A high-strength zirconia setter plate and its manufacturing method

A production method and technology of setter plates, which are applied in furnaces, lighting and heating equipment, charging support, etc., can solve the problems of short service life, economic loss of enterprises, and low strength, so as to achieve the goal of not easily deforming, improving service life, Make simple effects

Active Publication Date: 2019-03-19
湖南仁海科技材料发展有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The setter plate is widely used in many fields. Its main function is that the fired product must be placed on the setter plate during the high-temperature firing process. For some special fired products, it cannot be placed on the general bearing plate. The zirconia setter plate must be used on the firing board, but the zirconia setter board in the prior art is damaged during use due to its low strength, the service life is not long, and it needs to be replaced for a long time, so not only the replacement It is troublesome, and it causes waste, which brings certain economic losses to the enterprise.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength zirconia setter plate and its manufacturing method
  • A high-strength zirconia setter plate and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The present invention provides such Figure 1-2 The shown high-strength zirconia setter includes a setter body 1, and a reinforcement rod is arranged inside the setter body 1, and the reinforcement rod includes a transverse reinforcement rod 3 and a longitudinal reinforcement rod 4, and the transverse The reinforcing rods 3 and the longitudinal reinforcing rods 4 are perpendicular to each other, and there are at least 3 sets of the transverse reinforcing rods 3 and the longitudinal reinforcing rods 4 respectively. It is located above the transverse reinforcing rod 3, and the transverse reinforcing rod 3 and the longitudinal reinforcing rod 4 are bound and fixed by tungsten wires. The edge of the setter body 1 is provided with a protective plate 2.

[0026] The present invention also provides a method for manufacturing a high-strength zirconia setter plate, comprising the following steps:

[0027] S1: Select the K500 Monel alloy pipe with a diameter of 2mm, and cut it i...

Embodiment 2

[0034] The present invention provides such Figure 1-2 The shown high-strength zirconia setter includes a setter body 1, and a reinforcement rod is arranged inside the setter body 1, and the reinforcement rod includes a transverse reinforcement rod 3 and a longitudinal reinforcement rod 4, and the transverse The reinforcing rods 3 and the longitudinal reinforcing rods 4 are perpendicular to each other, and there are at least 3 sets of the transverse reinforcing rods 3 and the longitudinal reinforcing rods 4 respectively. It is located above the transverse reinforcing rod 3, and the transverse reinforcing rod 3 and the longitudinal reinforcing rod 4 are bound and fixed by tungsten wires. The edge of the setter body 1 is provided with a protective plate 2.

[0035] The present invention also provides a method for manufacturing a high-strength zirconia setter plate, comprising the following steps:

[0036] S1: Select the K500 Monel alloy pipe with a diameter of 3mm, and cut it i...

Embodiment 3

[0043] The present invention provides such Figure 1-2 The shown high-strength zirconia setter includes a setter body 1, and a reinforcement rod is arranged inside the setter body 1, and the reinforcement rod includes a transverse reinforcement rod 3 and a longitudinal reinforcement rod 4, and the transverse The reinforcing rods 3 and the longitudinal reinforcing rods 4 are perpendicular to each other, and there are at least 3 sets of the transverse reinforcing rods 3 and the longitudinal reinforcing rods 4 respectively. It is located above the transverse reinforcing rod 3, and the transverse reinforcing rod 3 and the longitudinal reinforcing rod 4 are bound and fixed by tungsten wires. The edge of the setter body 1 is provided with a protective plate 2.

[0044]The present invention also provides a method for manufacturing a high-strength zirconia setter plate, comprising the following steps:

[0045] S1: Select the K500 Monel alloy pipe with a diameter of 2.5mm, and cut it ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength zirconia setter plate and a manufacturing method thereof. The high-strength zirconia setter plate comprises a setter plate body internally provided with stiffeners. Each stiffener comprises a transverse stiffener and a longitudinal stiffener which are perpendicular to each other, and protective plates are arranged around the edge of the setter plate body. The high-strength zirconia setter plate and the manufacturing method thereof have the beneficial effects that the high-strength zirconia setter plate is novel in structure design, through the multiple sets of stiffeners and the surrounding protective plates, the strength of the zirconia setter plate can be improved, the service life is prolonged, the manufacturing method of the zirconia setter plate is simple in manufacturing and reasonable in design, and the strength of the zirconia setter plate is improved.

Description

technical field [0001] The invention belongs to the technical field of zirconia setter plates, and in particular relates to a high-strength zirconia setter plate and a manufacturing method thereof. Background technique [0002] The setter plate is widely used in many fields. Its main function is that the fired product must be placed on the setter plate during the high-temperature firing process. For some special fired products, it cannot be placed on the general bearing plate. The zirconia setter plate must be used on the firing plate, but the zirconia setter plate in the prior art, due to its low strength, will be damaged during use, the service life is not long, and it needs to be replaced for a long time, so not only the replacement It is troublesome, and it causes waste, which brings certain economic losses to the enterprise. Contents of the invention [0003] The object of the present invention is to provide a high-strength zirconia setter and its manufacturing metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F27D5/00C04B35/80C04B35/48
CPCF27D5/00C04B35/48F27M2003/04
Inventor 潘建华
Owner 湖南仁海科技材料发展有限公司