A kind of preparation method of ti2alnb alloy wire material

An alloy wire and rod technology, which is applied in the field of preparation of Ti2AlNb alloy wire, can solve the problem that automatic repair welding process cannot be applied, and achieve the effect of avoiding crack defects and improving plasticity.

Active Publication Date: 2018-05-29
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At this stage, under laboratory conditions, the wire cutting method is used to cut strips on the ingot to prepare welding filler materials. Due to the length limitation, the wire prepared by this method cannot be used in the automatic repair welding process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1, to prepare Ti2AlNb wire with a diameter of 1.6 mm, the steps of adopting the method of the present invention are as follows:

[0020] 1. Pier pulling: The Ti2AlNb ingot with a diameter of 45mm is forged by free forging, and the pier drawing is repeated twice, and the diameter of the pier pulling ingot is still 45mm;

[0021] 2. Forging: Put the Ti2AlNb ingot after pier drawing into the furnace for heat treatment, the temperature of entering the furnace is 900 °C, and then the temperature is raised to 1100 °C with the furnace, holding for 20 minutes, and then forging is started. The forging temperature is 1050 °C and the final forging temperature is 950 °C. Follow-up mill caliber requirements, obtain forged bars with a diameter of 30mm;

[0022] 3. Rolling: The forged bar is first kept at 930 °C for 30 minutes, then heated to 980 °C with the furnace, and held for 10 minutes, and then rolled. The rolling temperature is about 980 °C, and the final rolling tem...

Embodiment 2

[0025] Embodiment 2, preparing Ti2AlNb wire with a diameter of 1.2mm, the steps of adopting the method of the present invention are as follows:

[0026] 1. Pier pulling: The Ti2AlNb ingot with a diameter of 60mm is forged by free forging, and the pier pulling is repeated 5 times, and the diameter of the pier pulling ingot is still 60mm;

[0027] 2. Forging: Put the Ti2AlNb ingot after the pier drawing into the furnace for heat treatment, the temperature of entering the furnace is 900 °C, then the temperature is raised to 1200 °C with the furnace, and the temperature is kept for 20 minutes, and then the forging is started. Follow-up mill caliber requirements, obtain forged bars with a diameter of 28mm;

[0028] 3. Rolling: The forged bar is first kept at 950 °C for 30 minutes, then heated to 1050 °C with the furnace, and held for 15 minutes, and then rolled. The rolling temperature is about 980 °C, and the final rolling temperature is 850 °C. Wire rods with a diameter of 8.5mm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of Ti2AlNb alloy wires. The method comprises the steps that a Ti2AlNb alloy ingot is forged, rolled and annealed through a specific technology, repeated drawing is carried out according to the specific reducing amplitude, and finally the Ti2AlNb alloy wires with the needed diameter are obtained. The low-plasticity difficult-to-machine material Ti2AlNb intermetallic compound wires are prepared through the drawing technology, the high-quality Ti2AlNb wires can be obtained, batch high-quality production of the wires is achieved, and the method can be applied in the field of welding, 3D printing and the like and is wide in application prospect.

Description

technical field [0001] The invention relates to a preparation method of Ti2AlNb alloy wire, belonging to the technical field of metal material processing. Background technique [0002] Ti2AlNb is an intermetallic compound with an ordered orthorhombic O phase as the main constituent phase. The alloy is an excellent structural material with the characteristics of low density, high specific strength, good corrosion resistance, good creep resistance and oxidation resistance, and has great hope as an alternative material for nickel-based superalloys. Widely used in aerospace field. However, a huge obstacle affecting its use is its low room temperature plasticity and poor thermal deformation ability. Although it is slightly better than TiAl-based alloys, it is still a difficult-to-deform material. [0003] At present, due to the characteristics of poor plasticity at room temperature and difficult processing of Ti2AlNb alloy, in actual work, the main forming method of this alloy ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21C37/04B21C9/02C22F1/16
CPCB21C9/02B21C37/047C22F1/16
Inventor 施瀚超李建崇郑涛乔燕琦
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com