Mask environment-friendly flame retardant foaming material and preparation method thereof

A foamed material and an environmentally friendly technology, which is applied in the field of environmentally friendly flame-retardant foamed materials for masks and their preparation, can solve the problems of poor flame retardancy, short escape time for personnel, hidden dangers and the like

Inactive Publication Date: 2017-10-27
YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, with the development of the automobile industry and the enhancement of people's awareness of safety and environmental protection, people's requirements for auto parts have also increased significantly. , High environmental protection characteristics, the characteristics of traditional masks usually can not achieve the ideal effect, in the event of an emergency, often due to poor flame retardancy, the escape time of personnel is short, and there is a great potential safety hazard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An environmentally friendly flame-retardant foaming material for a face mask, comprising the following preparation steps: firstly, a composite material is prepared in parts by mass:

[0021] Polyester 3628: 30 parts;

[0022] Polyether 330: 40 parts;

[0023] Polyether 403: 25 parts;

[0024] Glass fiber: 200 parts;

[0025] Polyether 135: 25 parts;

[0026] Silicone oil: 3 parts;

[0027] Catalyst A33: 1.5 parts;

[0028] Strong catalyst HP-50: 1.2 parts;

[0029] Water: 4.8 parts;

[0030] Flame retardant DMMP: 30 parts.

[0031] Add the above materials into the reaction kettle for mixed reaction, wherein the silicone oil is silicone oil AK-8803, the stirring speed is 130r / min, and the stirring time is 5h to obtain the combined material, and then the acetonitrile polyester and the combined material are mixed at a ratio of 1:1.4 The mass ratio is mixed evenly, and the environment-friendly flame-retardant foaming material for the mask can be prepared.

Embodiment 2

[0033] An environmentally friendly flame-retardant foaming material for a face mask, comprising the following preparation steps: firstly, a composite material is prepared in parts by mass:

[0034] Polyester 3628: 35 parts;

[0035] Polyether 330: 45 parts;

[0036] Polyether 403: 26.5 parts;

[0037] Glass fiber: 250 parts;

[0038] Polyether 135: 30 parts;

[0039] Silicone oil: 3.25 parts;

[0040] Catalyst A33: 1.75 parts;

[0041] Strong catalyst HP-50: 1.7 parts;

[0042] Water: 4.8 parts;

[0043] Flame retardant DMMP: 34 parts.

[0044] Put the above materials into the reaction kettle for mixed reaction, wherein the silicone oil is silicone oil AK-8803, the stirring speed is 140r / min, and the stirring time is 4.5h to obtain the combined material, and then the acetonitrile polyester and the combined material are mixed according to 1: The mass ratio of 1.4 is mixed evenly, and the environment-friendly flame-retardant foaming material for the mask can be prepared....

Embodiment 3

[0046] An environmentally friendly flame-retardant foaming material for a face mask, comprising the following preparation steps: firstly, a composite material is prepared in parts by mass:

[0047] Polyester 3628: 40 parts;

[0048] Polyether 330: 50 parts;

[0049] Polyether 403: 28 parts;

[0050] Glass fiber: 300 parts;

[0051] Polyether 135: 35 parts;

[0052] Silicone oil: 3.5 parts;

[0053] Catalyst A33: 2.5 parts;

[0054] Strong catalyst HP-50: 2.2 parts;

[0055] Water: 4.8 parts;

[0056] Flame retardant DMMP: 38 parts.

[0057] Put the above materials into the reaction kettle for mixed reaction, wherein the silicone oil is silicone oil AK-8803, the stirring speed is 150r / min, and the stirring time is 4h to obtain the combined material, and then the acetonitrile polyester and the combined material are mixed at a ratio of 1:1.4 The mass ratio is mixed evenly, and the environment-friendly flame-retardant foaming material for the mask can be prepared.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a mask environment-friendly flame retardant foaming material and a preparation method thereof. The mask environment-friendly flame retardant foaming material is prepared from the following components including acetonitrile polyester and a composition material with the mass proportion of 1 to 1.4; the composition material is prepared from the following components in parts by mass: 30-40 parts of polyester 3628, 40-50 parts of polyether 330, 25-28 parts of polyether 403, 200-300 parts of glass fiber, 25-35 parts of polyether 135, 3-3.5 parts of silicone oil, 1.5-2.5 parts of catalyst A33, 1.2-2.2 parts of powerful catalyst HP-50, 4.8 parts of water and 30-38 parts of flame retardant DMMP, wherein the silicone oil is silicone oil AK-8803. The preparation method comprises the following steps: adding the components of the composition material in a reaction kettle to carry out mixing reaction with the stirring speed being 130-150r / min and the stirring time being 4-5h to obtain the composition material, then uniformly mixing the acetonitrile polyester and the composition material according to the mass ratio of 1 to 1.4 to prepare the mask environment-friendly flame retardant foaming material. By adopting the materials and the method, the prepared mask environment-friendly flame retardant foaming material is high in high temperature resistance performance, flame retardant performance and strength, and is environmentally friendly.

Description

technical field [0001] The invention relates to an environment-friendly flame-retardant foaming material for a mask and a preparation method thereof, belonging to the field of automobiles. Background technique [0002] At present, with the development of the automobile industry and the enhancement of people's awareness of safety and environmental protection, people's requirements for auto parts have also increased significantly. , High environmental protection characteristics, the characteristics of traditional masks usually can not achieve a more ideal effect, in the event of an emergency, often due to poor flame retardancy and resulting in a short escape time, there is a great safety hazard. Therefore, exploring high-strength, high flame-retardant, high-environmental protection foaming materials is the goal that this field has been pursuing. Contents of the invention [0003] The object of the present invention is to overcome the defects in the prior art, and provide an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/48C08G18/42C08K7/14C08K5/521C08J9/08C08G101/00
CPCC08G18/4018C08G18/42C08G18/4804C08K5/521C08K7/14C08G2110/0083
Inventor 朱章娣朱凌宇纪朝根
Owner YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap