High-toughness chemical-resistant cable sheath material

A technology of cable sheathing material and chemical resistance, applied in the direction of rubber insulators, organic insulators, etc., to achieve the effect of excellent elasticity and chemical resistance

Inactive Publication Date: 2017-11-24
ANHUI LIETA CABLE GROUP
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] When chemical instruments are used, the toughness and chemical resistance of electrical cables are very high. The cables used in chemical instruments in the prior art cannot meet the needs of actual use. Therefore, continue to develop a high-toughness and chemical-resistant cable. Sheath material to solve the problems in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness chemical-resistant cable sheath material
  • High-toughness chemical-resistant cable sheath material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A high-toughness and chemical-resistant cable sheathing material proposed by the present invention, its raw materials include by weight: 100 parts of xanthic acid-modified medium-high Mooney neoprene rubber, 20 parts of dioctyl phthalate, formosan 5 parts of base silicone oil, 60 parts of carbon nanotube, 60 parts of glass fiber, 2 parts of light magnesium oxide, 0.5 part of stearic acid, 0.5 part of antioxidant ODA, 1 part of dispersant, 3 parts of zinc oxide, accelerator NA-22 0.5 parts, silane coupling agent KH-550 0.1 parts.

Embodiment 2

[0021] The present invention proposes a high-toughness and chemical-resistant cable sheathing material, whose raw materials include by weight: 100 parts of xanthic acid-modified medium-high Mooney neoprene rubber, 15 parts of dioctyl phthalate, formazan 10 parts of base silicone oil, 75 parts of carbon nanotubes, 40 parts of glass fiber, 3 parts of light magnesium oxide, 1 part of stearic acid, 1 part of antioxidant ODA, 2 parts of dispersant, 5 parts of zinc oxide, accelerator NA-22 1 part, silane coupling agent KH-550 0.3 part.

Embodiment 3

[0023] A high-toughness and chemical-resistant cable sheathing material proposed by the present invention, its raw materials include by weight: 100 parts of xanthic acid-modified medium-high Mooney neoprene rubber, 10 parts of dioctyl phthalate, formazan 15 parts of base silicone oil, 85 parts of carbon nanotubes, 30 parts of glass fiber, 4 parts of light magnesium oxide, 1.5 parts of stearic acid, 1.5 parts of antioxidant ODA, 3 parts of dispersant, 10 parts of zinc oxide, accelerator NA-22 1.5 parts, silane coupling agent KH-550 0.6 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-toughness chemical-resistant cable sheath material which comprises the following raw materials in parts by weight: 100 parts of chloroprene rubber, 5-20 parts of dioctyl phthalate, 5-20 parts of methyl silicon oil, 60-110 parts of carbon nanotubes, 10-60 parts of a glass fiber, 2-5 parts of light magnesium oxide, 0.5-2.5 parts of stearic acid, 0.5-2.5 parts of an anti-aging agent, 1-5 parts of a dispersing agent, 3-10 parts of zinc oxide, 0.5-2.5 parts of an accelerant and 0.1-1 part of another accelerant. The high-toughness chemical-resistant cable sheath material disclosed by the invention is excellent in toughness and chemical resistance.

Description

technical field [0001] The invention relates to the technical field of cables, in particular to a high-toughness and chemical-resistant cable sheathing material. Background technique [0002] When chemical instruments are used, the toughness and chemical resistance of electrical cables are very high. The cables used in chemical instruments in the prior art cannot meet the needs of actual use. Therefore, continue to develop a high-toughness and chemical-resistant cable. The sheathing material solves the problems in the prior art. Contents of the invention [0003] In order to solve the technical problems in the background technology, the present invention proposes a high-toughness and chemical-resistant cable sheathing material, which has excellent toughness and chemical resistance. [0004] A high-toughness and chemical-resistant cable sheath material proposed by the present invention, its raw materials include by weight: 100 parts of neoprene rubber, 5-20 parts of diocty...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L15/00C08L83/04C08K13/04C08K7/14C08K5/12C08K7/24C08K3/22C08K5/09C08K5/544H01B3/28
CPCC08L15/00C08K2003/222C08K2003/2296C08L2203/202H01B3/28
Inventor 张晓飞胡世安齐迎忠
Owner ANHUI LIETA CABLE GROUP