Anti-aging texture stone-like paint

A real stone paint, anti-aging technology, used in biocide-containing paints, antifouling/underwater coatings, coatings, etc., can solve the problems of real stone paint prone to cracks, peeling, poor aging resistance, etc. Achieve good antibacterial and self-cleaning properties, optimized film formation, and good aging resistance

Inactive Publication Date: 2018-01-19
WUHU SHUANGBAO BUILDING MATERIAL
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Real stone paint is used as the wall of buildings. Most of the existing products focus on protection and decoration functions, which leads to the fact that real stone paint is prone to cracks during film formation and use, and its aging resistance is not good, and it is prone to peeling. With the improvement of people's living standards, the existing real stone paint can no longer meet people's needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A real stone paint with anti-aging texture, said real stone paint includes the following raw materials in parts by weight: 30 parts of quartz sand, 25 parts of colored sand, 7 parts of modified styrene-acrylic emulsion, SiO 2 10 parts of airgel powder, 4 parts of thickener, 2 parts of ethylene glycol butyl ether, 0.2 parts of methyl benzyl alcohol, 2 parts of wetting agent, 1 part of defoamer, 1 part of chitin, 0.1 parts of water repellent share.

Embodiment 2

[0021] A real stone paint with anti-aging texture, said real stone paint includes the following raw materials in parts by weight: 40 parts of quartz sand, 18 parts of colored sand, 12 parts of modified styrene-acrylic emulsion, SiO 2 6 parts of airgel powder, 6 parts of thickener, 1 part of ethylene glycol butyl ether, 0.3 parts of methyl benzyl alcohol, 1 part of wetting agent, 2 parts of defoamer, 0.5 parts of chitin, 0.2 parts of water repellent share;

[0022] Wherein, the antifoaming agent is polydimethylsiloxane;

[0023] The preparation method of the modified styrene-acrylic emulsion is: sequentially adding nano-TiO 2 , sodium bicarbonate, deionized water, heated to 70°C, sequentially add the monomer mixture of styrene and butyl acrylate, emulsifier, add the initiator at the stirring speed of 400r / min and the temperature of 80°C, keep the temperature for 2h, A modified styrene-acrylic emulsion was obtained.

Embodiment 3

[0025] A real stone paint with anti-aging texture, said real stone paint comprises the following raw materials composed by weight: 35 parts of quartz sand, 21 parts of colored sand, 9 parts of modified styrene-acrylic emulsion, SiO 2 8 parts of airgel powder, 5 parts of thickener, 1.5 parts of ethylene glycol butyl ether, 0.25 parts of methyl benzyl alcohol, 1.5 parts of wetting agent, 1.5 parts of defoamer, 0.7 parts of chitin, 0.15 parts of water repellent share;

[0026] Wherein, the antifoaming agent is tributyl phosphate;

[0027] The preparation method of the modified styrene-acrylic emulsion is: sequentially adding nano-TiO 2 , sodium bicarbonate, deionized water, heated to 80°C, sequentially add the monomer mixture of styrene and butyl acrylate, emulsifier, add the initiator at a stirring speed of 300r / min and a temperature of 90°C, and keep it warm for 1h. Obtain modified styrene-acrylic emulsion;

[0028] Wherein, the emulsifier includes sodium lauryl sulfate and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-aging texture stone-like paint. The stone-like paint comprises the following raw materials in parts by weight: 30 to 40 parts of quartz sand, 18 to 25 parts of coloredsand, 7 to 12 parts of modified styrene-acrylic emulsion, 6 to 10 parts of SiO2 aerogel powder, 4 to 6 parts of a thickening agent, 1 to 2 parts of butyl cellosolve, 0.2 to 0.3 part of methyl alcohol,1 to 2 parts of a wetting agent, 1 to 2 parts of a defoaming agent, 0.5 to 1 part of chitin and 0.1 to 0.2 part of a water repellent. The stone-like paint disclosed by the invention has preferable anti-aging performance, and simultaneously is high in cracking resistance, heat stability, heat insulation and mechanical property.

Description

technical field [0001] The invention relates to real stone paint, in particular to an aging-resistant real stone paint. Background technique [0002] Real stone paint is a kind of paint with a decorative effect similar to marble and granite. The coating of real stone paint is composed of primer layer, real stone paint layer and finish paint layer. The primer layer adopts a primer with anti-alkali sealing effect, which can isolate and prevent moisture from penetrating into the coating from the base concrete, strengthen the adhesion between the coating and the base surface, and avoid peeling off of the coating; The three-dimensional main body material plays various protective functions. The overcoat is a decorative protective layer, which can not only strengthen the waterproof function of the real stone paint layer, but also improve the weather resistance and pollution resistance of the coating, enhance the hardness of the coating film, and make the coating surface more glos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/16C09D5/14C09D7/61C09D7/63C09D7/65
Inventor 胡昌悌
Owner WUHU SHUANGBAO BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap