A kind of antibacterial calligraphy and painting paper with controllable wetness and preparation method thereof

A technology of calligraphy and painting paper and antibacterial agent, which is applied in the field of papermaking, can solve the problems of poor antibacterial and anti-corrosion ink moistening properties, failure to meet quality standards, and low porosity of calligraphy and painting paper, and achieve improved paper strength, good physical strength indicators, and excellent biological properties. active effect

Active Publication Date: 2020-01-14
SOUTH CHINA UNIV OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using bamboo pulp to make auxiliary pulp to produce calligraphy and painting paper, although to a certain extent alleviated the problem of shortage of raw material sources, inevitably leads to a decline in product quality, and even fails to meet the requirements of quality standards
Bamboo pulp and some auxiliary materials contain high hemicellulose content, and contain a small amount of impurities such as protein, pectin, and miscellaneous cells, resulting in low porosity, low bulk, poor water absorption, and poor air permeability of calligraphy and painting paper, which further leads to paper. Poor anti-bacterial and anti-corrosion properties, and some defects in ink wetting
[0005] Based on the current situation of machine-made calligraphy and painting paper due to the poor antibacterial ability of raw materials and paper sheets, it is necessary to find a low-cost, high-efficiency antibacterial and anti-corrosion process to make up for the shortcomings of poor durability of machine-made painting and calligraphy paper; Sexual adjustment method to produce calligraphy and painting paper with different ink moistening properties to meet the needs of different groups of people

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antibacterial calligraphy and painting paper with controllable wetness and preparation method thereof
  • A kind of antibacterial calligraphy and painting paper with controllable wetness and preparation method thereof
  • A kind of antibacterial calligraphy and painting paper with controllable wetness and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] (1) preparation of online slurry;

[0070] ① stock preparation

[0071] Wherein the bleached bamboo pulp fiber utilizes a hydropulper to disintegrate, and after screening and slag removal, beating is carried out, and the degree of beating is 30 ° SR to obtain bleached bamboo pulp for subsequent use; the asparagus fiber is disintegrated through a hydropulper, screened, Beating after slag removal, beating degree is 35 ° SR, obtains asparagus pulp, standby; Proportioning is bleached bamboo pulp in pulp tank: the mass ratio of asparagus pulp is 5:5;

[0072] ②Preparation of compound antibacterial agent

[0073] Chitosan (Jinan Tianben Biotechnology Co., Ltd., molecular weight 9.0×10) with deacetylation degree greater than 90% 4 ) was dissolved in a dilute acetic acid solution with a concentration of 3.0% by mass, and stirred for 3 hours; then according to the ratio of chitosan: inorganic antibacterial agent mass ratio of 1:1, adding silver ion inorganic antibacterial agen...

Embodiment 2

[0088] (1) preparation of online slurry;

[0089] ① stock preparation

[0090] Wherein the bleached bamboo pulp fiber utilizes a hydropulper to disintegrate, and after screening and slag removal, beating is performed, and the degree of beating is 35 ° SR to obtain bleached bamboo pulp for subsequent use; wherein the asparagus fiber is disintegrated through a hydropulper, screened , beating after slag removal, beating degree is 40 ° SR, obtains asparagus straw pulp, for subsequent use; Proportioning is bleached bamboo pulp in pulp tank: the mass ratio of asparagus straw pulp is 6:4;

[0091] ②Preparation of compound antibacterial agent

[0092] Chitosan (molecular weight is 9.0×10 4 ) was dissolved in a dilute acetic acid solution with a concentration of 3.5% by mass, stirred for 3 hours, and added a silver ion inorganic antibacterial agent (Japan Oasis 7600-Ag+25) according to the ratio of chitosan: inorganic antibacterial agent mass ratio of 1:1 , adjust the concentration ...

Embodiment 3

[0107] (1) preparation of online slurry;

[0108] ① stock preparation

[0109]Wherein the bleached bamboo pulp fiber utilizes a hydropulper to disintegrate, and is beaten after screening and slag removal, and the beating degree is 40°SR to obtain bleached bamboo pulp for subsequent use; wherein the asparagus fiber is disintegrated through a hydropulper, screened , beating after slag removal, beating degree is 35 ° SR, obtains asparagus straw pulp, for subsequent use; Proportioning is bleached bamboo pulp in pulp tank: the mass ratio of asparagus straw pulp is 7:3;

[0110] ②Preparation of compound antibacterial agent

[0111] Chitosan (molecular weight is 9.0×10 4 ) was dissolved in a dilute acetic acid solution with a concentration of 4.0% by mass, stirred for 3 hours, and added a silver ion inorganic antibacterial agent (Japan Oasis 7600-Ag+25) according to the ratio of chitosan: inorganic antibacterial agent mass ratio of 1:1 , adjust the concentration of the solution to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
drynessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antibacterial writing and painting paper having a controllable wetting property, and a making method thereof. The antibacterial writing and painting paper having a controllable wetting property comprises raw materials and assistants, the raw materials comprise, by weight, 50-70 parts of bleached bamboo pulp fibers and 30-50 parts of Eulaliopsis binata fibers, and the assistants (by absolutely dry slurry) comprise, by weight, 0.8-1.6 parts of a composite antibacterial agent, 0.1-0.4 part of a dispersant, 0.05-0.1 part of a retention aid and 1.0-10.0 parts of light calcium carbonate. Chitosan and the inorganic silver ion composite antibacterial agent are used to realize antibacterial and anticorrosive effects and utilize the enhancement effect of the chitosan, so various strength indexes of the paper are improved; and the use amount of the light calcium carbonate is controlled to improve the wetting property of the paper, so the applicability of the writing and painting paper is improved.

Description

technical field [0001] The invention belongs to the technical field of papermaking, and in particular relates to an antibacterial calligraphy and painting paper with controllable wettability and a preparation method thereof. Background technique [0002] Calligraphy and painting paper is a special paper for calligraphy and painting in our country, and it is one of the "four treasures of the study" in our country. There are many performance indicators of calligraphy and painting paper, mainly including the absorbency, ink wetting, durability and some strength indicators of the paper. The absorbency and ink-wetting properties of paper are mainly related to the fiber raw materials used in production, while the antibacterial and anti-corrosion properties of paper are mainly determined by the production process. [0003] At present, calligraphy and painting paper is mainly made of cotton, hemp, leather and other raw materials, compounded with some short-fiber pulp such as broad-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21H11/12D21H27/00D21H17/24D21H17/67D21H17/63D21H19/14D21H21/36D21H23/50D21F11/06
CPCD21F11/06D21H11/12D21H17/24D21H17/63D21H17/675D21H17/74D21H19/14D21H21/36D21H23/50D21H27/007
Inventor 杨仁党王阳刘旭
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap