Mildew-resistant emulsion paint capable of clearing dampness

A latex paint and dehumidification technology, applied in latex paint, biocide-containing paint, anti-fouling/underwater paint, etc., can solve problems such as cracking, peeling, and affecting the appearance of objects, and achieve efficient anti-mildew technology and prevent The effect of mildew on the wall

Inactive Publication Date: 2017-11-28
杨芳
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The occurrence of mold not only affects the appearance of the surface of the object, but the mold that grows in the deep layer can also break through the paint film and cause cracking and peeling, resulting in damage to the object; and the growth of mold can also threaten the health of animals and humans

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] A mildew-proof and damp-removing latex paint provided by the invention comprises pure acrylic emulsion, styrene-acrylic emulsion, silicon oxide particles, nano-silver powder, cocoic acid diethanolamide, ethyl orthosilicate, sodium hexametaphosphate, water, each The mass parts of the components are: pure acrylic emulsion 30-60, styrene-acrylic emulsion 20-50, silicon oxide particles 18-22, nano silver powder 10-20, coconut acid diethanolamide 15-20, ethyl orthosilicate 30-40, sodium hexametaphosphate 30-60, water 50-70.

[0012] As a preference, the parts by mass of each component of the mildew-proof and damp-removing latex paint are: pure acrylic emulsion 50, styrene-acrylic emulsion 40, silicon oxide particles 20, nano-silver powder 20, coconut acid diethanolamide 15, orthosilicic acid Ethyl ester 35, sodium hexametaphosphate 35, water 60.

[0013] Preferably, the particle size of the silicon oxide particles is 1000-1100 mesh, more preferably 1000 mesh.

[0014] Pref...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a mildew-proof and damp-removing latex paint, which comprises pure acrylic emulsion, styrene-acrylic emulsion, silicon oxide particles, nano-silver powder, coconut acid diethanolamide, ethyl orthosilicate, sodium hexametaphosphate, water, each group The parts by mass are: pure acrylic emulsion 30-60, styrene-acrylic emulsion 20-50, silicon oxide particles 18-22, nano-silver powder 10-20, coconut acid diethanolamide 15-20, tetraethyl orthosilicate 30 ‑40, sodium hexametaphosphate 30‑60, water 50‑70. The invention has a more efficient anti-mildew technology, effectively absorbs moisture in humid air, prevents mildew on the wall, sweeps away the dull breath caused by musty smell, is breathable and moisture-proof, and provides the best wall effect, especially suitable for wall renovation and interior renovation.

Description

technical field [0001] The invention relates to the technical field of paint preparation, in particular to a mildew-proof and moisture-removing latex paint. Background technique [0002] Traditional coatings mostly use downstream products of the petroleum industry as the main raw materials, and are mixtures of polymer substances and ingredients. With the continuous improvement of people's health awareness, people's requirements for the coating products used are also getting higher and higher. [0003] In real life, temperature, humidity, and mold spores are the three necessary conditions for mold, and the temperature at which the human body feels comfortable is also the temperature at which mold grows, which cannot be changed. The occurrence of mold not only affects the appearance of the surface of the object, but the mold that grows in the deep layer can also break through the paint film and cause cracking and peeling, resulting in damage to the object; and the growth of mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D125/14C09D5/14C09D5/02
CPCC09D133/04C08K2003/0806C08K2201/011C09D5/024C09D5/14C08L25/14C08K13/02C08K3/36C08K3/08C08K5/20C08K3/32
Inventor 杨芳
Owner 杨芳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products