Polypropylene filler yarn and preparation method thereof

A technology of polypropylene filling rope and polypropylene resin, which is applied in the field of polypropylene filling rope and its preparation, can solve the problems of insufficient tensile strength, easy breakage, cable roundness and decrease in compressive and tensile strength, and achieve improved Compressive and tensile performance, retention performance, and toughness improvement effect

Inactive Publication Date: 2017-06-23
中山市华子电缆有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polypropylene is widely used as a filler for wires and cables due to its excellent mechanical properties, such as the manufacture of polypropylene filled ropes, but the current polypropylene filled ropes have insufficient tensile strength and are easy to break, resulting in the use of cables. The roundness and compressive and tensile capacity of the steel pipe are reduced, which cannot meet the requirements of medium and high-end wire and cable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A polypropylene filling rope, which is made of polypropylene resin (Maoming Sinopec T03), filler masterbatch (Hongbao Plastic Chemical Technology Co., Ltd. CP28), defoamer (Hongbao Plastic Chemical Technology Co., Ltd. BP608) and hot extrusion , cutting, polypropylene resin and filler masterbatch are mixed at a weight ratio of 1:1, and the proportion of defoamer added is 1 / 25 of the total weight of polypropylene resin and filler masterbatch after mixing.

[0025] Its preparation method is:

[0026] Step 1: At a temperature of 75°C, mix polypropylene resin and filler masterbatch in a mixer according to the proportion, stir for 20 minutes, then add defoamer, continue stirring for no less than 15 minutes, and form a mixture after stirring evenly material;

[0027] Step 2: Soften the mixed material in the main machine of the hot extrusion machine. The temperature in the main machine is 180-220 ° C. After that, the softened mixed material is extruded into a film through the...

Embodiment 2

[0032] A polypropylene filling rope, which is made of polypropylene resin (Maoming Sinopec T03), filler masterbatch (Hongbao Plastic Chemical Technology Co., Ltd. CP28), defoamer (Hongbao Plastic Chemical Technology Co., Ltd. BP608) and hot extrusion , cutting, polypropylene resin and filler masterbatch are mixed at a weight ratio of 1:3, and the proportion of defoamer added is 1 / 25 of the total weight of polypropylene resin and filler masterbatch after mixing.

[0033] Its preparation method is identical with embodiment 1.

[0034] The film thickness of the polypropylene filling rope is 0.1±0.03mm, and the finished products with film widths of 10mm, 20mm, 30mm, 40mm and 50mm are tested.

Embodiment 3

[0036] A polypropylene filling rope, consisting of polypropylene resin (Maoming Sinopec T03), filler masterbatch (75 parts of calcium carbonate, 15 parts of paraffin, 10 parts of silane coupling agent), defoamer (Hongbao Plastic Chemical Technology Co., Ltd. BP608) mixed and hot-extruded and cut. Polypropylene resin and filler masterbatch are mixed at a weight ratio of 1:1. The proportion of defoamer added is 1 / 1 of the total weight of polypropylene resin and filler masterbatch. 25.

[0037] Its preparation method is:

[0038] Step 1: Under the temperature condition of 75°C, mix the polypropylene resin and the filler masterbatch in the mixer according to the proportion, stir for 20 minutes, then add the defoamer, continue stirring, and then rotate and mix evenly in the hopper. The rotational speed is 16 rpm;

[0039] Step 2: Soften the mixed material in the main machine of the hot extrusion machine. The temperature in the main machine is 180-220 ° C. After that, the softened...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polypropylene filler yarn. The polypropylene filler yarn is prepared by the following steps: mixing polypropylene resin, a filling master batch and a defoaming agent; carrying out hot extrusion and cutting, wherein the weight ratio of the polypropylene resin to the filling master batch is 1 to 1 or 1 to 3; the adding proportion of the defoaming agent is 1 / 25 of total weight of a mixture of the polypropylene resin and the filling master batch. According to the polypropylene filler yarn disclosed by the invention, the polypropylene resin and the filling master batch are used as raw materials; by means of the filling master batch, the toughness of the polypropylene filler yarn is improved, the tensile and compressive performances of the polypropylene filler yarn are improved, the tensile rate reaches 20 to 30 percent, and the tensile strength is 6 to 10N / mm; by adding the defoaming agent, the performance of the polypropylene filler yarn is favorably further maintained and the influence of bubbles on the performance of the polypropylene filler yarn in a production process is avoided.

Description

technical field [0001] The invention relates to the field of cable filling rope manufacture, in particular to a polypropylene filling rope and a preparation method thereof. Background technique [0002] The wire and cable industry accounts for 1 / 4 of the output value of China's electrical industry. It has a wide range of applications, involving electric power, construction, communication, manufacturing and other industries, and is closely related to various sectors of the national economy. Wires and cables are also known as the "arteries" and "nerves" of the national economy. They are indispensable basic equipment for transmitting electric energy, transmitting information, manufacturing various motors, instruments, and meters, and realizing electromagnetic energy conversion. Basic products necessary in a modernized society. [0003] Polypropylene, English name: Polypropylene, referred to as polypropylene, is a thermoplastic resin made by polymerizing propylene. Polypropyle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L91/06C08K3/26C08K5/54B29C47/92B29C48/92
CPCC08L23/12B29C48/92B29C2948/92704C08J5/18C08J2323/12C08J2491/06C08L2203/202C08L91/06C08K2003/265C08K5/54
Inventor 桑梓华
Owner 中山市华子电缆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products