A coating process and color technology, which is applied to the surface coating device, coating, special surface, etc., can solve the problems that the chroma cannot be high, and the color depth cannot be displayed, and the operating energy consumption and The effect of low material cost, small amount of modification, and simple post-processing

Inactive Publication Date: 2017-08-18
湖南湘江关西涂料有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the traditional pearlescent red on the market is usually made by mixing pearlescent and ordinary colors, and the chroma cannot be very high. Because the pearlescent and ordinary pigments are mixed together, it cannot show the deep sense of color.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment l

[0029] A car color painting process, which is: ED (primer layer) + intermediate coating (1PH drying) + BC1 metallic color paint layer + BC2 transparent color paint layer (2PH pre-baking) + varnish, the specific process operation is as follows :

[0030] First surface treatment of the steel plate → cathodic electrophoretic primer → primer workpiece 170 ℃ * 20min baking, the film thickness is required to be 20-25um, cooling → primer grinding and cleaning → mid-coat spraying → leveling 7 minutes and then 140 ℃ * Dry for 30 minutes, the film thickness is required to be 30-40um, cool down → use a robot for BC1 coating, flash dry for 2 minutes after spraying, and the film thickness is required to be 8 μm → use a robot for BC2 coating, leveling for 3 minutes after spraying, pre-baking Bake at 80°C for 5 minutes, cool to room temperature, the film thickness is required to be 8 μm → use an automatic machine for coating, level off for 10 minutes after spraying, and then dry at 140°C for...

Embodiment 2

[0038] A car color painting process, which is: ED (primer layer) + intermediate coating (1PH pre-baking) + BC1 metallic color paint layer + BC2 transparent color paint layer (2PH pre-baking) + varnish, the specific process operation as follows:

[0039] First surface treatment of the steel plate → cathodic electrophoretic primer → primer workpiece 170 ℃ * 20min baking, the film thickness is required to be 20-25um, cooling → primer grinding and cleaning → water-based medium coating spraying → 80 ℃ after leveling for 3 minutes *5min pre-baking, the film thickness is required to cool at 25-30um → use a robot for BC1 coating, flash dry for 2 minutes after spraying, and the film thickness is required to be 8μm → use a robot for BC2 coating, leveling for 3 minutes after spraying, pre-baking Bake at 80℃*5min, cool to room temperature, the film thickness is required to be 8μm→use an automatic machine for coating, level off for 10min after spraying, and then dry at 140℃*25min, the film...

Embodiment 3

[0047] A car color painting process, which is: ED (primer layer) + mid-coat (1PH flash dry) + BC1 metallic paint layer + BC2 transparent paint layer (2PH pre-baking) + varnish, the specific process operation is as follows :

[0048] First, surface treatment of the steel plate → cathodic electrophoretic primer → bake the primer workpiece at 170°C*20min, the film thickness is required to be 20-25um, cool down → polish the primer → spray water-based medium coating → flash dry for 384s, the film thickness It is required to be 20-25um → use a robot for BC1 coating, flash dry for 2 minutes after spraying, and the film thickness is required to be 8 μm → use a robot for BC2 coating, leveling for 3 minutes after spraying, pre-baking at 80°C for 5 minutes, and cooling to At room temperature, the film thickness is required to be 8 μm → use an automatic machine for coating, level off for 10 minutes after spraying, and then dry at 140°C for 25 minutes. The film thickness is required to be ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an automobile color coating process. The coating process comprises the steps of ED coating, floating coat coating, BC1 metal-color paint layer coating, BC2 transparent color paint layer coating and varnish coating. According to the coating process, the light transmission principle is utilized to improve the red color chroma and the angle-dependent color change degree, so that the red charm degree is increased; an automobile coating line does not need to be changed in a large range, by adding one color paint can, the red color chroma can be greatly higher than that of the existing colors, and the 15-degree chroma of the red color adopting the coating process can reach 90-100 while the 15-degree chroma of the mainstream red color in the market is 50-70. According to the coating process, the existing water-based advanced processes 3C1B and 3C2B are combined so that the energy-saving and environment-friendly effects can be effectively carried out.

Description

technical field [0001] The invention belongs to the field of automobile painting techniques, and in particular relates to an automobile color painting technique. Background technique [0002] Red is the most important color in China, and even the cultural totem and spiritual conversion of the Chinese nation. It represents lively, festive and peaceful in China. [0003] The high-glamor red in the color of the car requires high chroma, and at the same time, it needs to show a sense of luxury through the metallic feeling of different colors at different angles, and show a sense of depth through color transparency. [0004] At present, the traditional pearlescent red on the market is usually made by mixing pearlescent and ordinary colors, and the chroma cannot be very high. Because the pearlescent and ordinary pigments are mixed together, the color depth cannot be displayed. [0005] The traditional water-based 3C1B (2PH) red process is: ED primer layer + middle coat (1PH pre-b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B05D5/06B05D7/00
CPCB05D5/06B05D7/574
Inventor 欧阳海云凌文文杨鹏飞张杰敖志强张少康
Owner 湖南湘江关西涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap