Colorful powdered ink, preparation method thereof and method for digital thermal transfer printing

A color toner and resin technology, applied in the field of color toner and its preparation, digital thermal transfer printing, can solve the problems of equipment maintenance, high maintenance cost, strict temperature and humidity environment requirements, and high ink cost, and meet the equipment operating environment requirements. Low cost, flexible printing and low paper cost

Inactive Publication Date: 2017-11-07
邯郸汉光办公自动化耗材有限公司
View PDF8 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] At present, digital thermal transfer printing mainly uses inkjet ink. Compared with traditional printing technology, the printing precision is high, no plate making is required, the batch is flexible, and personalized e-commerce consumption can be realized through the network, but the printing speed is slow and the cost of ink is high. , the nozzle is easy to be blocked during use, the temperature and humidity environment of the equipment operation is strictly required, and the maintenance and repair costs of the equipment are relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colorful powdered ink, preparation method thereof and method for digital thermal transfer printing
  • Colorful powdered ink, preparation method thereof and method for digital thermal transfer printing
  • Colorful powdered ink, preparation method thereof and method for digital thermal transfer printing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The preparation of black toner among the present invention comprises the steps:

[0041] (1) According to the formula proportioning in table 1, styrene-acrylic resin, dispersion black, wax, charge regulator are mixed uniformly, form mixture A;

[0042] (2) The mixture A is melted and mixed by a kneader (mixing temperature 100° C.), and then pressed into tablets to form flakes, which are then mechanically crushed to a particle size of 1 to 2 mm;

[0043] (3) The flakes that have been mechanically crushed enter the jet mill (pressure 1.0MPa, frequency 50Hz), ultra-fine crushing and grading system (speed 15000rpm, air volume 100Nm 3 / h), to obtain a graded product with a volume D50 of 6-7 μm;

[0044] (4) After mixing the classified product and the external additive, stirring for 5 minutes at a stirring rate of 30 m / s, a black toner was obtained.

[0045] Preparation of yellow, red and blue toner:

[0046] Using the preparation method of the above-mentioned black toner,...

Embodiment 2

[0053] The preparation of black toner among the present invention comprises the steps:

[0054] (1) According to the formula ratio in Table 1, polyester resin, styrene-acrylic resin, disperse black, wax, and charge regulator are mixed uniformly to form mixture A;

[0055] (2) The mixture A is melted and mixed by a kneader (mixing temperature 130° C.), and then pressed into tablets to form flakes, and the flakes are then mechanically crushed to a particle size of 1 to 2 mm;

[0056] (3) The mechanically crushed flakes enter the jet mill (pressure 0.8MPa, frequency 40Hz), ultra-fine crushing and grading system (speed 13000rpm, air volume 60Nm 3 / h), to obtain a graded product with a volume D50 of 8-9 μm;

[0057] (4) After mixing the classified product and the external additive, stirring was carried out for 7 minutes at a stirring rate of 40 m / s to obtain a black toner.

[0058] Preparation of yellow, red and blue toner:

[0059] Using the preparation method of the above-ment...

Embodiment 3

[0066] The preparation of black toner among the present invention comprises the steps:

[0067] (1) According to the formula ratio in Table 1, the polyester resin, disperse black, wax, and charge regulator are mixed uniformly to form mixture A;

[0068] (2) The mixture A is melted and mixed by a kneader (mixing temperature 150° C.), and then pressed into tablets to form flakes, which are then mechanically crushed to a particle size of 1 to 2 mm;

[0069] (3) The mechanically crushed flakes enter the jet mill (pressure 0.7MPa, frequency 35Hz), ultra-fine crushing and grading system (speed 12000rpm, air volume 40Nm 3 / h), to obtain a graded product with a volume D50 of 9 to 10 μm;

[0070] (4) After mixing the graded product and the external additive, stirring for 10 min at a stirring rate of 50 m / s, a black toner was obtained.

[0071] Preparation of yellow, red and blue toner:

[0072] Using the preparation method of the above-mentioned black toner, replace the disperse bla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses colorful powdered ink, a preparation method thereof and a method for digital thermal transfer printing. The colorful powdered ink is composed of, by mass, 77-95% of resin, 2-8% of disperse dye, 2-7% of paraffin, 0.1-4% of charge control agent and 0.9-4% of external addition agent. The colorful powdered ink, with disperse printing dye, prepared through a dry-type physical method has the function of thermal transfer printing. After patterns are printed through a laser printing machine, the patterns can be subjected to transfer printing on substrates of textile products, ceramic, metal, glass, plastic and others through transfer printing equipment by the adoption of a thermal transfer technology of 180-230 DEG C and 10-120 s. Compared with a current ink-spraying thermal transfer technology, the method for digital thermal transfer printing has the advantages that printing speed is high, the production technology is mature, the production process is safer and environmentally friendlier, cost is low, the substrates are wide in application range, the firmness of the patterns after transfer printing is good, and the method is suitable for large-scale printing and personalized customization.

Description

technical field [0001] The invention relates to a color toner used in laser printers and copiers, in particular to a color toner, a preparation method thereof, and a digital thermal transfer printing method. Background technique [0002] Laser printers and electrostatic copiers are the main equipment of office automation. Toner, the main consumable for printing and copying, has a huge market and has become the main growth point of industry output value and profit. [0003] Color toner (also known as color toner) is a key consumable for color laser printing and color digital copying. It is mainly composed of resins, pigments, charge regulators, and various additives. At present, toner preparation methods are mainly divided into two types: physical method (that is, traditional melting and pulverization method) and chemical method (suspension polymerization method, aggregation-fusion method, etc.). [0004] At present, laser printing color toners used in office usually use org...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03G9/08
CPCG03G9/08G03G9/0802
Inventor 续守民杜丽英李杨彭立政李振华杨联明
Owner 邯郸汉光办公自动化耗材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap