the boundary, while the in-plane atoms do not have catalytic activity, which makes the proportion of atoms that can contribute to the catalytic activity very low, which seriously restricts the MoS 2 Catalytic hydrogen evolution ability
[0004] However, the preparation of SV-MoS 2 The nanosheet process requires the MoS 2 The transfer of nanosheets to other substrates is relatively complicated, and the transferred MoS 2 The adhesion between the nanosheet and the substrate is not strong, and it is easy to fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high density porous two-dimensional molybdenum disulfide nanosheet
  • Method for preparing high density porous two-dimensional molybdenum disulfide nanosheet
  • Method for preparing high density porous two-dimensional molybdenum disulfide nanosheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0031] Such as figure 1 Shown is the flow process of the method for preparing high-density porous two-dimensional molybdenum disulfide nanosheets, the method comprising,

[0032] 101. Prepare an ordered aluminum nanohole AAO array template;

[0033] Once oxidized, the aluminum sheet with a purity of 99.999% will be oxidized at a temperature of 0.6°C, a voltage of 24V, and 0.3wt.% H 2 SO 4 Under the chemical conditions, after 24 hours of oxidation, the alumi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of nanomaterial preparation and particularly relates to a method for preparing a high density porous two-dimensional molybdenum disulfide nanosheet. The method comprises preparing an ordered aluminum nanometer hole AAO array template, directly forming a single layer of MoS2 nanosheets on a SiO2 / Si base through a CVD method, transferring the ordered aluminum nanometer hole AAO array template to the single layer of MoS2 nanosheets to obtain a MoS2 nanosheet sample, transferring the MoS2 nanosheet sample into an ion etching chamber, carrying out etching, bombarding the MoS2 nanosheet sample, and removing the template of the MoS2 nanosheet sample to obtain the high density porous two-dimensional molybdenum disulfide nanosheets. The method can introduce a boundary-like structure to the base surface of the two-dimensional MoS2 to increase the number of active sites, can directly form a single layer of MoS2 on the SiO2 / Si base, prevents MoS2 transferring and prevents a MoS2 loss during the transferring.

Description

technical field [0001] The invention relates to the technical field of nanomaterial preparation, in particular to a method for preparing high-density porous two-dimensional molybdenum disulfide nanosheets. Background technique [0002] Energy and the environment are topics that are closely related to us, and the contradiction between the two seems sharp and irreconcilable at present, but there is a magical balance between them-clean energy. Among them, the high-efficiency electrolysis of water for hydrogen production is recognized as the "leader" in the method of obtaining clean energy (hydrogen energy). However, the development of suitable catalysts to accelerate the process of electrolysis of water for hydrogen production to achieve commercial-scale production of hydrogen energy has always been a challenge for scientists. Headache problem. At present, materials with good catalytic performance (noble metals such as Pt and Pb) are very expensive. Therefore, various catalyst...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G39/06B01J27/051B01J35/10
CPCC01G39/06B01J27/051C01P2004/20C01P2002/82C01P2004/03C01P2004/02B01J35/60
Inventor 张璋苏绍强曾志强汤丹程鹏飞林晓姿雷勇
Owner 山东天汇光年无人机科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products