Heat treatment method of transmission metal chain

A heat treatment method and metal chain technology, applied in the chain field, can solve problems such as easily damaged parts, and achieve the effects of eliminating stress, improving wear resistance, and not easy to stick

Inactive Publication Date: 2017-12-08
河池桂嘉知识产权服务有限公司
View PDF13 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a heat treatment method for transmission metal chains, which can solve the problem of easy damage to components in the prior art when heat treatment is performed to improve the wear resistance of transmission metal chains

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The heat treatment method of the transmission metal chain of this embodiment includes the following steps:

[0017] A. Carburizing treatment: Put each component of the transmission metal chain into a carburizing furnace for carburizing treatment. The carburizing temperature is 750°C, the carburizing time is 50 minutes, and the carburizing time reaches 20 minutes, and an exhaust gas operation is performed; The fire temperature is 360℃, and the tempering time is 40 minutes. After the furnace is air-cooled, the parts are taken out of the carburizing furnace for surface cleaning;

[0018] B. Quenching: Take two heating furnaces marked (1) and (2), preheat the temperature of the two heating furnaces to 900℃ and 830℃ respectively, discharge the exhaust gas in the heating furnace, and then discharge the outside The chain plates and inner chain plates are placed in the heating furnace (1), and the heating furnace (1) is heated to 920°C for 80 minutes, and then the outer and inner ch...

Embodiment 2

[0021] The heat treatment method of the transmission metal chain of this embodiment includes the following steps:

[0022] A. Carburizing treatment: Put each part of the transmission metal chain into a carburizing furnace for carburizing treatment. The carburizing temperature is 760°C, the carburizing time is 55 minutes, and the carburizing time reaches 23 minutes for one exhaust gas operation; The fire temperature is 370℃, and the tempering time is 43 minutes. After the furnace is air-cooled, the parts are taken out of the carburizing furnace for surface cleaning;

[0023] B. Quenching: Take two heating furnaces marked (1) and (2), preheat the temperature of the two heating furnaces to 900℃ and 830℃ respectively, discharge the exhaust gas in the heating furnace, and then discharge the outside The chain plates and inner chain plates are placed in the heating furnace (1), and the heating furnace (1) is heated to 930°C for 83 minutes, and then the outer and inner chain plates are coo...

Embodiment 3

[0026] The heat treatment method of the transmission metal chain of this embodiment includes the following steps:

[0027] A. Carburizing treatment: Put each part of the transmission metal chain into a carburizing furnace for carburizing treatment. The carburizing temperature is 780℃, the carburizing time is 65 minutes, and the carburizing time reaches 26 minutes, and an exhaust gas operation is performed; The fire temperature is 390℃, and the tempering time is 46 minutes. After the furnace is air-cooled, the parts are taken out of the carburizing furnace for surface cleaning;

[0028] B. Quenching: Take two heating furnaces marked (1) and (2), preheat the temperature of the two heating furnaces to 900℃ and 830℃ respectively, discharge the exhaust gas in the heating furnace, and then discharge the outside The chain plates and inner chain plates are put into heating furnace (1), and heating furnace (1) is heated to 940°C for 86 minutes, and then the outer and inner chain plates are ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat treatment method for a transmission metal chain, which relates to the technical field of chains; it includes the following steps: A. Carburizing treatment: each component of the transmission metal chain is put into a carburizing furnace for carburizing treatment, and the carburizing temperature is 750 ℃ ​​~ 800 ℃, carburizing time 50 minutes ~ 70 minutes, tempering temperature 360 ​​℃ ~ 400 ℃, tempering time 40 minutes ~ 50 minutes; B, quenching: put each part of the transmission metal chain into two heating Oil cooling after heating in the furnace; C. Tempering: Temper and heat all parts at medium temperature and then air cool with the furnace. Compared with the prior art, the present invention can solve the problem in the prior art that parts are easily damaged when heat treatment is performed to improve the wear resistance of the transmission metal chain.

Description

Technical field [0001] The invention relates to the technical field of chains, in particular to a heat treatment method for transmission metal chains. Background technique [0002] In the field of mechanical transmission, the use of metal chains for transmission is very common. The basic structure of the transmission metal chain is that many chain link units of the same structure are connected end to end in the form of hinge pairs. Each part of the chain link unit includes two sets of oppositely arranged and The outer chain plate and the inner chain plate are connected by a pin, a sleeve is arranged between the two opposite inner chain plates, and the sleeve is sleeved with rollers. This structural feature enables the chain to have high strength and The chain can be flexibly changed in the specified direction, so that the chain can be widely used in agriculture, textiles, geological product mining, construction and automobile industries, covering a wide range of applications; but...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21D9/00C21D1/18C23C8/20
CPCC21D9/0087C21D1/18C23C8/20
Inventor 黄丽萍
Owner 河池桂嘉知识产权服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap